Synthesis, crystal structure, and transport properties of quaternary tetrahedral chalcogenides

Abstract

Quaternary chalcogenides with tetrahedral zinc-blend structure types continue to be of interest for thermoelectrics applications. We report on the synthesis, crystal structure, and high temperature transport properties of Cu2.1Fe0.9SnSe4, Cu2.2Fe0.8SnSe4 and Cu2.2Zn0.2Fe0.6SnSe4. The identity and compositions for each specimen were established using a combination of Rietveld refinement and elemental analysis and indicate that all compositions are homogeneous with the stannite crystal structure. Excess Cu reduces the electrical resistivity, ρ, by an order of magnitude compared with Cu2FeSnSe4 with no significant degradation of the Seebeck coefficient, S. The energy band gaps were estimated from the high temperature S values and indicate that Cu2.1Fe0.9SnSe4 and Cu2.2Fe0.8SnSe4 possess narrow band gaps, 0.18 eV and 0.25 eV, respectively, as compared to most other quaternary chalcogenides. The power factor (PF = S2/ρ) increases with decreasing Fe content. Although Cu2.2Fe0.8SnSe4 possesses a smaller PF than that of Cu2.2Zn0.2Fe0.6SnSe4, a ZT of 0.45 was obtained at 750 K for Cu2.2Fe0.8SnSe4 due to its low thermal conductivity.

Graphical abstract: Synthesis, crystal structure, and transport properties of quaternary tetrahedral chalcogenides

Supplementary files

Article information

Article type
Paper
Submitted
02 јун. 2015
Accepted
09 јул. 2015
First published
09 јул. 2015

J. Mater. Chem. C, 2015,3, 10436-10441

Author version available

Synthesis, crystal structure, and transport properties of quaternary tetrahedral chalcogenides

Y. Dong, L. Wojtas, J. Martin and G. S. Nolas, J. Mater. Chem. C, 2015, 3, 10436 DOI: 10.1039/C5TC01606A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements