Robocasting of 3D printed and sintered ceria scaffold structures with hierarchical porosity for solar thermochemical fuel production from the splitting of CO2

Abstract

We report the first ever robocast (additive manufacturing/3D printing) sintered ceria scaffolds, and explore their use for the production of renewable fuels via solar thermochemical fuel production (STFP, water and carbon dioxide splitting using concentrated solar energy). CeO2 catalyst scaffolds were fabricated as 50 mm diameter discs (struts and voids ∼500 μm), sintered at 1450 °C, with specific surface area of 1.58 m2 g−1. These scaffolds have hierarchical porosity, consisting of the macroporous scaffold structure combined with nanoscale porosity within the ceria struts, with mesopores <75 Å and an average pore size of ∼4 nm, and microporosity <2 nm with a microporous surface area of 0.29 m2 g−1. The ceria grains were ≤500 nm in diameter after sintering. STFP testing was carried out via thermogravimetric analysis (TGA) with reduction between 1050–1400 °C under argon, and oxidation at 1050 °C with 50% CO2, gave rapid CO production during oxidation, with high peak CO production rates (0.436 μmol g−1 s−1, 0.586 ml g−1 min−1), for total CO yield of 78 μmol g−1 (1.747 ml g−1). 90% CO was obtained after just 10 min of oxidation, comparing well to reticulated ceria foams, this CO production rate being an order of magnitude greater than that for ceria powders when tested at similar temperatures.

Graphical abstract: Robocasting of 3D printed and sintered ceria scaffold structures with hierarchical porosity for solar thermochemical fuel production from the splitting of CO2

Article information

Article type
Paper
Submitted
20 Janv. 2022
Accepted
06 Marts 2022
First published
07 Marts 2022
This article is Open Access
Creative Commons BY-NC license

Nanoscale, 2022,14, 4994-5001

Robocasting of 3D printed and sintered ceria scaffold structures with hierarchical porosity for solar thermochemical fuel production from the splitting of CO2

B. A. E. Ben-Arfa, S. Abanades, I. M. M. Salvado, J. M. F. Ferreira and R. C. Pullar, Nanoscale, 2022, 14, 4994 DOI: 10.1039/D2NR00393G

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements