Roll-coating fabrication of flexible large area small molecule solar cells with power conversion efficiency exceeding 1%

Abstract

All solution-processed flexible large area small molecule bulk heterojunction solar cells were fabricated via roll-coating technology. Our devices were produced from slot-die coating on a lab-scale mini roll-coater under ambient conditions without the use of spin-coating or vacuum evaporation methods. Four diketopyrrolopyrrole based small molecules (SMs 1–4) were utilized as electron donors with (6,6)-phenyl-C61-butyric acid methyl ester as an acceptor and their photovoltaic performances based on roll-coated devices were investigated. The best power conversion efficiency (PCE) of 1.01%, combined with an open circuit voltage of 0.73 V, a short-circuit current density of 3.13 mA cm−2 and a fill factor of 44% were obtained for the device with SM1, which was the first example reported for efficient roll-coating fabrication of flexible large area small molecule solar cells with PCE exceeding 1%. In addition, roll-coated devices based on SMs 2–4 also showed good performances with PCEs of 0.41%, 0.54%, and 0.31%, respectively. Our results prove that small molecules have the potential for use in industries for large scale production of efficient organic solar cells.

Graphical abstract: Roll-coating fabrication of flexible large area small molecule solar cells with power conversion efficiency exceeding 1%

Article information

Article type
Paper
Submitted
11 Seb 2014
Accepted
24 Seb 2014
First published
25 Seb 2014

J. Mater. Chem. A, 2014,2, 19809-19814

Roll-coating fabrication of flexible large area small molecule solar cells with power conversion efficiency exceeding 1%

W. Liu, S. Liu, N. K. Zawacka, T. R. Andersen, P. Cheng, L. Fu, M. Chen, W. Fu, E. Bundgaard, M. Jørgensen, X. Zhan, F. C. Krebs and H. Chen, J. Mater. Chem. A, 2014, 2, 19809 DOI: 10.1039/C4TA04733H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements