Oxygen vacancy regulation and its high frequency response mechanism in microwave ceramics

Abstract

Li2ZnTi3−xMxO8 {M = Al3+, Nb5+, (Al0.5Nb0.5)4+, (Zn1/3Nb2/3)4+, and (Li1/4Nb3/4)4+} systems were fabricated by a facile solid-state reaction method. According to the substitution rule of radius and valence, all of the doping ions {Al3+, Nb5+, (Al0.5Nb0.5)4+, (Zn1/3Nb2/3)4+, and (Li1/4Nb3/4)4+} should occupy Ti4+ sites. EPR spectra showed that paramagnetic Ti3+ centers and oxygen vacancies co-existed in the pure Li2ZnTi3O8 ceramics. The oxygen vacancies in Li2ZnTi3O8 were attributed to the deoxidation process during high temperature sintering. The inhibitory effects of acceptor ion, donor ion and co-doped ions on oxygen vacancies were related to the lattice energy (U) of O(1). An appropriate amount of (Al0.5Nb0.5)4+, (Zn1/3Nb2/3)4+ and (Li1/4Nb3/4)4+ greatly reduced the microwave dielectric loss of the Li2ZnTi3O8 systems. And, the microwave dielectric loss deteriorated seriously in Al3+-doped systems. For the first time, a systematic exposition on the response process of dielectric loss in Li2ZnTi3O8 ceramics was discussed based on the ac impedance analysis and terahertz time-domain spectroscopy (THz-TDS) analysis in detail. Deeper analysis revealed that the absorption of structural phonon oscillation and long-range movement of weakly bound defects (Image ID:c8tc03936d-t1.gif) were two major contributors to the microwave dielectric loss.

Graphical abstract: Oxygen vacancy regulation and its high frequency response mechanism in microwave ceramics

Supplementary files

Article information

Article type
Paper
Submitted
07 ago 2018
Accepted
26 set 2018
First published
27 set 2018

J. Mater. Chem. C, 2018,6, 11023-11034

Oxygen vacancy regulation and its high frequency response mechanism in microwave ceramics

B. Zhang, L. Li and W. Luo, J. Mater. Chem. C, 2018, 6, 11023 DOI: 10.1039/C8TC03936D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements