High-performance spinel NiMn2O4 microspheres self-assembled with nanosheets by microwave-assisted synthesis for supercapacitors

Abstract

Spinel NiMn2O4 microspheres self-assembled with nanosheets directly grown on a 3D nickel foam were successfully prepared by a facile microwave-assisted hydrothermal process. The structural and morphology evolution behavior and the charge storage mechanism of the as-prepared samples were thoroughly characterized and assessed. It was found that the formation of the product occurred in a stepwise manner, and the steps involved were nucleation, regular growth, and a self-assembly process (from nanosheets to small microspheres and further aggregation to large microspheres), resulting in a flower-like microsphere structure. Furthermore, a study on the energy storage mechanism of the prepared spinel NiMn2O4 indicated that the diffusion-controlled process dominated charge storage at low scan rates, while the capacitive process was dominant as the scan rate increased. As a result, the as-prepared NiMn2O4 showed high specific capacitance up to 768.9 F g−1 at 1 A g−1 when measured by a charge–discharge test and excellent cycling stability (85.8% capacity retention and near 100% Coulombic efficiency after 6000 cycles at 5 A g−1), which indicated that the fabricated products show a great potential in commercial supercapacitor applications.

Graphical abstract: High-performance spinel NiMn2O4 microspheres self-assembled with nanosheets by microwave-assisted synthesis for supercapacitors

Supplementary files

Article information

Article type
Paper
Submitted
15 Қаз. 2019
Accepted
03 Жел. 2019
First published
04 Жел. 2019

CrystEngComm, 2020,22, 1645-1652

High-performance spinel NiMn2O4 microspheres self-assembled with nanosheets by microwave-assisted synthesis for supercapacitors

Y. Sun, J. Zhang, X. Sun and N. Huang, CrystEngComm, 2020, 22, 1645 DOI: 10.1039/C9CE01623F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements