Highly bright and stable white-light-emitting cadmium-free Ag,Mn co-doped Zn–In–S/ZnS quantum dots and their electroluminescence

Abstract

Optimized white light emitting Ag,Mn:Zn–In–S quantum dots (QDs) were synthesized via a simple, scalable, reproducible, and low-cost one-pot non-injection synthetic approach. After coating a thick ZnS shell (∼12 monolayers) on the core QDs, high photoluminescence (PL) quantum yield (QY) up to 76% was achieved and high emission efficiency was retained even when the initially oil-soluble QDs were transferred into aqueous media by ligand replacement. Moreover, both thermal stability and photostability of thick shell-Ag,Mn:Zn–In–S/ZnS QDs were significantly enhanced as compared with those of Ag,Mn:Zn–In–S core QDs due to the suppressed surface defects resulting from the passivation of the dense ZnS layers. White quantum dot light-emitting diodes (QD-LEDs) were fabricated using thick shell Ag,Mn:Zn–In–S/ZnS QDs as single QDs emitter, showing good performance with maximum current efficiency of 1.86 cd A−1 corresponding to external quantum efficiency (EQE) of 0.82% at a current density of 0.065 mA cm−2, color rendering indices (CRI) of 83, Commission International d’Eclairage (CIE) coordinates of (0.344, 0.393) and correlated color temperature (CCT) of 5156 K.

Graphical abstract: Highly bright and stable white-light-emitting cadmium-free Ag,Mn co-doped Zn–In–S/ZnS quantum dots and their electroluminescence

Supplementary files

Article information

Article type
Paper
Submitted
27 Шіл. 2018
Accepted
14 Там. 2018
First published
16 Там. 2018

J. Mater. Chem. C, 2018,6, 10233-10240

Highly bright and stable white-light-emitting cadmium-free Ag,Mn co-doped Zn–In–S/ZnS quantum dots and their electroluminescence

W. Zhang, C. Pan, F. Cao, H. Wang and X. Yang, J. Mater. Chem. C, 2018, 6, 10233 DOI: 10.1039/C8TC03742F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements