Non-classical growth of brookite nanorods

Abstract

To understand the growth processes of the brookite phase under hydrothermal conditions, several series of the samples were prepared, with varying temperatures, durations of the synthesis, precursor types and concentrations. A titanium lactate complex and amorphous hydrated titania were used as precursors. The samples were thoroughly characterized by XRD: integral intensities of the fitted peaks were used for the determination of the degree of crystallinity, phase composition and anisotropy of the particles. A series for which the duration of the synthesis was varied has shown that, at the initial stage, only amorphous and anatase phases were formed from the titanium lactate complex, while the brookite phase appeared after 4 hours of synthesis and its content grew with increasing synthesis time, at the expense of the anatase and amorphous phases. In all the cases when synthetic conditions allowed for brookite formation, the size of anatase crystallites was smaller than 19 nm, and the size of brookite particles was larger than 11 nm. A detailed HRTEM study of brookite particles has shown that they have pores and are built from several blocks. These results indicate that, under hydrothermal conditions, the formation of the brookite phase occurs due to a non-classical oriented attachment growth mechanism.

Graphical abstract: Non-classical growth of brookite nanorods

Supplementary files

Article information

Article type
Paper
Submitted
04 میٔ 2019
Accepted
18 اگست 2019
First published
29 اگست 2019

CrystEngComm, 2019,21, 5673-5681

Non-classical growth of brookite nanorods

I. V. Kolesnik, D. A. Kozlov, A. S. Poluboyarinov, A. V. Garshev and V. K. Ivanov, CrystEngComm, 2019, 21, 5673 DOI: 10.1039/C9CE00682F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements