Simultaneous polymerization enabled the facile fabrication of S-doped carbons with tunable mesoporosity for high-capacitance supercapacitors

Abstract

A cationic polymerization of 2-thiophenemethanol (ThM) and a sol–gel polycondensation of tetraethylorthosilicate (TEOS) were simultaneously catalyzed by trifluoroacetic acid in a single process step to produce poly(2-thiophenemethanol)/silica (PThM/SiO2) composites. S-Doped mesoporous carbon (S-MC) materials were then achieved by high-temperature carbonization of PThM/SiO2 under an inert atmosphere and subsequent etching off SiO2 in hydrofluoric acid. This in situ crafting process allows us to tailor the porosity of S-MC in the range of 6 to 30 nm. The specific surface area (278–650 m2 g−1) and pore volume (0.15–0.67 cm3 g−1) increase with increasing the feed ratio of TEOS to ThM. Both the specific surface area and pore volume of S-MC are also higher than those of the un-doped mesoporous carbon (MC) materials using furfuryl alcohol as the starting monomer. The S-MC electrodes thus show larger specific capacitance (Cs) values (252 F g−1 at 25 mV s−1 and 125 F g−1 at 0.5 A g−1) compared to the un-doped MC electrode (203 F g−1 at 25 mV s−1 and 110 F g−1 at 0.5 A g−1). The retention of initial Cs for S-MC is 66%, higher than 53% for MC after a 20-fold increase in the scan rate. After 1000 charge/discharge cycles, the Cs retention for S-MC is 97%, also higher than that of MC (93%). As expected, the S-MC electrodes exhibit larger Cs, higher rate performance, and better cycling stability, compared to the MC counterparts and those fabricated in the absence of TEOS by identical experimental processes. Excellent performance can be contributed to the mesoporous morphology in combination with active doping of rich S heteroatoms.

Graphical abstract: Simultaneous polymerization enabled the facile fabrication of S-doped carbons with tunable mesoporosity for high-capacitance supercapacitors

Article information

Article type
Paper
Submitted
30 Қыр. 2017
Accepted
18 Қаз. 2017
First published
18 Қаз. 2017

J. Mater. Chem. A, 2017,5, 23513-23522

Simultaneous polymerization enabled the facile fabrication of S-doped carbons with tunable mesoporosity for high-capacitance supercapacitors

Y. Lu, C. He, P. Gao, S. Qiu, X. Han, D. Shi, A. Zhang and Y. Yang, J. Mater. Chem. A, 2017, 5, 23513 DOI: 10.1039/C7TA08663F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements