Nanostructure-induced L10-ordering of twinned single-crystals in CoPt ferromagnetic nanowires

Abstract

L10-ordered ferromagnetic nanowires with large coercivity are essential for realizing next-generation spintronic devices. Ferromagnetic nanowires have been commonly fabricated by first L10-ordering of initially disordered ferromagnetic films by annealing and then etching them into nanowire structures using lithography. If the L10-ordered nanowires can be fabricated using only lithography and subsequent annealing, the etching process can be omitted, which leads to an improvement in the fabrication process for spintronic devices. However, when nanowires are subjected to annealing, they easily transform into droplets, which is well-known as Plateau–Rayleigh instability. Here, we propose a concept of “nanostructure-induced L10-ordering” of twinned single-crystals in CoPt ferromagnetic nanowires with a 30 nm scale ultrafine linewidth on Si/SiO2 substrates. The driving forces for nanostructure-induced L10-ordering during annealing are atomic surface diffusion and extremely large internal stress at ultrasmall 10 nm scale curvature radii of the nanowires. (Co/Pt)6 multilayer nanowires are fabricated by a lift-off process combining electron-beam lithography and electron-beam evaporation, followed by annealing. Cross-sectional scanning transmission electron microscope images and nano-beam electron diffraction patterns clearly indicate nanostructure-induced L10-ordering of twinned single-crystals in the CoPt ferromagnetic nanowires, which exhibit a large coercivity of 10 kOe for perpendicular, longitudinal, and transversal directions of the nanowires. Two-dimensional grazing incidence X-ray diffraction shows superlattice peaks with Debye–Scherrer ring shapes, which also supports the nanostructure-induced L10-ordering. The fabrication method for nanostructure-induced L10-ordered CoPt ferromagnetic nanowires with twinned single-crystals on Si/SiO2 substrates would be significant for future silicon-technology-compatible spintronic applications.

Graphical abstract: Nanostructure-induced L10-ordering of twinned single-crystals in CoPt ferromagnetic nanowires

Supplementary files

Article information

Article type
Paper
Submitted
14 Sept. 2022
Accepted
06 Okt. 2022
First published
06 Okt. 2022
This article is Open Access
Creative Commons BY-NC license

Nanoscale Adv., 2022,4, 5270-5280

Nanostructure-induced L10-ordering of twinned single-crystals in CoPt ferromagnetic nanowires

R. Toyama, S. Kawachi, J. Yamaura, T. Fujita, Y. Murakami, H. Hosono and Y. Majima, Nanoscale Adv., 2022, 4, 5270 DOI: 10.1039/D2NA00626J

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements