Lithiation/delithiation of silicon heavily doped with boron synthesized using the Czochralski process

Abstract

The effects of B doping and its impurity concentration (1600, 4700, and 12 400 ppm) on the electrochemical lithiation/delithiation of Si, which has the potential to replace graphite currently used as a negative electrode material in Li-ion batteries due to its huge theoretical capacity, were examined using single-crystals synthesized by the Czochralski method. XRD, Raman spectroscopic measurements, and TEM observation identified the substitution of B with Si without any impurity segregation and TOF-SIMS demonstrated that the dopant concentration was homogeneous against the depth direction. The B doping allowed Li insertion into Si at a higher voltage than the undoped Si irrespective of the B concentration, while the first delithiation capacity decreased from 3360 to 2980 mA h g−1 with the concentration increasing from 1600 to 12 400 ppm, despite the increase in electrical conductivity with increasing B doping. This result indicates the electrochemical inertness of B with Li. The heavy B doping of 12 400 ppm caused a decrease in the mechanical durability of Si, resulting in deteriorated electrode performance compared to that of the undoped Si. Even when 5 vol% fluoroethylene carbonate as a film-forming additive was added to the electrolyte and the lithiation capacity (degree of volume change) was restricted to 1000 mA h g−1, a significant improvement was not observed for the undoped Si. On the other hand, the doping at 4700 ppm provided moderate softness to Si so as not to cause the loss of the fracture toughness and its high electrical conductivity was exerted to achieve high performance with a reversible capacity of 1000 mA h g−1 at the 280th cycle.

Graphical abstract: Lithiation/delithiation of silicon heavily doped with boron synthesized using the Czochralski process

Supplementary files

Article information

Article type
Paper
Submitted
10 Қаң. 2023
Accepted
19 Сәу. 2023
First published
20 Сәу. 2023
This article is Open Access
Creative Commons BY license

Energy Adv., 2023,2, 813-819

Lithiation/delithiation of silicon heavily doped with boron synthesized using the Czochralski process

M. Shimizu, K. Kimoto, A. Kikuchi, T. Taishi and S. Arai, Energy Adv., 2023, 2, 813 DOI: 10.1039/D3YA00021D

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements