Ultrahigh energy storage density and instantaneous discharge power density in BaO–PbO–Na2O–Nb2O5–SiO2–Al2O3 glass-ceramics

Abstract

Compared with traditional dielectric materials, ferroelectric glass-ceramic capacitors have higher energy storage densities and faster discharge speeds. In this study, 21.6BaO–2.4PbO–6Na2O–30Nb2O5–10Al2O3–30SiO2 glass-ceramics and their single-layer capacitors were successfully prepared. A maximum energy storage density of 20.7 J cm−3 was obtained in these glass-ceramics. For glass-ceramics capacitors crystallized at 900 °C, under an electric field of 400 kV cm−1, the maximum instantaneous power density reached was 78.2 MW cm−3 and the discharge time was <35 ns. The effects of crystallization temperature on dielectric energy storage properties were illustrated by investigating the crystallization kinetics, phase evolution, and microstructure of these glass-ceramics. The crystallization process was mainly affected by the bonding strengths of Si–O and Al–O. When the crystallization temperature increased from 850 to 1000 °C, crystallinity increased from 64.5 to 97.3%, Ba2NaNb5O15 and NaNbO3 were precipitated in all samples, and microstructural pores and microcracks gradually appeared. All the results showed that these materials were promising candidates for application in pulse capacitors.

Graphical abstract: Ultrahigh energy storage density and instantaneous discharge power density in BaO–PbO–Na2O–Nb2O5–SiO2–Al2O3 glass-ceramics

Article information

Article type
Paper
Submitted
16 8 2018
Accepted
22 10 2018
First published
23 10 2018

J. Mater. Chem. C, 2018,6, 12608-12614

Ultrahigh energy storage density and instantaneous discharge power density in BaO–PbO–Na2O–Nb2O5–SiO2–Al2O3 glass-ceramics

S. Wang, J. Tian, J. Liu, K. Yang, B. Shen and J. Zhai, J. Mater. Chem. C, 2018, 6, 12608 DOI: 10.1039/C8TC04096F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements