Electrodeposited thin-film CuxSb anodes for Li-ion batteries: enhancement of cycle life via tuning of film composition and engineering of the film-substrate interface

Abstract

Electrodeposited Cu–Sb thin films on Cu and Ni substrates are investigated as alloy anodes for Li-ion batteries to elucidate the effects of both the film composition and substrate interactions on anode cycling stability and lifetime. Thin films of composition CuxSb (0 < x < 2) exhibit the longest cycle lifetimes nearest x = 1. Additionally, the Cu–Sb films exhibit shorter cycle lifetimes when electrodeposited onto Cu substrates when compared to equivalent films on Ni substrates. Ex situ characterization and differential capacity analysis of the anodes reveal that significant interdiffusion occurs during cycling between pure Sb films and Cu substrates. The great extent of interdiffusion results in mechanical weakening of the film–substrate interface that exacerbates film delamination and decreases cycle lifetimes of Cu–Sb films on Cu substrates regardless of the film's composition. The results presented here demonstrate that the composition of the anode alone is not the most important predictor of long term cycle stability; the composition coupled with the identity of the substrate is key. These interactions are critical to understand in the design of high capacity, large volume change materials fabricated without the need for additional binders.

Graphical abstract: Electrodeposited thin-film CuxSb anodes for Li-ion batteries: enhancement of cycle life via tuning of film composition and engineering of the film-substrate interface

Supplementary files

Article information

Article type
Paper
Submitted
23 فرؤری 2018
Accepted
19 میٔ 2018
First published
21 میٔ 2018

J. Mater. Chem. A, 2018,6, 12708-12717

Author version available

Electrodeposited thin-film CuxSb anodes for Li-ion batteries: enhancement of cycle life via tuning of film composition and engineering of the film-substrate interface

M. C. Schulze, R. K. Schulze and Amy L. Prieto, J. Mater. Chem. A, 2018, 6, 12708 DOI: 10.1039/C8TA01798K

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements