Sulfidation and NaOH etching in CoFeAl LDH evolved catalysts for an efficient overall water splitting in an alkaline solution

Abstract

In this study, a hierarchical interconnected porous metal sulfide heterostructure was synthesized from CoFeAl layered double hydroxides (LDHs) by a two-step hydrothermal process (sulfidation and a NaOH etching process). Among the as-made samples, the CoFeAl-T-NaOH electrode exhibited excellent oxygen and hydrogen evolution reaction catalytic activities with overpotentials of 344 mV and 197 mV at the current density of 100 mA cm−2, respectively. Meanwhile, small Tafel slopes of 57.7 mV dec−1 and 106.5 mV dec−1 for water oxidation and hydrogen evolution were observed for the CoFeAl-T-NaOH, respectively. Serving as both the cathode and anode for overall water splitting, the CoFeAl-T-NaOH electrode reached a current density of 10 mA cm−2 at a cell voltage of 1.65 V with excellent stability. The enhanced electrocatalytic activity could be attributed to: the hierarchical interconnected nanosheet structure facilitating mass transport; the porous structure promoting electrolyte infiltration and reactant transfer; the heterojunction accelerating charge transfer; and the synergistic effect between them. This study offered a new clue for in situ synthesizing porous transition-metal based heterojunction electrocatalysts with a careful tuning of the sequence of sulfuration and alkaline etching to enhance the electrocatalytic performance.

Graphical abstract: Sulfidation and NaOH etching in CoFeAl LDH evolved catalysts for an efficient overall water splitting in an alkaline solution

Supplementary files

Article information

Article type
Paper
Submitted
20 3 2023
Accepted
25 4 2023
First published
25 4 2023

Nanoscale, 2023,15, 9049-9059

Sulfidation and NaOH etching in CoFeAl LDH evolved catalysts for an efficient overall water splitting in an alkaline solution

X. Deng, S. Wang, Y. Liu, J. Cao, J. Huang and X. Shi, Nanoscale, 2023, 15, 9049 DOI: 10.1039/D3NR01276J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements