Na-Ion storage in iron hydroxide phosphate hydrate through a reversible crystalline-to-amorphous phase transition

Abstract

Iron(III) hydroxide phosphate hydrate Fe1.13(PO4)(OH)0.39(H2O)0.61 is investigated for the first time as a Na-ion battery cathode, which reveals that the material exhibits similar storage capacities for Na- and Li-ions at relatively low current rates (i.e. C/10). Interestingly, operando X-ray diffraction shows that insertion of Na-ions induces a solid solution transition in the crystalline Fe1.13(PO4)(OH)0.39(H2O)0.61 end-member simultaneously with a major amorphization. This result adds to the series of observations of phosphate-based materials undergoing order-disorder transitions during Na-ion storage. Fe1.13(PO4)(OH)0.39(H2O)0.61 is thus ideal for enhancing our knowledge on such phenomena. To this end, using total X-ray scattering with pair distribution function analysis, we show that the amorphous phase is Na-rich NaxFe1.13(PO4)(OH)0.39(H2O)0.61 with the local [FeO6]-[PO4] motif retained but with coherence lengths of only ca. 0.6 nm. Our investigation also reveals that the crystallinity of Fe1.13(PO4)(OH)0.39(H2O)0.61 is regained upon Na-extraction (battery recharge), i.e. the order-disorder transition is reversible.

Graphical abstract: Na-Ion storage in iron hydroxide phosphate hydrate through a reversible crystalline-to-amorphous phase transition

Supplementary files

Article information

Article type
Paper
Submitted
07 Marts 2020
Accepted
26 Maijs 2020
First published
29 Maijs 2020

Nanoscale, 2020,12, 12824-12830

Author version available

Na-Ion storage in iron hydroxide phosphate hydrate through a reversible crystalline-to-amorphous phase transition

C. Henriksen, M. A. Karlsen, C. L. Jakobsen and D. B. Ravnsbæk, Nanoscale, 2020, 12, 12824 DOI: 10.1039/D0NR01922D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements