Atomic layer deposition of vanadium oxide films for crystalline silicon solar cells

Abstract

Transition metal oxides (TMOs) are promising materials to develop selective contacts on high-efficiency crystalline silicon solar cells. Nevertheless, the standard deposition technique used for TMOs is thermal evaporation, which could add potential scalability problems to industrial photovoltaic fabrication processes. As an alternative, atomic layer deposition (ALD) is a thin film deposition technique already used for dielectric deposition in the semiconductor device industry that has a straightforward up scalable design. This work reports the results of vanadium oxide (V2O5) films deposited by ALD acting as a hole-selective contact for n-type crystalline silicon (c-Si) solar cell frontal transparent contact without the additional PECVD passivating layer. A reasonable specific contact resistance of 100 mΩ cm2 was measured by the transfer length method. In addition, measurements suggest the presence of an inversion layer at the c-Si/V2O5 interface with a sheet resistance of 15 kΩ sq−1. The strong band bending induced at the c-Si surface was confirmed through capacitance–voltage measurements with a built-in voltage value of 683 mV. Besides low contact resistance, vanadium oxide films provide excellent surface passivation with effective lifetime values of up to 800 μs. Finally, proof-of-concept both-side contacted solar cells exhibit efficiencies beyond 18%, shedding light on the possibilities of TMOs deposited by the atomic layer deposition technique.

Graphical abstract: Atomic layer deposition of vanadium oxide films for crystalline silicon solar cells

Supplementary files

Article information

Article type
Paper
Submitted
06 Sep 2021
Accepted
05 Okt 2021
First published
12 Okt 2021
This article is Open Access
Creative Commons BY license

Mater. Adv., 2022,3, 337-345

Atomic layer deposition of vanadium oxide films for crystalline silicon solar cells

E. R. Costals, G. Masmitjà, E. Almache, B. Pusay, K. Tiwari, E. Saucedo, C. J. Raj, B. C. Kim, J. Puigdollers, I. Martin, C. Voz and P. Ortega, Mater. Adv., 2022, 3, 337 DOI: 10.1039/D1MA00812A

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements