Mn dopant induced high-valence Ni3+ sites and oxygen vacancies for enhanced water oxidation

Abstract

Cost effective and durable electrocatalysts are urgently required in the oxygen evolution reaction (OER), a critical process in electrochemical energy storage and conversion devices. Conventional catalysts involve the alloying of rare elements, limiting their wide applications. In this paper, Mn doped ultrathin Ni–Fe–O nanosheets are prepared and demonstrated as an efficient OER catalyst. Mn dopant induces the generation of high valence state Ni3+ sites and an increased oxygen vacancy concentration in the Mn–Ni–Fe–O nanosheets, thus achieving enhanced OER kinetics. Experimentation of various dopant concentrations reveals that 2 wt% Mn doping is optimal for OER catalytic performance, achieving low overpotentials of 225 mV at a current density of 10 mA cm−2 and 297 mV at 100 mA cm−2, respectively, a small Tafel slope of 38.2 mV dec−1, and excellent stability in an alkaline medium, which is superior to pristine Ni–Fe–O nanosheets and the state-of-the-art RuO2 catalyst.

Graphical abstract: Mn dopant induced high-valence Ni3+ sites and oxygen vacancies for enhanced water oxidation

Supplementary files

Article information

Article type
Research Article
Submitted
06 میٔ 2020
Accepted
28 میٔ 2020
First published
28 میٔ 2020

Mater. Chem. Front., 2020,4, 1993-1999

Mn dopant induced high-valence Ni3+ sites and oxygen vacancies for enhanced water oxidation

Y. Zhang, Z. Zeng and D. Ho, Mater. Chem. Front., 2020, 4, 1993 DOI: 10.1039/D0QM00300J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements