Enhancing thermoelectric performance of n-type PbSe via additional meso-scale phonon scattering

Abstract

The study of the lead chalcogenides system has been extended throughout the history of thermoelectrics due to their extraordinary physical and chemical properties. Compared with PbTe, PbSe has been drawing increased attention because it combines several attractive features, such as higher melting point, lower cost, and higher operation temperatures. The all-scale hierarchical structures were successfully applied to p-type PbSe systems, and a fascinating ZT value was achieved by effectively reducing the lattice thermal conductivity, which could be attributed to phonon scattering with a spectrum of wavelengths. However, the lattice thermal conductivity also reached about 1.0 W m−1 K−1 in the n-type PbSe system, which is very high compared with p-type PbSe that has been reported. In this study, by means of introducing mesostructures, the lattice thermal conductivity was efficaciously lowered from ∼1.3 W m−1 K−1 to ∼1.2 W m−1 K−1 at room temperature and ∼0.9 W m−1 K−1 to ∼0.6 W m−1 K−1 at 923 K for the n-type PbSe–PbS system. Correspondingly, a marked increase in ZT value from ∼1.3 to ∼1.5 at 923 K was observed, which indicated that the applications with superior conversion efficiencies on a large scale could be achieved from systems consisting of abundant and inexpensive chemical elements.

Graphical abstract: Enhancing thermoelectric performance of n-type PbSe via additional meso-scale phonon scattering

Article information

Article type
Research Article
Submitted
24 Ama 2017
Accepted
07 Gur 2017
First published
08 Gur 2017

Inorg. Chem. Front., 2017,4, 719-726

Enhancing thermoelectric performance of n-type PbSe via additional meso-scale phonon scattering

X. Qian, L. Zheng, Y. Xiao, C. Chang and L. Zhao, Inorg. Chem. Front., 2017, 4, 719 DOI: 10.1039/C7QI00051K

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements