Direct ink writing advances in multi-material structures for a sustainable future

Victoria G. Rocha *a, Eduardo Saiz b, Iuliia S. Tirichenko b and Esther García-Tuñón c
aSchool of Engineering, Cardiff University, Cardiff CF243AA, UK. E-mail: GarciaRochaV@cardiff.ac.uk
bCentre for Advanced Structural Ceramics, Imperial College London, London SW7 2AZ, UK
cSchool of Engineering, Materials Innovation Factory, University of Liverpool, UK

Received 22nd April 2020 , Accepted 22nd July 2020

First published on 22nd July 2020


Abstract

Novel manufacturing techniques such as additive manufacturing (AM, also referred to as 3D printing) will play a critical role in building a sustainable future. AM will reduce waste, energy consumption and production time by eliminating the need to assemble components. It will also enable the mass customization of complex devices. To reach their full potential, additive manufacturing technologies should be able to combine different materials in a single processing step. Although the development of multi-material printing is in its infancy, it could have a massive impact in fields as diverse as energy storage and generation, electronic devices, healthcare or structural composites to name a few. Here we provide a critical perspective on the advances and potential of multi-material printing using direct extrusion-based printing, also known as direct ink writing (DIW) or robocasting. We will show examples of devices and structures combining a wide range of materials from ceramics to metals, polymers and carbon with particular focus on three promising applications: energy storage, lightweight composites and sensors. The goals are to assess the progress made so far, to point out specific challenges and areas for further development and to provide guidelines to those interested in multi-material DIW.


image file: d0ta04181e-p1.tif

Victoria G. Rocha

Victoria G. Rocha is Honorary Research Fellow in the School of Engineering at Cardiff University and has been recently awarded a Ramón y Cajal Tenure Track fellowship to join the National Institute of Carbon Science and Technology, CSIC, in Spain where she had obtained her PhD in Materials Science in 2008. Before joining Cardiff University, she worked at ITMA Materials Technology, Bath University and she was Intra-European Marie Curie Fellow at the Centre of Advanced Structural Ceramics at Imperial College London. Her research focuses on design and formulation of multi-material pastes for extrusion-based printing in energy storage applications and composites but also on processing and development of novel bioinspired graphene/ceramic composites through spark plasma sintering.

image file: d0ta04181e-p2.tif

Eduardo Saiz

Eduardo Saiz is a Professor in the Department of Materials at Imperial College, where he directs the Centre for Advanced Structural Ceramics. He received his PhD degree in Applied Physics from Universidad Autónoma de Madrid. Before joining Imperial College, he worked at Lawrence Berkeley National Laboratory. His research focuses on the processing and characterization of ceramics and ceramic-based composites for different applications from aerospace to healthcare and the study of high temperature interfacial phenomena.

image file: d0ta04181e-p3.tif

Iuliia S. Tirichenko

Iuliia S. Tirichenko is currently a postdoctoral research associate in the Centre for Advanced Structural Ceramics (CASC), Department of Materials, Imperial College London. She received her specialist degree in Physics of Metals from Voronezh State Technical University, Voronezh, Russia and her PhD in Chemical Engineering from Imperial College London. Her research interests include colloid science, processing, and formulations for additive manufacturing of ceramic materials.

image file: d0ta04181e-p4.tif

Esther García-Tuñón

Esther García-Tuñón completed her degree in Chemical Engineering and a PhD in Materials Science from the University of Santiago de Compostela, Galicia (Spain). She moved to the UK to join the Centre for Advanced Structural Ceramics (CASC) at Imperial College London with a Barrie de la Maza fellowship in October 2011. After five years as a postdoctoral researcher at Imperial, Esther joined the University of Liverpool in 2017 as a Lecturer in Materials Science and Engineering. Her group, affiliated to the Materials Innovation Factory (MIF) and the School of Engineering, works across different disciplines. Her research interests include processing, complex fluids and rheology.


1. Introduction

In 2015 the United Nations agreed the 2030 Agenda for Sustainable Development. Goals 9 and 13 mention the importance of sustainable industrial development, and of taking actions to combat climate change respectively.1 To achieve those goals industry must implement innovative approaches to manufacture more efficiently with less raw materials in order to build a future that is more prosperous, more just, and more secure. Traditional mass production of identical commodity items usually involves processes such as casting, forging or machining, which do not minimise waste. At the same time many of these processes limit the complexity of the structures that can be fabricated and therefore impose additional design constraints. Many efforts are being made to develop novel manufacturing techniques such as additive manufacturing (AM, also referred to as 3D printing) that unlike casting do not rely on the use of moulds and enable the fabrication of complex geometric shapes that can be mass-customized. AM is a group of technologies capable to build structures layer-by-layer through a series of cross-sectional slices, that are generated by a design software. AM design concepts are translated into products via digital manufacturing which allows merging of multiple components in one fabrication step without additional assembly operations, thus saving materials and energy.2 There are over fifty different AM techniques usually classified into seven different processes in accordance to the ASTM F2792-12a: binder jetting, material jetting, material extrusion, vat photopolymerisation, powder bed fusion, energy deposition and sheet lamination.3

The published literature on AM has grown exponentially since 2004, being major contributors to its development scientists and engineers from a wide range of disciplines from material science to chemistry and physics, mechanical engineering and artificial intelligence. The outcomes of this research investment are having an impact in numerous fields from healthcare, electronics and civil engineering to energy generation and storage, environmental engineering, education or entertainment to name some.2 As this emerging field quickly develops, the number of published reviews in AM doubles every two years. Some of them focus on objects made of an individual family of materials such as polymers,4,5 metals,6–8 ceramics,9 carbon-based10 materials and even nanomaterials11 using different AM techniques, while others cover a single material or a very specific technique. The number of reviews focusing on a specific application such as energy storage12–16 and electrochemical devices17–19 is also growing, which reveals the fast development of a wide multi-disciplinary field. A review by MacDonald et al.20 highlights the potential of multi-process (or hybrid) 3D printing, in which complementary technologies, both novel and traditional, are ‘collaboratively’ combined to advance the future of manufacturing. The authors state that the next generation of 3D printing will enable the integration of dissimilar materials and allow the integration of active components to deliver functionality that was not possible previously.20

The development of multi-material printing is at its infancy however it could have a massive impact for example in energy applications, electronic devices and composites. Combining different materials in a single manufacturing process will reduce waste and production time by eliminating the need to assemble components. It will also expand the design space, enabling new products, composites and devices with structural and functional properties. Among all the AM processes only material jetting and material extrusion have shown promising results in multi-material printing, one of the biggest challenges in AM today.

Material extrusion techniques such as fused deposition modelling (FDM) enable multi-material structures by melting filaments made of pure polymeric materials or a combination of different polymers with functional materials. Several reviews4,5 have highlighted the success. Here we provide a critical perspective on the fabrication of ‘truly’ multi-material structures in which different classes of materials, such as ceramics, metals, polymers and carbon-based materials are combined using direct ink writing (DIW) 3D printing.

3D-printing through material extrusion of viscoplastic pastes (also referred to as ‘inks’) is also known as direct ink writing (DIW) or robocasting. DIW was initially developed to create complex ceramic structures, hence the term robocasting, and so far, has been mainly exploited in research labs for small scale fabrication. The number of research groups using this technique has expanded worldwide beyond the structural ceramics field into other areas, such as 3D bioprinting,21–23 energy,24–27 composites,28,29 sensors,30 robots31etc. DIW is the most versatile AM technique in terms of materials development, it enables the creation of complex 3D shapes using any material by formulating a paste with controlled rheology27,32–36 (a shear-thinning yield stress fluid37). The current advances in formulation design34,38 and the fundamental understanding of the rheological parameters that define ‘printability’29,35,39,40 will pave the way for scaling up and industrial use. Another advantage of DIW is that it enables a combination of different formulations into complex structures by using multiple extrusion nozzles (Fig. 1). Modifications of the extrusion system by using microfluidic printheads allows to switch41,42 or mix43,44 (Fig. 1) different materials in a single pass. Multi-material DIW has also the potential to provide engineered interfaces. Formulations with similar composition and rheology have been combined to make soft structures,42 or glass with varying compositions.45 However, so far there are only a few examples in the literature of what we consider ‘truly’ multi-material structures. In part this is due to the limitations imposed by the post-printing steps (drying, de-binding and consolidation) that are often necessary but restrict the combination of materials with very different properties (e.g. thermal expansion, melting point or oxygen sensitivity). An alternative approach is to formulate printable materials that can be shaped and used as printed, avoiding post-processing without compromising functionality. This approach has been used to make thick semisolid electrodes for Li-ion batteries.26


image file: d0ta04181e-f1.tif
Fig. 1 Multi-material 3D printing approaches for soft-materials. (a) Systems for active mixing in situ during printing using rotating impellers (grey shadow) designed for large (LVM) and reduced (RVM) volumes. These systems enable the integration of multi-material graded compositions into a structure. Reproduced from ref. 44 with permission from John Wiley and Sons. (b) Multi-material, multi-nozzle 3D printheads in a microfluidic system combining fast pneumatic solenoids and soft inks enable voxelated printing. Reproduced from ref. 42 with permission from Springer Nature. (c) Multi-material deposition of hydrogel structures based on an aspiration-on-demand protocol. The constitutive multi-material segments of extruded filaments were first assembled in liquid state by sequential aspiration of inks into a glass capillary, followed by in situ gel formation. Scale bar (2 mm). Reproduced from ref. 46 with permission from Springer Nature.

In this perspective, we review the progress made to date pointing out specific challenges and areas for further development in order to provide guidelines for those interested in multi-material DIW. We highlight successful examples in three promising applications: energy storage, lightweight composites and sensors.

2. Direct ink writing for multi-material printing

Current approaches for direct ink writing of disparate materials with high spatial resolution are based on precision motion control systems. This is normally an XYZ gantry robot with a few microns (1–3 μm) accuracy and repeatability in the 3 directions. At the laboratory scale, this robot is normally equipped with linear motors that can reach maximum speeds between 0.1 and 2 m s−1. The gantry robot is coupled with a printer head device with multiple syringes pumps or pressure-driven reservoirs for different formulations. Disparate materials can be combined in the same object by synchronising XYZ motion with the plunger displacement or applied pressure. The precise movements of the XYZ gantry robot and syringe pumps are controlled through a user interface or software that translates a predefined 3D design into g-code commands that guide the printing of the desired object.

Several add-ons and modifications of the basic set-up described above can expand the versatility of the technique and the range of formulations used to increase the complexity of the printed object. For example by designing active mixers43 and droplet generators;47 attaching CCD cameras48 or UV-light sources to cure polymers49 (Fig. 2); using humidifiers, suspension baths for embedded printing, and heated syringes and/or platforms;50 combining DIW with additional Fused Deposition Modelling (FDM) printer heads51 (Fig. 2); or simply by placing the system under controlled atmospheres.26


image file: d0ta04181e-f2.tif
Fig. 2 Examples of modified DIW systems (a and b) and criteria for ink printability (c and d). (a) The scheme shows a multi-phase additive manufacturing system that combines DIW components (1) with FDM modules (2) heated platform (3) and with gear-boxes allowing spatial resolution of ±3.4 μm (4). Reproduced from ref. 51 with permission from Elsevier. (b) Schematic showing the processes involved in a dynamic photomask-assisted DIW multi-material system. The DIW-printed structure is placed under the dynamic photomask which consists on a projector with a set of light patterns whose display time is controlled by the software. Reproduced from ref. 52 with permission from John Wiley and Sons. (c) Amplitude sweep at fixed frequency of inks with varying graphene oxide (GO) content showing some of the main rheology parameters (G′, G′′ and flow stress) that can be used to quantify printability. Reproduced from ref. 35 with permission from RSC. (d) Printability map that shows the optimum region for DIW of graphene oxide suspensions, those with a crossover point (flow stress) above 500 Pa, image file: d0ta04181e-t1.tif of the order of 104 to 105 Pa, and FTI below 20 with very small uncertainties. Reproduced from ref. 35 with permission from RSC.

The main difference between FDM and DIW is that in FDM polymeric filaments must be melted during extrusion, while DIW systems rely purely on pastes with very specific rheology that are stored in a syringe cartridge. These complex fluids are formulations that typically comprise a mixture of powdered materials (and in most cases different additives) in a liquid with concentrations that are systematically adjusted to achieve a paste with yield stress and shear thinning behaviour. After careful mixing and conditioning (e.g. defoaming, cooling or heating, or even after reactions that may need to take place between the components in the mixture) these pastes should easily flow under shear and quickly recover upon deposition. Printable formulations are non-Newtonian fluids with a yield stress often described as Herschel–Bulkley fluids (τ = τy + K[small gamma, Greek, dot above]n where τ (Pa) is the shear stress applied, τy (Pa) is the yield stress, K (Pa sn) the viscosity parameter and [small gamma, Greek, dot above] (s−1) the shear rate).32 Other models for non-Newtonian fluids with a yield stress could be more suitable but they have not been widely used in the DIW community so far.53 In general, beyond the yielding point these yield stress fluids have a shear thinning behaviour with very small flow index values (the dimensionless coefficient n that measures to which degree the fluid is shear thinning or shear thickening, for Newtonian fluids n = 1). Shear tests for printable pastes are extremely affected by transient effects, shear banding and shear induced fracture so data interpretation and analysis should be carefully done. After the yielding point the flow index can be more accurately determined from a viscosity plot (log[thin space (1/6-em)]μ (Pa s) vs. log[thin space (1/6-em)][small gamma, Greek, dot above] (s−1)) using the power law model τ = K[small gamma, Greek, dot above]n and only with the data in the shear thinning region at mid-shear rates. Oscillatory rheology is a less uncertain alternative to quantify printability using bulk rheological parameters obtained from an amplitude sweep: the storage modulus in the linear viscoelastic region (LVR), image file: d0ta04181e-t2.tif (Pa); the crossover point (Pa, stress at which G′ = G′′, where G′′ is the loss modulus); and the flow transition index, FTI (dimensionless, stress at yielding point image file: d0ta04181e-t3.tif, (G′ = G′′)) (Fig. 2c and d).35 The figure of merit (FoM, image file: d0ta04181e-t4.tif) is another dimensionless number that can provide guidance in formulation design.29 As a benchmark guide the crossover stress (G′ = G′′) determined from an amplitude sweep must be high enough for the formulation to be self-supportive in the absence of stress (∼500 Pa) but not too high (<2500 Pa) as this could easily compromise the extrusion process by clogging the nozzles or leading to filter press effects for filled systems. The kinetics of the recovery scales with image file: d0ta04181e-t5.tif,35 which must broadly reach values of the order 104 to 105 Pa for DIW applications but heading towards the upper range (105 Pa) to guarantee good printing resolution of multi-material structures. Formulations should also have FTI values below 20 and FoM values above 20. The wider DIW community will benefit from adopting a systematic rheological characterisation using common protocols and defining the meaning and origin of every rheological parameter used. For example, the cross over point (G′ = G′′) can be referred as the yield stress or flow stress depending on the source, while some papers refer only to viscosity values at a certain shear rate, which is not enough to characterise such complex fluids.

3. DIW approaches to multi-material structures: challenges and opportunities

Different approaches can be used to print multi-material structures, each of them with potential in different fields but also with specific technical issues. Here we classify them based on the number of printing cartridges used:

-Single-paste cartridge. In these systems, an object is constructed using a multi-material ink extruded from a single cartridge through a single nozzle. We include here those systems in which the composition of the ink may be gradually changed (e.g. by using in situ mixing to change the ratio between two components). A variant of multi-material building using a single cartridge is the use of robotic-assisted deposition to build preforms that are then filled by a second phase.

-Multiple-pastes cartridges. In these systems, an object or a device is built by alternatively extruding formulations with different compositions from different cartridges through one to multiple nozzles. It involves switching of cartridges and/or nozzles on the flight during printing. This is the approach generally considered as “true” multi-material printing that has been used to print complex devices like those designed for energy storage.

-Co-extrusion of pastes. Between the two approaches described above are coextrusion systems designed with concentric nozzles to print core–shell filaments (with the core and shell from different compositions). There are already large-scale co-extrusion systems designed to print polymer-based composites.

This simple classification enables us to highlight specific challenges and areas for development. In the next subsections, we review specific examples for each approach.

3.1 Single-paste cartridge systems

A wide range of multi-material inks have been formulated to print composites for different applications, from lightweight structural materials,28,54 to tissue engineering scaffolds,55 sensors30,56–59 or thermoelectric devices.60 All these applications demand careful structural control not only at the macrolevel (where 3D printing has clear advantages) but also at the micro level and below. The later has been a challenge but as the technology advances it is also becoming evident that the extrusion process itself can be used to open new possibilities in microstructural design. Several groups have used additive manufacturing to create porous preforms that are infiltrated with a second phase.61 In this case, the preform design is used to control microstructure. Another fruitful approach is the use of flow during extrusion, sometimes in coordination with external fields, to align anisotropic particles (typically fibres or platelets) in a matrix (usually organic).62,63 In some cases, both approaches are combined and preforms are built using fibres or platelets that can be subsequently infiltrated to generate the composite material.29

Usually, when printing structural composites, the focus is often to enhance fracture resistance. By controlling the distribution and orientation of stiff and anisotropic reinforcements in a matrix it is possible to manipulate crack paths and promote extrinsic toughening. This opens new opportunities for ceramic-based composites that are often the only alternative for applications at high temperature or in highly corrosive environments and whose use is in many cases limited by their fracture resistance rather than their strength. Printed composites have also been used in sensors for stress or temperature developed for soft robotics64 or wearable devices.65 Inks containing carbon nanotubes or graphene enable the formation of carbon networks in elastomeric polymeric matrices that can be used for piezopotential or resistive sensing. An illustration in the case of resistive sensing is the alignment during printing of graphene sheets in a PDMS matrix that results in interconnected networks with enhanced electrical conductivity at lower carbon contents. As a result, variations of electrical resistance with flexion or pressure can be easily detected. Carbon nanotubes networks in a PDMS matrix also enhance the performance of printed piezoresistive strain sensors.66

Another area of application is in the field of active materials: 4D printing. The fourth dimension is described by Tibbits67 as transformation over time, emphasising that printed structures are no longer simply static, dead objects; rather, they can be programmed to be active and can transform independently. DIW single-cartridge systems have been successfully used to print soft material composites whose microstructure is designed to provide programmable shape response (after immersion in water,68 using magnetic fields69 or temperature control70) yielding complex three-dimensional morphologies.

In general, for extrusion-based additive manufacturing to provide further practical advances it will be necessary to push the limits of structural manipulation at all length scales. This type of control can often be achieved by manipulating the composition of the inks and the size and structure of the particles used in their formulation. For instance, work with platelet-based materials suggests that platelet roughness at a submicron level can have a large contribution to the mechanical response of composites.71,72 It can be more difficult to manipulate structure at the microlevel and this may require modifications of the printing system as in the use of magnetic fields to manipulate particle orientation63 or systems designed to actively mix43,44 the cartridge in situ during printing while controlling the feeding of the different components to enable compositional variations along the structure73,74 (Fig. 3).


image file: d0ta04181e-f3.tif
Fig. 3 Multi-material structures using single-cartridge (a), co-extrusion (b), active mixing (c) and multi-cartridge (d) DIW approaches. (a) Example of 4D printing using a single cartridge: NdFeB ferromagnetic particles embedded in an elastomeric composite paste can be aligned on demand through a magnetic field coupled to the DIW nozzle to fabricate shape-programmable soft materials (4D printing). Reproduced from ref. 69 with permission from Springer Nature. (b) DIW coextrusion methodology of a core–shell carbon fibers/silicon carbide (Cf/SiC) lightweight composite. The dense SiC shell provides strength while the core contains highly oriented Cf that enhance the material toughness. Reproduced from ref. 75 with permission from Elsevier. (c) Combination of an active mixer with DIW to control spatially the extent of a thermite reaction (Al, CuO) within a structure. The speed of the rotating impeller gives an additional degree of control over the mixing and results in a homogeneous composition at sufficiently high rotational speeds. This is a promising pathway for the manipulation of microstructure within a printed object. Reproduced from ref. 74 with permission from John Wiley and Sons. (d) Multi-cartridge system with add-ons, including a magnetic field generator, an UV-light for in situ curing and movable platform. An ink of magnetically responsive anisotropic and stiff particles was printed to make an helicoidal staircase suspended in a light-sensitive liquid resin of tuneable composition. Soft mechanical fasteners fabricated through programmable multi-material magnetically assisted DIW printing of shape-changing objects. Printed key–lock objects before and after the shape change. Reproduced from ref. 63 with permission from Springer Nature.

3.2 Coextrusion of pastes

Co-axial extrusion systems have been used to print ceramic matrix composites,75 filaments with sacrificial cores that are subsequently eliminated to create channels76 and cellular structures with high stiffness built from filaments combining stiff, brittle epoxy shells with a flexible core (Fig. 3b).77,78 These designs are often limited by the diameter of the co-axial printing nozzles. Composite manufacturing will also demand the development of effective strategies to engineer the core–shell interface for a wide range of material combinations.

3.3 Multi-paste cartridge systems

Most advances in this area have been made to create devices for electrochemical energy storage. This is one of the fields that is pushing the multi-material challenge given the nature of the application, in which the combination of very disparate materials from polymers, ceramics and metals in one single device is key for performance (Fig. 4).
image file: d0ta04181e-f4.tif
Fig. 4 Multi-material structures for energy applications using multi-cartridge DIW approaches. (a) The ink formulations used to fabricate a polymer electrolyte and a carbon/ceramic electrode via sequential printing led to a tight and continuous interface between the electrode and electrolyte layers. The electrochemical performance of these flexible devices is on par with commercial systems even at current rates as high as 5C. Reproduced from ref. 24 with permission from John Wiley and Sons. (b) An interdigitated supercapacitor made of reduced graphene oxide and copper was fabricated by combining Pluronic-F127®-based inks to formulate both the electrode and current collector pastes, multi-cartridge DIW and post-printing heat treatments. Reproduced from ref. 27 with permission from American Chemical Society. (c) Complexity via interdigitated multi-material DIW printing was also achieved for an asymmetric micro supercapacitor (MSC). The combination of an ink formulation based on graphene oxide as binder for the electrodes and a gel-electrolyte with several post-printing steps (freeze drying and hydrazine chemical reduction) resulted in a complex-shaped device with ultrahigh areal energy density and excellent performance. Reproduced from ref. 79 with permission from John Wiley and Sons. (d) Proof of concept of complex Li-ion batteries with solid electrolytes via multi-cartridge DIW: the inks must be formulated to reach good interfacial contact and electrochemical performance. This was first achieved on a flat system using α-MnO2 as electrode, then a heated-cartridge add-on allowed extrusion of a solid electrolyte paste. Finally, a proof of concept of an interdigitated Li-ion battery was DIW using a LTO/solid electrolyte/LFP and PDMS as packaging. Reproduced from ref. 50 with permission from John Wiley and Sons. (e) Fully 3D printed and packaged Li-ion battery (LIB) made using multi-cartridge DIW. The post-processing steps were eliminated through careful formulation design, placing the printer in an Ar-filled glove box and using UV light source to cure the packaging in situ. Reproduced from ref. 26 with permission from John Wiley and Sons.

When printing using multiple nozzles, in addition to adjusting the ink rheology to satisfy printing demands, there are other technical aspects that must be considered like tip alignment and start/stop flow settings. Tip alignment is crucial to guarantee precise control of the interface between the extruded lines, which may become even more challenging as the number of cartridges increases. Start/stop flow settings mainly depend on the density and rheology of the formulation. When switching from one nozzle to the next one, some inks may continue flowing when the plunger stops moving, making necessary to pull back the plunger to stop the flow. The “extra” flow of material from the tip is likely related to gravitational and rheological effects as inertial effects can be dismissed based on the very low Reynolds number (Re = ρvD/μ where: ρ is the density (kg m−3), v, the velocity (m s−1), D, the diameter of the nozzle (m) and μ the viscosity (Pa s)) values for highly viscoelastic shear thinning fluids flowing through very small nozzles. For example, Re values are of the order of 10−3 to 10−5 for graphene oxide-based inks at estimated shear rates of 20 s−1 and 200 s−1 in the nozzle, and printing speeds of 10 mm s−1. To effectively stop flow during switching, the back-off distance setting brings the plunger back and pulls the material inside the syringe preventing ink overflow, this distance must then be accounted for when pushing the plunger down to re-initiate flow. An added difficulty is that each DIW system may have different processes to ensure tip alignment, define and code printing settings to minimize flaws when switching cartridges, which often are not detailed in published literature.

One of the earliest successful attempts at multi-material DIW was the printing of the most fundamental components of a Zn–air battery,80 including the Zn anode, separator, cathode catalyst, anode/cathode terminals, and casing. The main challenge in this work was to select material formulations that could be deposited to fabricate all the essential components in the battery without compromising the performance of the final device. Subsequently, a huge effort has been made in the field to develop inks/pastes for each component and a large number of reviews on 3D printing for energy storage have been published but there are still very few examples in which multi-material devices have been successfully fabricated. So far, there have been many attempts to print electrodes and some solid electrolytes.14,81

One of the challenges in multi-cartridge printing is to engineer the interfaces between the different components to achieve the right degree of interconnection. Several research groups are trying to develop universal ink formulations based in the same carriers for different materials to ensure good interfacial contact and, if possible, avoid post-processing after printing. For example, Durstock et al.24 used a dry inversion method and a nanosized alumina filler to control the porosity of the polymeric electrolyte (Fig. 4a). They used a similar approach for the carbon/ceramic electrode formulation and thus succeed in DIW discs of both electrode and electrolyte while maintaining expected functionalities in both layers. This formulation approach demonstrates that the electrolyte can be sequentially printed directly over an electrode layer without sacrificing performance. They achieved a tight and continuous interface, which is a desired trait for discharge voltage stability in a flexible energy storage device under mechanical load. Similarly, Rocha et al.27 successfully printed a symmetric supercapacitor device by designing an environmentally friendly formulation that includes a thermo-responsive polymer as a carrier of both graphene oxide (electrodes) and copper (current collector) (Fig. 4b). This work illustrates another challenge. Often post-printing heat treatments are required to dry and eliminate organics as well as to consolidate the parts. These treatments should be compatible with all the materials allowing an accurate control of dimensional changes and the formation of stable interfaces. In this case, both graphene oxide reduction and Cu sintering can occur at the same temperature and atmosphere enabling the fabrication of an interdigitated shape with a strong interface between the current collector and the binder-free electrode.

Recently Yang et al.79 used DIW to make a multi-material asymmetric micro supercapacitor (MSC) with ultrahigh areal energy density (Fig. 4c). Cathode and anode inks of vanadium pentoxide (V2O5) and graphene–vanadium nitride quantum dots (G–VNQDs) with highly concentrated graphene oxide (GO) dispersions, as well as a LiCl–PVA gel electrolyte were designed and formulated. The 3D printed asymmetric MSC with interdigitated electrodes exhibited excellent structural integrity, a large areal mass loading of 3.1 mg cm−2, and a wide electrochemical potential window of 1.6 V. Moreover, there were substantial open macropores in the 3D printed electrodes, which provided numerous channels to facilitate mass transportation.

Cheng et al.50 also tackled the challenge of adding complexity and printed an interdigitated full cell battery. Lithium iron phosphate (LFP) and lithium titanium oxide (LTO) materials were formulated with poly(vinylidene-fluoride) PVDF, deposited onto pre-printed polydimethylsiloxane (PDMS) substrates and used as the cathode and anode respectively (Fig. 4d). A key step in this work is the formulation of a solid electrolyte using a polymer N-propyl-N-methyl pyrrolidinium bis(trifluoromethanesulfonyl)imide (Pyr13TFSI) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) salt mixed on poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-co-HFP) previously dissolved into N-methyl-2-pyrrolidone (NMP) solvent to then be filled with nanosized TiO2. They achieved a shear-thinning behaviour and very good wettability with the electrode substrates by elevated temperature DIW. A continuous, thin, and dense layer is formed between the porous electrolyte layer and the electrode, which effectively reduces the interfacial resistance of the solid-state battery. The interdigitated full battery was then sealed using polydimethylsiloxane (PDMS) gel under argon and showed an initial discharge capacity of 112 mA h g−1 at 16 mA g−1.

The latest work of Lewis et al.26 in this field shows a fully 3D printed and packaged LIB using DIW in which typical LIB manufacturing steps such as drying, electrolyte infilling, calendaring, clamping and heat sealing processes were eliminated by careful ink formulation together with encasing the custom-made 3D printer in an Ar-filled glove box and the use of UV light to cure the packaging seal (Fig. 4d). The formulation of inks to 3D print disparate materials without post-processing is a step forward and demonstrates the potential of this research area. Using biphasic semisolid carbon–ceramic mixtures with enhanced conductivity as thick electrodes and polymers–ceramic composites as separator and packaging they produced a fully 3D printed LIB that exhibited a ten-fold enhancement in areal capacity compared with their previous work.82 In a previous work, Sun et al.82 used the same technique to make a micro LIB battery with a more efficient approach to exploit the areal capacity by 3D printing interdigitated electrodes. The challenge was to seal the device in this configuration and they suggested to 3D print the packaging to solve this problem.

Beyond the field of energy storage there have been some demonstration of multi-cartridge printing in the area of sensors. Guo et al.83 fabricated a 3D tactile sensor composed of 3 layers (top and bottom electrode and sensor layer) (Fig. 5c). The composition of the electrodes and the sensors were very similar (silver in silicone in different proportions) and the fabrication required to print a sacrificial layer to support the structure that is subsequently eliminated. This strategy has been previously employed to widen the range of structures that can be fabricated by DIW and requires the combination of several cartridges, one of them containing the support material that is eliminated during postprocessing.84,85


image file: d0ta04181e-f5.tif
Fig. 5 Direct ink writing of multi-material sensor structures. (a) Fabrication of a multilayer tactile sensor using several cartridges and sequential printing; the device is manufactured using Ag/silicone inks with various solid loading fractions for each layer to create the functional components of the sensor (electrodes, sensor, isolation). To print overhanging features, a supporting hydrogel (Pluronic®) layer is used and subsequently removed. Reproduced from ref. 83 with permission from John Wiley and Sons. (b) Somatosensitive actuator featuring multiple soft sensors produced via embedded 3D-printing using a combination of robocasting and moulds; each sensor is produced by printing directly into a matrix material in a mould. Three moulds, with three different matrices (dorsal, actuator, anterior – two-part platinum-cure silicone elastomers of different compositions) are used to host three different components (curvature, inflation, contact – 6 wt% fumed silica in an ionic liquid EMIM-ES). Reproduced from ref. 59 with permission from John Wiley and Sons. (c) Stretchable piezoresistive sensor fabricated by step-by-step printing of a PDMS substrate (cured straight after printing using oxygen plasma treatment), electrode layer, and sensor layer. Reproduced from ref. 86 with permission from John Wiley and Sons.

4. Outlook, challenges and opportunities

In this perspective, we have highlighted the potential of printing multi-material structures via direct ink writing (DIW). This is a promising manufacturing technology, that undoubtedly could contribute towards a sustainable future. We have reviewed potential and issues in formulation and processing for multi-material DIW in several engineering applications: energy storage devices, lightweight composites and sensors. From this review some key issues emerge:

4.1 Formulation approaches

One of the main challenges of multi-cartridge printing is to design and formulate the viscoplastic and self-healing soft inks that easily flow under shear and quickly recover upon deposition, which are required as inks to print different compounds. There are many strategies to formulate pastes for DIW. Researchers often look for flexible approaches that can be adapted to formulate printing inks with a wide range of materials. Beyond exhibiting the right rheology, it is usually preferable if the organic content of the ink is low (to limit de-binding problems) and its solid contents is high (to minimize dimensional changes after shaping). In the case of multi-material printing other requirements arise such as the need to minimise or avoid postprocessing in structures containing different materials and the adjustment of rheology to allow smooth switching of cartridges and the formation of strong, well connected interfaces.

4.2 DIW systems

Very often it is difficult to reach the right rheology to print parts that do not deform and retain their shape with inks that flow easily through the printing nozzle. In these cases, part consolidation during printing can be achieved using systems that incorporate a secondary process such as polymer curing or drying. When using multi-cartridge approaches there are still technical problems that should be addressed from a wider cross-disciplinary community. It is key to carry out fundamental studies combining fluid mechanics, rheology and physics to develop the methodologies needed to overcome some of the issues we face, for example when switching ink flow from one nozzle to the next one. This is sometimes approached as a trial-error adjustment of printing parameters. Often this is know-how that is not openly shared or discussed in depth but that is critical for successful multi-material printing. Recently it has been shown how an alternative DIW system42 based on microfluidic printing heads enables very fast switching between materials and voxel by voxel fabrication to build soft-matter devices. The challenge now is to translate some of these concepts to the fabrication of hard, inorganic structures. This is an area where fundamental science will have to meet applied engineering, process control and machine learning. The development of systems able to monitor in situ printing variables (e.g. pressures and flows) and with the embedded “knowledge” to change them on the fly to correct for environmental fluctuations, or to adapt extrusion to create specific features, can bring multi-material printing closer to a commercial reality.

4.3 Structural control

One of the advantages of DIW for any application comes from the possibility to exert structural control simultaneously at multiple length scales from the micro to the macro levels. At the macro level, the technique can be used to implement some complex designs that may be difficult to access using other methodologies. For instance, DIW is particularly adept to the fabrication of light cellular structures.29,54,87 However, extrusion technologies face challenges when printing bulk materials that require stacking of several layers as gas can be trapped between them. This problem can be solved by programming the right degree of overlap between printed lines and reducing the height between layers in order to deform to some extent the filament during printing to fill the gaps.29 In some cases, post-printing treatments such as cold or hot isostatic pressing or lamination can be applied.29,88 These treatments will have an impact on the microstructure of the final materials. Another challenge in DIW is to print large overhangs or spans without sagging. This requires careful manipulation of formulation rheology but even when this is optimised, there are still some limits on the features that can be made using this technique. Sacrificial supports84 or embedded printing in a gel89 have been used to expand the range of shapes that can be printed by DIW.

The examples reviewed in this paper show that extrusion opens some possibilities for microstructural manipulation (such as the generation of specific textures). However, further control is often needed and additives can be used to optimize the microstructure as it has been shown in flexible pressure sensors formed by PDMS microspheres and PDMS elastomer fibres coated with CNTs, where the incorporation of microspheres significantly enhanced performance.90 Other approaches used sacrificial additions to create microporosity (for instance, to enhance tissue integration of implants and scaffolds).66,86 All these modifications and additions have to be done while maintaining the printability of the ink and retaining performance. An example is when fibre-reinforced epoxies are made printable by incorporating nano-clays.62 In this case there may be limits to the reinforcement content and it is important to ensure that the additions are not detrimental to the mechanical performance of the product.

4.4 Upscaling

Like for many other AM technologies, a key challenge for extrusion-based printing of structural materials is upscaling. Fabrication of large structures with fine details that require very small nozzles may require impractical time scales. One possibility is to modify the printing systems to combine printing heads with different resolutions. In addition, shaping often needs to be combined with subsequent treatments (e.g. drying, de-binding and sintering) while retaining dimensional accuracy and controlling the reactivity of the different components. Here, the combination of AM with novel fast densification technologies such as field assisted sintering can open new opportunities to build complex structures with phases that will be incompatible when using conventional heat treatments that require long firing times.

4.5 Commercial impact

The incentives to use 3D printing are cost-effectiveness (stock materials are often expensive), reduction of waste and ease of design implementation (printing of pre-designed structures). DIW has definitive potential on the easy and fast fabrication of prototypes for testing. However, when it comes to practical commercial application it will be necessary to take full advantage of its capabilities for the fabrication of complex structures that are not accessible by other processing technologies. It is unlikely that DIW will displace well established, mature technologies for mass production such as roll to roll fabrication of batteries but it may open new opportunities in the ad hoc design of devices in specific situations and the implementation of true 3D structures designed to optimize performance. In this respect, it should also be considered that the fabrication of three-dimensional devices also imposes constraints in subsequent packaging steps. An example is the field of lithium ion batteries where the potential to fully print high performance LIBs with nearly arbitrary form factors has been demonstrated. However, the papers often report printing of almost flat 2D configurations that could be easily accessible with other technologies in order to allow sealing of the thick electrodes that contain the active materials.

4.6 Sustainability

Conventional manufacturing processes can be very energy intensive and generate large amounts of waste. Additive manufacturing technologies, and in particular direct ink writing, can address some of these issues and play an important role in the development of more sustainable industries. They can be used to build parts on demand without moulds or machining, reducing consumption of raw materials and emissions. DIW presents the additional advantages of enabling the use of eco-friendly, often water-based, inks and low energy consumption as extrusion happens at room temperature using gantry robots. However, when looking at the development of cleaner, more sustainable manufacturing we should take into account that after shaping, consolidation usually requires energy-demanding treatments (e.g. drying or sintering). It is necessary to take a holistic approach in which additive manufacturing can play a key part. As shown in this paper, in the case of DIW this could involve the minimization of post-printing procedures, the integration of shaping and consolidation in a single step or the combination with new, more efficient sintering technologies (e.g. field assisted or cold sintering).

Multi-material additive manufacturing will also contribute to a more sustainable society by opening new possibilities on the fabrication of structures and devices. Some of the applications have been reviewed here and include ultralight structures, longer-lasting implants and tissue engineering scaffolds with improved bio-integration, wearable sensors or novel devices for energy storage and generation. All these technologies have the potential to change the way we store and consume energy and to provide longer lasting, more efficient solutions for a wide range of fields from health care to construction and transportation. Here DIW has an advantage over other additive manufacturing technologies in that, despite the technical challenges, the integration of different materials in a single processing step is conceptually straightforward. As we have shown, these challenges are being currently addressed and numerous solutions are being developed. With these solutions DIW enables the rapid fabrication and testing of new design concepts, accelerating discovery in a way that is not easily accessible with other techniques. Some of these concepts may be commercially implemented using other technologies but DIW could also be play a role in manufacturing. It already allows the ad hoc fabrication of devices for specific applications in relatively small batches (e.g. custom designed scaffolds or sensors). However, the issues of upscaling device size and reducing production times to enable large batches are still barriers for mass implementation. Solving these problems will open new opportunities to create a more sustainable economy.

The challenges are multiple but multi-material direct ink writing offers a unique space for collaborative research. This collaboration should include not only those working on processing or machine design but also the end users. Their needs can offer guidelines for technique development. It is often not only about enhancing printing precision or fabrication speeds, but also building systems that are reliable and easy to use in a production environment. The outcomes of this research will have an extremely broad impact and support progress in many applications from health, chemistry and materials science to engineering and entertainment thus the establishment of wider multi-disciplinary collaborations would be hugely beneficial.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

ES and IE would like to acknowledge the EPSRC Future Manufacturing Hub in Manufacture using Advanced Powder Processes (MAPP) EP/P006566/1.

Notes and references

  1. U. Nations, The 2030 Agenda for Sustainable Development, United Nations Department of Economic and Social Affairs, 2015 Search PubMed.
  2. W. Gao, Y. Zhang, D. Ramanujan, K. Ramani, Y. Chen, C. B. Williams, C. C. L. Wang, Y. C. Shin, S. Zhang and P. D. Zavattieri, Comput.-Aided Des., 2015, 69, 65–89 CrossRef.
  3. A. Zhakeyev, P. Wang, L. Zhang, W. Shu, H. Wang and J. Xuan, Adv. Sci., 2017, 4, 1700187 CrossRef PubMed.
  4. S. C. Ligon, R. Liska, J. Stampfl, M. Gurr and R. Mulhaupt, Chem. Rev., 2017, 117, 10212–10290 CrossRef CAS PubMed.
  5. S. C. Daminabo, S. Goel, S. A. Grammatikos, H. Y. Nezhad and V. K. Thakur, Mater. Today Chem., 2020, 16, 100248 CrossRef CAS.
  6. D. D. Gu, W. Meiners, K. Wissenbach and R. Poprawe, Int. Mater. Rev., 2013, 57, 133–164 CrossRef.
  7. T. DebRoy, H. L. Wei, J. S. Zuback, T. Mukherjee, J. W. Elmer, J. O. Milewski, A. M. Beese, A. Wilson-Heid, A. De and W. Zhang, Prog. Mater. Sci., 2018, 92, 112–224 CrossRef CAS.
  8. S. Das, D. L. Bourell and S. S. Babu, MRS Bull., 2016, 41, 729–741 CrossRef.
  9. Z. Chen, Z. Li, J. Li, C. Liu, C. Lao, Y. Fu, C. Liu, Y. Li, P. Wang and Y. He, J. Eur. Ceram. Soc., 2019, 39, 661–687 CrossRef CAS.
  10. H. Li and J. Liang, Adv. Mater., 2020, 32, e1805864 CrossRef PubMed.
  11. C. Zhu, T. Liu, F. Qian, W. Chen, S. Chandrasekaran, B. Yao, Y. Song, E. B. Duoss, J. D. Kuntz, C. M. Spadaccini, M. A. Worsley and Y. Li, Nano Today, 2017, 15, 107–120 CrossRef CAS.
  12. P. Chang, H. Mei, S. Zhou, K. G. Dassios and L. Cheng, J. Mater. Chem. A, 2019, 7, 4230–4258 RSC.
  13. M. P. Browne, E. Redondo and M. Pumera, Chem. Rev., 2020, 120(5), 2783–2810 CrossRef CAS PubMed.
  14. F. Zhang, M. Wei, V. V. Viswanathan, B. Swart, Y. Shao, G. Wu and C. Zhou, Nano Energy, 2017, 40, 418–431 CrossRef CAS.
  15. M. Cheng, R. Deivanayagam and R. Shahbazian-Yassar, Batteries Supercaps, 2020, 3, 130–146 CrossRef CAS.
  16. Y. Z. Zhang, Y. Wang, T. Cheng, L. Q. Yao, X. Li, W. Y. Lai and W. Huang, Chem. Soc. Rev., 2019, 48, 3229–3264 RSC.
  17. A. Ambrosi and M. Pumera, Chem. Soc. Rev., 2016, 45, 2740–2755 RSC.
  18. X. Tian, J. Jin, S. Yuan, C. K. Chua, S. B. Tor and K. Zhou, Adv. Energy Mater., 2017, 7, 1700127 CrossRef.
  19. T. S. Arthur, D. J. Bates, N. Cirigliano, D. C. Johnson, P. Malati, J. M. Mosby, E. Perre, M. T. Rawls, A. L. Prieto and B. Dunn, MRS Bull., 2011, 36, 523–531 CrossRef CAS.
  20. E. MacDonald and R. Wicker, Science, 2016, 353(6307), aaf2093 CrossRef CAS PubMed.
  21. A. Lee, A. Hudson, D. Shiwarski, J. Tashman, T. Hinton, S. Yerneni, J. Bliley, P. Campbell and A. Feinberg, Science, 2019, 365, 482–487 CrossRef CAS PubMed.
  22. S. V. Murphy and A. Atala, Nat. Biotechnol., 2014, 32, 773 CrossRef CAS PubMed.
  23. M. S. Mannoor, Z. Jiang, T. James, Y. L. Kong, K. A. Malatesta, W. O. Soboyejo, N. Verma, D. H. Gracias and M. C. McAlpine, Nano Lett., 2013, 13, 2634–2639 CrossRef CAS PubMed.
  24. A. J. Blake, R. R. Kohlmeyer, J. O. Hardin, E. A. Carmona, B. Maruyama, J. D. Berrigan, H. Huang and M. F. Durstock, Adv. Energy Mater., 2017, 7(14), 1602920 CrossRef.
  25. M. Wei, F. Zhang, W. Wang, P. Alexandridis, C. Zhou and G. Wu, J. Power Sources, 2017, 354, 134–147 CrossRef CAS.
  26. T. S. Wei, B. Y. Ahn, J. Grotto and J. A. Lewis, Adv. Mater., 2018, 30, e1703027 CrossRef PubMed.
  27. V. G. Rocha, E. Garcia-Tunon, C. Botas, F. Markoulidis, E. Feilden, E. D'Elia, N. Ni, M. Shaffer and E. Saiz, ACS Appl. Mater. Interfaces, 2017, 9, 37136–37145 CrossRef CAS PubMed.
  28. B. G. Compton and J. A. Lewis, Adv. Mater., 2014, 26, 5930–5935 CrossRef CAS PubMed.
  29. E. Feilden, C. Ferraro, Q. Zhang, E. Garcia-Tunon, E. D'Elia, F. Giuliani, L. Vandeperre and E. Saiz, Sci. Rep., 2017, 7, 13759 CrossRef PubMed.
  30. J. T. Muth, D. M. Vogt, R. L. Truby, Y. Mengüç, D. B. Kolesky, R. J. Wood and J. A. Lewis, Adv. Mater., 2014, 26, 6307–6312 CrossRef CAS PubMed.
  31. M. Wehner, R. L. Truby, D. J. Fitzgerald, B. Mosadegh, G. M. Whitesides, J. A. Lewis and R. J. Wood, Nature, 2016, 536, 451–455 CrossRef CAS PubMed.
  32. J. E. Smay, J. Cesarano and J. A. Lewis, Langmuir, 2002, 18, 5429–5437 CrossRef CAS.
  33. J. A. Lewis, J. E. Smay, J. Stuecker and J. Cesarano, J. Am. Ceram. Soc., 2006, 89, 3599–3609 CrossRef CAS.
  34. E. Garcia-Tunon, E. Feilden, H. Zheng, E. D'Elia, A. Leong and E. Saiz, ACS Appl. Mater. Interfaces, 2017, 9, 32977–32989 CrossRef CAS PubMed.
  35. A. Corker, H. C. Ng, R. J. Poole and E. Garcia-Tunon, Soft Matter, 2019, 15, 1444–1456 RSC.
  36. R. L. Truby and J. A. Lewis, Nature, 2016, 540, 371–378 CrossRef CAS PubMed.
  37. A. Z. Nelson and R. H. Ewoldt, Soft Matter, 2017, 13, 7578–7594 RSC.
  38. M. Greaves, S. Barg and M. A. Bissett, Batteries Supercaps, 2020, 3, 214 CrossRef CAS.
  39. P. T. Smith, A. Basu, A. Saha and A. Nelson, Polymer, 2018, 152, 42–50 CrossRef CAS.
  40. A. M'barki, L. Bocquet and A. Stevenson, Sci. Rep., 2017, 7, 1–10 CrossRef PubMed.
  41. J. O. Hardin, T. J. Ober, A. D. Valentine and J. A. Lewis, Adv. Mater., 2015, 27, 3279–3284 CrossRef CAS PubMed.
  42. M. A. Skylar-Scott, J. Mueller, C. W. Visser and J. A. Lewis, Nature, 2019, 575, 330–335 CrossRef CAS PubMed.
  43. T. J. Ober, D. Foresti and J. A. Lewis, Proc. Natl. Acad. Sci. U. S. A., 2015, 112, 12293–12298 CrossRef CAS PubMed.
  44. J. M. Ortega, M. Golobic, J. D. Sain, J. M. Lenhardt, A. S. Wu, S. E. Fisher, L. X. Perez Perez, A. W. Jaycox, J. E. Smay and E. B. Duoss, Adv. Mater. Technol., 2019, 4, 1800717 CrossRef CAS.
  45. N. A. Dudukovic, L. L. Wong, D. T. Nguyen, J. F. Destino, T. D. Yee, F. J. Ryerson, T. Suratwala, E. B. Duoss and R. Dylla-Spears, ACS Appl. Nano Mater., 2018, 1, 4038–4044 CrossRef CAS.
  46. A. Nadernezhad, N. Khani, G. A. Skvortsov, B. Toprakhisar, E. Bakirci, Y. Menceloglu, S. Unal and B. Koc, Sci. Rep., 2016, 6, 1–12 CrossRef PubMed.
  47. X. Li, J. M. Zhang, X. Yi, Z. Huang, P. Lv and H. Duan, Adv. Sci., 2019, 6, 1800730 CrossRef PubMed.
  48. S. Nesaei, Y. Song, Y. Wang, X. Ruan, D. Du, A. Gozen and Y. Lin, Anal. Chim. Acta, 2018, 1043, 142–149 CrossRef CAS PubMed.
  49. K. J. Chen, X. Kuang, V. Li, G. Z. Kang and H. J. Qi, Soft Matter, 2018, 14, 1879–1886 RSC.
  50. M. Cheng, Y. Jiang, W. Yao, Y. Yuan, R. Deivanayagam, T. Foroozan, Z. Huang, B. Song, R. Rojaee, T. Shokuhfar, Y. Pan, J. Lu and R. Shahbazian-Yassar, Adv. Mater., 2018, 30, e1800615 CrossRef PubMed.
  51. L. Fieber, J. D. Evans, C. Huang and P. S. Grant, Addit. Manuf., 2019, 28, 344–353 CAS.
  52. K. Chen, L. Zhang, X. Kuang, V. Li, M. Lei, G. Kang, Z. L. Wang and H. J. Qi, Adv. Funct. Mater., 2019, 29, 1903568 CrossRef.
  53. H. Zhu, Y. D. Kim and D. De Kee, J. Non-Newtonian Fluid Mech., 2005, 129, 177–181 CrossRef CAS.
  54. G. Franchin, L. Wahl and P. Colombo, J. Am. Ceram. Soc., 2017, 100, 4397–4401 CrossRef CAS.
  55. B. Dorj, J. E. Won, J. H. Kim, S. J. Choi, U. S. Shin and H. W. Kim, J. Biomed. Mater. Res., Part A, 2013, 101, 1670–1681 CrossRef PubMed.
  56. X. You, J. Yang, M. Wang, J. Hu, Y. Ding, X. Zhang and S. Dong, 2D Materials, 2019, 7(1), 015025 CrossRef.
  57. M. Abshirini, M. Charara, P. Marashizadeh, M. C. Saha, M. C. Altan and Y. Liu, Appl. Nanosci., 2019, 9, 2071–2083 CrossRef CAS.
  58. S. Kim, J. Oh, D. Jeong and J. Bae, ACS Appl. Mater. Interfaces, 2019, 11, 20557–20565 CrossRef CAS PubMed.
  59. R. L. Truby, M. Wehner, A. K. Grosskopf, D. M. Vogt, S. G. M. Uzel, R. J. Wood and J. A. Lewis, Adv. Mater., 2018, 30, e1706383 CrossRef PubMed.
  60. F. Kim, B. Kwon, Y. Eom, J. E. Lee, S. Park, S. Jo, S. H. Park, B.-S. Kim, H. J. Im, M. H. Lee, T. S. Min, K. T. Kim, H. G. Chae, W. P. King and J. S. Son, Nat. Energy, 2018, 3, 301–309 CrossRef CAS.
  61. C. S. Marchi, M. Kouzeli, R. Rao, J. A. Lewis and D. C. Dunand, Scr. Mater., 2003, 49, 861–866 CrossRef.
  62. N. S. Hmeidat, J. W. Kemp and B. G. Compton, Compos. Sci. Technol., 2018, 160, 9–20 CrossRef CAS.
  63. D. Kokkinis, M. Schaffner and A. R. Studart, Nat. Commun., 2015, 6, 8643 CrossRef PubMed.
  64. T. J. Wallin, J. Pikul and R. F. Shepherd, Nat. Rev. Mater., 2018, 3, 84–100 CrossRef.
  65. P. Jiang, Z. Ji, X. Zhang, Z. Liu and X. Wang, Progress in Additive Manufacturing, 2017, 3, 65–86 CrossRef.
  66. Y. Zhang, G. Shi, J. Qin, S. E. Lowe, S. Zhang, H. Zhao and Y. L. Zhong, ACS Appl. Electron. Mater., 2019, 1, 1718–1734 CrossRef CAS.
  67. S. Tibbits, Archit. Des., 2014, 84, 116–121 Search PubMed.
  68. A. S. Gladman, E. A. Matsumoto, R. G. Nuzzo, L. Mahadevan and J. A. Lewis, Nat. Mater., 2016, 15, 413–418 CrossRef.
  69. Y. Kim, H. Yuk, R. Zhao, S. A. Chester and X. Zhao, Nature, 2018, 558, 274–279 CrossRef CAS.
  70. X. Wan, H. Wei, F. Zhang, Y. Liu and J. Leng, J. Appl. Polym. Sci., 2019, 136(44), 48177 CrossRef.
  71. M. Grossman, F. Bouville, K. Masania and A. R. Studart, Proc. Natl. Acad. Sci. U. S. A., 2018, 115, 12698–12703 CrossRef CAS PubMed.
  72. T. P. Niebel, D. Carnelli, M. R. Binelli, R. Libanori and A. R. Studart, J. Mech. Behav. Biomed. Mater., 2016, 60, 367–377 CrossRef CAS PubMed.
  73. J. E. Smay, B. Tuttle and J. C. Iii, in Piezoelectric and Acoustic Materials for Transducer Applications, Springer, US, 2008, pp. 305–318,  DOI:10.1007/978-0-387-76540-2_15.
  74. A. M. Golobic, M. D. Durban, S. E. Fisher, M. D. Grapes, J. M. Ortega, C. M. Spadaccini, E. B. Duoss, A. E. Gash and K. T. Sullivan, Adv. Eng. Mater., 2019, 21(8), 1900147 CrossRef.
  75. Y. L. Xia, Z. L. Lu, A. J. W. Cao, K. Miao, J. Li and D. C. Li, Scr. Mater., 2019, 165, 84–88 CrossRef CAS.
  76. Z. W. Fu, M. Freihart, T. Schlordt, T. Fey, T. Kraft, P. Greil and N. Travitzky, Rapid Prototyp. J., 2017, 23, 423–433 CrossRef.
  77. J. Mueller, J. R. Raney, K. Shea and J. A. Lewis, Adv. Mater., 2018, 30, 1705001 CrossRef.
  78. C. Paredes, F. J. Martinez-Vazquez, A. Pajares and P. Miranda, Ceram. Int., 2019, 45, 19572–19576 CrossRef CAS.
  79. K. Shen, J. Ding and S. Yang, Adv. Energy Mater., 2018, 8, 1800408 CrossRef.
  80. E. Malone, M. Berry and H. Lipson, Rapid Prototyp. J., 2008, 14, 128–140 CrossRef.
  81. L. J. Deiner, C. A. G. Bezerra, T. G. Howell and A. S. Powell, Adv. Eng. Mater., 2019, 21(11), 1900737 CrossRef CAS.
  82. K. Sun, T. S. Wei, B. Y. Ahn, J. Y. Seo, S. J. Dillon and J. A. Lewis, Adv. Mater., 2013, 25, 4539–4543 CrossRef CAS PubMed.
  83. S. Z. Guo, K. Qiu, F. Meng, S. H. Park and M. C. McAlpine, Adv. Mater., 2017, 29, 1701218 CrossRef PubMed.
  84. F. J. Martinez-Vazquez, A. Pajares and P. Miranda, J. Eur. Ceram. Soc., 2018, 38, 2247–2250 CrossRef CAS.
  85. J. A. Lewis, Adv. Funct. Mater., 2006, 16, 2193–2204 CrossRef CAS.
  86. Z. Wang, X. Guan, H. Huang, H. Wang, W. Lin and Z. Peng, Adv. Funct. Mater., 2019, 29(11), 1807569 CrossRef.
  87. A. M. Stanciuc, C. M. Sprecher, J. Adrien, L. I. Roiban, M. Alini, L. Gremillard and M. Peroglio, J. Eur. Ceram. Soc., 2018, 38, 845–853 CrossRef CAS.
  88. I. K. Jones, Z. M. Seeley, N. J. Cherepy, E. B. Duoss and S. A. Payne, Opt. Mater., 2018, 75, 19–25 CrossRef CAS.
  89. A. K. Grosskopf, R. L. Truby, H. Kim, A. Perazzo, J. A. Lewis and H. A. Stone, ACS Appl. Mater. Interfaces, 2018, 10, 23353–23361 CrossRef CAS.
  90. Y. Gao, M. Xu, G. Yu, J. Tan and F. Xuan, Sens. Actuators, A, 2019, 299, 111625 CrossRef CAS.

This journal is © The Royal Society of Chemistry 2020