Controllable crystal growth of a NiCo-LDH nanostructure anchored onto KCu7S4 nanowires via a facile solvothermal method for supercapacitor application

Abstract

The application of NiCo-LDHs as electrode materials for supercapacitors has attracted widespread attention. However, pristine NiCo-LDHs always suffer from low conductivity and instability that limit their electrochemical performance in supercapacitors. Herein, we rationally engineered a novel KCu7S4@NiCo-LDH core–shell structure with good capacitive performance using a simple one-step solvothermal method and applied this structure as an electrode material for supercapacitors. KCu7S4 nanowires act as a dependable “skeleton” for supporting the NiCo-LDH nanosheets, thus preventing the aggregation of NiCo-LDHs and improving their conductivity. By controlling the reaction time and the ratio of Ni/Co in the precursor solution, according to the results of electrochemical testing, an optimal composite was obtained with Ni/Co = 2/1 and the reaction time of 8 h; the final KCu7S4@Ni2Co1-LDH composite possessed the high specific capacitance of 1104.5 F g−1 (122.7 mA h g−1) at 2 A g−1, good rate capability of 65.9% when the current density reached up to 10 A g−1, and a long-term stability (an 83.5% capacitance retention after 1000 cycles).

Graphical abstract: Controllable crystal growth of a NiCo-LDH nanostructure anchored onto KCu7S4 nanowires via a facile solvothermal method for supercapacitor application

Supplementary files

Article information

Article type
Paper
Submitted
11 Там. 2019
Accepted
26 Қыр. 2019
First published
26 Қыр. 2019

CrystEngComm, 2020,22, 1602-1609

Controllable crystal growth of a NiCo-LDH nanostructure anchored onto KCu7S4 nanowires via a facile solvothermal method for supercapacitor application

P. Yang, C. Jing, J. C. Liu, K. Chen and Y. X. Zhang, CrystEngComm, 2020, 22, 1602 DOI: 10.1039/C9CE01261C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements