Distortion induced structural characteristics of Ba2R2/3TeO6 (R = Y, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) double perovskites and their multifunctional optical properties for lighting and ratiometric temperature sensing

Abstract

Group theoretical predictions obtained from Raman and IR spectra emphasize the structures of B-site ordered double perovskites Ba2R2/3TeO6 (R = Y, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) with ubiquitous BO6 or B′O6 octahedral tilting are monoclinic (P21/n), which was further confirmed via the Rietveld refinement of XRD patterns. The wide band gaps of these compounds were consistent with their ability to absorb UV radiation and hence their potential to act as photoluminescent host materials. Photoluminescence spectra of Eu3+-activated Ba2Y2/3TeO6, irrespective of substitution at A- or B-sites, yielded a dominant magnetic dipole transition at 592 nm and a less intense electric dipole transition at 610 nm when excited at 276 nm suggested the preference of Eu3+ ions to occupy Y3+ sites. The thermal activation energy of the Ba2Y2/3TeO6:Eu3+ phosphor was 0.15 eV and its relative sensitivity in the temperature range 300–500 K was estimated to have a maximum of 0.18% K−1 at 300 K for FIR measurements, which is better than its decay lifetime counterpart. The red shift and the peak broadening of the high-energy Raman modes at elevated temperatures of Ba2Y2/3TeO6:Eu3+ are due to enhanced B-site octahedral distortions and are correlated with the thermal quenching of Eu3+ emission. Temperature-dependent lifetimes in the range 80–500 K imply intensification of non-radiative relaxation within the limit. Furthermore, the phosphorescence lifetime, color parameters, and JuddOfelt parameters are explained in detail. The multifunctional optical properties of this phosphor can thus be utilized for technological applications, such as solid-state lighting and ratiometric optical thermometry.

Graphical abstract: Distortion induced structural characteristics of Ba2R2/3TeO6 (R = Y, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) double perovskites and their multifunctional optical properties for lighting and ratiometric temperature sensing

  • This article is part of the themed collection: Perovskites

Supplementary files

Article information

Article type
Paper
Submitted
01 7 2020
Accepted
08 12 2020
First published
10 12 2020
This article is Open Access
Creative Commons BY license

Mater. Adv., 2021,2, 1328-1342

Distortion induced structural characteristics of Ba2R2/3TeO6 (R = Y, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) double perovskites and their multifunctional optical properties for lighting and ratiometric temperature sensing

S. C. Lal, J. Isuhak Naseemabeevi and S. Ganesanpotti, Mater. Adv., 2021, 2, 1328 DOI: 10.1039/D0MA00471E

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements