Synthesis and characterization of waterborne polyurethane containing poly(3-hydroxybutyrate) as new biodegradable elastomers

Abstract

Poly(3-hydroxybutyrate) (PHB) is a biodegradable polymer with good biocompatibility. The crystalline and brittle nature has limited its processing for further applications. In this study, PHB diols were employed as a part of the soft segment to synthesize waterborne polyurethane (PU). Poly(ε-caprolactone) (PCL) diol was used as the major soft segment (80 mol%) and blended with PHB diol (20 mol%) at the beginning of the synthesis. PHB diols with three different molecular weights (1352, 1679, and 2062 g mol−1) were respectively used. The microphase separation was adjusted by changing the prepolymerization temperature. Physico-chemical characterization revealed that the PCL–PHB-based PUs had 3–7% crystallinity, good flexibility (∼1–8 MPa modulus and ∼500% elongation), and some shape memory behavior (up to ∼80% shape recovery). The use of higher molecular weight PHB diol (2062 g mol−1) and a prepolymerization temperature at 95 °C gave rise to PU with the best properties in general. The latter PU also showed excellent biodegradation (52% weight loss after 30 days) and biocompatibility (capsule thickness ∼23 μm) in vivo. Furthermore, the PU dispersion could be electrospun into nanofibers (∼400 nm diameter) without the use of organic solvents. Therefore, the eco-friendly PU containing PHB blocks has good mechanical properties, processing abilities, and biocompatibility, and may be a new category of biodegradable elastomers and potential biomaterials for cardiovascular and other medical applications.

Graphical abstract: Synthesis and characterization of waterborne polyurethane containing poly(3-hydroxybutyrate) as new biodegradable elastomers

Supplementary files

Article information

Article type
Paper
Submitted
27 Aug. 2015
Accepted
30 Okt. 2015
First published
16 Nov. 2015

J. Mater. Chem. B, 2015,3, 9089-9097

Synthesis and characterization of waterborne polyurethane containing poly(3-hydroxybutyrate) as new biodegradable elastomers

S. Hsu, C. Hsieh and Y. Sun, J. Mater. Chem. B, 2015, 3, 9089 DOI: 10.1039/C5TB01773D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements