Measuring metal halide perovskite single cell degradation consistent with module-based conditions

Abstract

In past years, there has been progress towards increasing the efficiency of metal halide perovskite solar cells (PSCs) without sacrificing long-term stability. However, preventing or mitigating degradation remains one of the major challenges for the commercialization of PSCs. Researchers must ensure that information learned from cell-level studies is relevant to the ultimate target of module application. In this work, we demonstrate that the bias condition used during aging studies has a measurable impact on degradation. We compared the performance of a large number of devices (n = 486) which were aged either under open-circuit (OC) or quasi-maximum power point (qMPP) conditions. The performance losses between the two conditions are found to be correlated, but notably, aging at OC leads to a more rapid performance decrease. Furthermore, this faster degradation in the OC condition compared with the qMPP condition occurs regardless of device stack design, treatments, or additives as demonstrated across approximately 160 variants of the p-i-n device stack. The OC condition is an important factor for field stability because partial shading of a module can result in individual cells going into OC. The fact that the degradation dynamics between qMPP and OC conditions are highly correlated indicates that aging studies at OC are related to relevant degradation processes. Consequently, stability studies to generate relevant insights into the degradation processes of PSCs can be executed without requiring sophisticated electronic infrastructure. However, care must be taken with cell-level experimental configurations because unintended, artificial degradation mechanisms may arise that are either not relevant to the application (e.g., modules) or obfuscate the results of the study being undertaken.

Graphical abstract: Measuring metal halide perovskite single cell degradation consistent with module-based conditions

Supplementary files

Article information

Article type
Paper
Submitted
29 sep 2023
Accepted
27 des 2023
First published
02 jan 2024
This article is Open Access
Creative Commons BY-NC license

Sustainable Energy Fuels, 2024,8, 546-553

Measuring metal halide perovskite single cell degradation consistent with module-based conditions

R. Tirawat, A. E. Louks, M. Yang, S. N. Habisreutinger, J. van de Lagemaat, S. Uličná, R. A. Kerner, K. Zhu, L. T. Schelhas, A. F. Palmstrom and J. J. Berry, Sustainable Energy Fuels, 2024, 8, 546 DOI: 10.1039/D3SE01268A

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements