Methane synthesis from CO2 and H2O using electrochemical cells with polymer electrolyte membranes and Ru catalysts at around 120 °C: a comparative study to a phosphate-based electrolyte cell

Abstract

Electrochemical cells with fluorine-based polymer electrolyte membranes (PEMs) and Ru catalysts have been investigated for the production of methane (CH4) from CO2 and H2O by using electricity at 120 °C. CH4 was synthesized with a rate of 12 nmol s−1 cm−2 at a current density of 10 mA cm−2 with a CO2 flow of 0.055 mlSTP min−1 in the cathode vessel and with an Ar + H2O flow of 10 mlSTP min−1 + 10 μLliquid min−1 in the anode vessel (STP; standard temperature and pressure at 0 °C and 101.3 kPa, respectively). This rate was corresponding to the current efficiency of ca. 85%, and unreacted H2 and subproducts of CO were obtained with current efficiencies of ca. 14 and 1%, respectively. The properties of temperature and current density dependence were discussed in this article. The present system exhibits significantly higher selectivity in synthesizing CH4 compared to electrochemical CO2 reduction systems at the electrode/electrolyte interfaces. Electrochemical CO2 reduction did not take place in the present system, and the importance of the combination of water electrolysis and catalytic methanation at solid/gas interfaces was proposed. A comparative study between phosphate (CsH2PO4/SiP2O7) at 250 °C and polymer electrolytes at 120 °C was performed and the possibility for practical applications of both systems was discussed.

Graphical abstract: Methane synthesis from CO2 and H2O using electrochemical cells with polymer electrolyte membranes and Ru catalysts at around 120 °C: a comparative study to a phosphate-based electrolyte cell

Supplementary files

Article information

Article type
Communication
Submitted
31 7 2023
Accepted
15 10 2023
First published
16 10 2023
This article is Open Access
Creative Commons BY license

Sustainable Energy Fuels, 2023,7, 5336-5341

Methane synthesis from CO2 and H2O using electrochemical cells with polymer electrolyte membranes and Ru catalysts at around 120 °C: a comparative study to a phosphate-based electrolyte cell

R. Sagara, R. Hayashi, A. Hirata, S. Nagaishi and J. Kubota, Sustainable Energy Fuels, 2023, 7, 5336 DOI: 10.1039/D3SE00985H

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements