A lithium carboxylate grafted dendrite-free polymer electrolyte for an all-solid-state lithium-ion battery

Abstract

A novel solid polymer electrolyte (SPE) was synthesized by a two-step polymerization process followed by mixing with solid lithium bis(trifluoromethane sulfonimide) (LiTFSI) salts, composed of hybrid copolymer matrices grafted with lithium carboxylate branched chains. The target SPE1 was based on the copolymer matrix grafted with a lithium-based precursor of LiDMPA, which was prepared by the reaction between dimethylol propionic acid (DMPA) and LiOH. The results showed that SPE1 had an ionic conductivity of 0.1 mS cm−1 at 25 °C, and displayed an electrochemical stability window up to 5.0 V (vs. Li+/Li) at a temperature of 60 °C. The grafting of LiDMPA onto the copolymer gave the SPE1 electrolyte a special structure to ensure a homogeneous current distribution and Li ion deposition, which successfully inhibited Li dendrite growth. As a result, an all-solid-state LiFePO4/SPE1/Li battery was assembled and it presents better electrochemical performance with a high capacity retention of 98.8% at 0.2C with 127.3 mA h g−1 after 100 cycles at 60 °C, and delivers capacities of 161.1, 86.7 and 54.5 mA h g−1 at temperatures of 80, 40 and 25 °C, respectively. This work provides a promising route to fabricate dendrite-free solid polymer electrolytes for all-solid-state lithium-ion batteries.

Graphical abstract: A lithium carboxylate grafted dendrite-free polymer electrolyte for an all-solid-state lithium-ion battery

Supplementary files

Article information

Article type
Communication
Submitted
27 септ. 2019
Accepted
27 окт. 2019
First published
30 окт. 2019

J. Mater. Chem. A, 2019,7, 25818-25823

A lithium carboxylate grafted dendrite-free polymer electrolyte for an all-solid-state lithium-ion battery

Z. Zhao, Y. Zhang, S. Li, S. Wang, Y. Li, H. Mi, L. Sun, X. Ren and P. Zhang, J. Mater. Chem. A, 2019, 7, 25818 DOI: 10.1039/C9TA10689H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements