Lithium ion transport in solid polymer electrolyte filled with alumina nanoparticles

Abstract

Using a solid polymer electrolyte (SPE) is a promising approach for improving lithium battery durability by suppressing the growth of lithium dendrites. However, the low conductivity at room temperature significantly limits its commercial application. In this work, Al2O3 nanoparticles are used as a filler in a SPE with polyethylene oxide (PEO) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) salt to improve its conductivity, and the resulting structure and transport properties are analyzed in detail using molecular dynamics simulations. The results show that the addition of Al2O3 nanoparticles decreases the crystallinity and increases the degree of order of the PEO chains and makes it easier for Li+ to combine with the PEO chains, thereby significantly enhancing Li+ transport along the PEO chains. Moreover, the addition of Al2O3 provides an additional Li+ transport path, which is the interface between the Al2O3 and PEO chains. Therefore, after adding Al2O3 nanoparticles, the conductivity is increased by 192.25% and 248.94% at 333 and 300 K, respectively, for the SPE with shorter PEO chains and by 225.2% and 285% at 333 and 300 K, respectively, for the SPE with longer PEO chains. Moreover, the enhancement effects of Al2O3 nanoparticles on conductivity are more significant for SPEs with longer PEO chains at lower temperatures.

Graphical abstract: Lithium ion transport in solid polymer electrolyte filled with alumina nanoparticles

Supplementary files

Article information

Article type
Paper
Submitted
25 Janv. 2022
Accepted
14 Marts 2022
First published
15 Marts 2022
This article is Open Access
Creative Commons BY license

Energy Adv., 2022,1, 269-276

Lithium ion transport in solid polymer electrolyte filled with alumina nanoparticles

J. Wang, L. Fan, Q. Du and K. Jiao, Energy Adv., 2022, 1, 269 DOI: 10.1039/D2YA00025C

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements