Synthesis of yellow mesoporous Ni-doped TiO2 with enhanced photoelectrochemical performance under visible light

Abstract

A novel ordered mesoporous Ni-doped TiO2 was successfully prepared via an in situ sol–gel method. TEM and SEM images showed that the synthesized material had a highly ordered and uniform mesoporous structure. EDS and XPS confirmed that the nickel element was doped into the TiO2 crystal lattice homogeneously in the form of Ni2+ ions. Meanwhile, the doping of Ni changed the positions of the energy bands of TiO2, resulting in the decrease of the band gap, and enhanced the absorption of visible light. Moreover, due to the defect sites induced by doping which could cause recombination of electrons and holes, different doping amounts were investigated in order to achieve optimized parameters. As a result, when the molar ratio of Ni/Ti was 0.01, the ordered mesoporous Ni-doped TiO2 exhibited the highest photocurrent density of 3.1 μA cm−2 at 1.3 V (vs. RHE) under visible light irradiation.

Graphical abstract: Synthesis of yellow mesoporous Ni-doped TiO2 with enhanced photoelectrochemical performance under visible light

Supplementary files

Article information

Article type
Research Article
Submitted
27 dez 2016
Accepted
16 fev 2017
First published
16 fev 2017

Inorg. Chem. Front., 2017,4, 898-906

Synthesis of yellow mesoporous Ni-doped TiO2 with enhanced photoelectrochemical performance under visible light

B. Gao, T. Wang, X. Fan, H. Gong, H. Guo, W. Xia, Y. Feng, X. Huang and J. He, Inorg. Chem. Front., 2017, 4, 898 DOI: 10.1039/C6QI00609D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements