Optimization of thermoelectric properties of n-type Ti, Pb co-doped SnSe

Abstract

n-Type polycrystalline SnSe with Ti, Pb co-doping was synthesized by combining mechanical alloying (MA) with spark plasma sintering (SPS). It is revealed that Ti is an effective cationic dopant to convert SnSe from a p-type to an n-type semiconductor, and the thermoelectric performance of the Ti-doped SnSe is also improved in comparison with the pristine sample due to an enhanced power factor. Furthermore, after further Pb doping, an obviously improved electrical conductivity together with a moderate Seebeck coefficient can be achieved, which results in an improvement of the power factor with a maximum value of 300 μW m−1 K−2 at 773 K. Meanwhile, the lattice thermal conductivity is significantly reduced because of the enhanced phonon scattering owing to the mass and strain fluctuations. Therefore, a final ZT value of 0.4 was obtained for composition of Sn0.74Pb0.20Ti0.06Se at 773 K, which is a conservative value for n-type SnSe with cationic dopant prepared by the simple preparation process of MA and SPS.

Graphical abstract: Optimization of thermoelectric properties of n-type Ti, Pb co-doped SnSe

Article information

Article type
Research Article
Submitted
26 جوٗلایی 2017
Accepted
22 اگست 2017
First published
23 اگست 2017

Inorg. Chem. Front., 2017,4, 1721-1729

Optimization of thermoelectric properties of n-type Ti, Pb co-doped SnSe

F. Li, W. Wang, X. Qiu, Z. Zheng, P. Fan, J. Luo and B. Li, Inorg. Chem. Front., 2017, 4, 1721 DOI: 10.1039/C7QI00436B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements