Improved breakdown strength and energy storage density of a Ce doped strontium titanate core by silica shell coating

Abstract

For single phase dielectric ceramics prepared using a traditional solid state method, the conflict between high dielectric permittivity and low breakdown strength has always limited the improvement of energy storage density. Here, we design a core–shell structure of Sr0.985Ce0.01TiO3 (SCT)@x wt% SiO2 combining a high dielectric permittivity core with an insulating shell material. The sample of x = 3 wt% sintered at 1300 °C has the largest energy storage density ∼2.23 J cm−3. The effects that different amounts of SiO2 have on phase, microstructure, dielectric and energy storage properties were investigated using X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy with energy dispersive X-ray spectrum (SEM-EDS) and dielectric measurements. As verified by finite element simulations, the energy storage properties are mainly governed by the electric field distribution owing to the introduction of a high dielectric permittivity core (SCT) in a low permittivity shell. The shell material provides an electrical shielding effect around the core, resulting in significant reduction in the field strength within the core material. A comparison of experimental and simulated results is also shown, which is in good agreement with the breakdown properties.

Graphical abstract: Improved breakdown strength and energy storage density of a Ce doped strontium titanate core by silica shell coating

Supplementary files

Article information

Article type
Paper
Submitted
29 Jūn. 2018
Accepted
24 Jūl. 2018
First published
27 Jūl. 2018

J. Mater. Chem. C, 2018,6, 9130-9139

Improved breakdown strength and energy storage density of a Ce doped strontium titanate core by silica shell coating

J. Qi, M. Cao, J. P. Heath, J. S. Dean, H. Hao, Z. Yao, Z. Yu and H. Liu, J. Mater. Chem. C, 2018, 6, 9130 DOI: 10.1039/C8TC03181A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements