A dual promotion strategy of interface modification and ion doping for efficient and stable carbon-based planar CsPbBr3 perovskite solar cells

Abstract

Carbon-based all-inorganic cesium lead bromide (CsPbBr3) halide perovskite solar cells (PSCs) have attracted tremendous attention owing to their low cost, simplified preparation, and outstanding stability even under harsh conditions. However, the CsPbBr3 perovskite always suffers from an undesirable crystallization and film morphology with incomplete coverage and numerous grain boundaries. Herein, a novel dual promotion strategy combining interface modification with ion doping is proposed to achieve highly efficient and stable carbon-based planar CsPbBr3 PSCs. A thin CsBr modified layer was first inserted between the compact TiO2 (c-TiO2) and PbBr2 layers, wherein the crystallization of PbBr2 can be enhanced and then assist the growth of perovskite grains can be provided, so that CsPbBr3 films can reduce pinhole generation and accelerate carrier extraction, and decrease the hysteresis effect. Then an appropriate cobalt (Co2+) ion is doped into the CsPbBr3 film, which not only increases the grain size with decreasing grain boundary, but also ameliorates the energy level and recombination. Consequently, the champion power conversion efficiency (PCE) of the CsPbBr3 PSCs reaches up to 8.67% with an increment of about 30%. Moreover, the best-performing PSC without encapsulation also displays excellent humidity and thermal stability, maintaining above 98% of its initial PCE in an air atmosphere after 100 days, and over 95% under heat treatment at 85 °C after 600 hours, respectively. This study provides a promising route to boost the performance of all-inorganic perovskite solar cells.

Graphical abstract: A dual promotion strategy of interface modification and ion doping for efficient and stable carbon-based planar CsPbBr3 perovskite solar cells

Supplementary files

Article information

Article type
Paper
Submitted
28 септ. 2020
Accepted
09 ноем. 2020
First published
10 ноем. 2020

J. Mater. Chem. C, 2020,8, 17211-17221

A dual promotion strategy of interface modification and ion doping for efficient and stable carbon-based planar CsPbBr3 perovskite solar cells

C. Wang, Y. Long, X. Liu, S. Fu, J. Wang, J. Zhang, Z. Hu and Y. Zhu, J. Mater. Chem. C, 2020, 8, 17211 DOI: 10.1039/D0TC04624H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements