Self-supported VO2 arrays decorated with N-doped carbon as an advanced cathode for lithium-ion storage

Abstract

The development of advanced cathodes for lithium-ion batteries (LIBs) with high capacity and large energy density is of significant importance. Herein, we report a facile solvothermal-polymerization approach for the fabrication of self-supported VO2 arrays decorated with N-doped carbon (N–C@VO2). A thin N–C shell obtained from polymerized dopamine was uniformly coated on the solvothermal-synthesized VO2 skeleton, and self-supported composite arrays were formed. The lithium storage performance of the designed N–C@VO2 arrays was thoroughly studied. Due to the enhanced conductivity and more stable structure, the N–C@VO2 arrays exhibited much better reactivity and high-rate capability with a higher capacity (295 mA h g−1vs. 254 mA h g−1 at 1C) and an improved high-rate cycling life (95.3% vs. 91.5% after 500 cycles at 1C) as compared to the pure VO2 arrays. The synergistic effect between the array architecture and the N–C shell is responsible for the performance enhancement due to the accelerated reaction kinetics. Our research shows a new way to fabricate advanced high-capacity cathodes for application in electrochemical energy storage.

Graphical abstract: Self-supported VO2 arrays decorated with N-doped carbon as an advanced cathode for lithium-ion storage

Supplementary files

Article information

Article type
Communication
Submitted
02 дек. 2018
Accepted
17 фев. 2019
First published
18 фев. 2019

J. Mater. Chem. A, 2019,7, 6644-6650

Self-supported VO2 arrays decorated with N-doped carbon as an advanced cathode for lithium-ion storage

M. Chen, X. Liang, F. Wang, D. Xie, G. Pan and X. Xia, J. Mater. Chem. A, 2019, 7, 6644 DOI: 10.1039/C8TA11578H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements