Open Access Article
This Open Access Article is licensed under a
Creative Commons Attribution 3.0 Unported Licence

Ratiometric electrochemical detection of kojic acid based on glassy carbon modified MXene nanocomposite

Gopi Karuppaiah , Aneesh Koyappayil, Anna Go and Min-Ho Lee*
School of Integrative Engineering, Chung-Ang University, 84 Heuseok-ro, Dongjak-Gu, Seoul 06974, Republic of Korea. E-mail: mhlee7@cau.ac.kr

Received 18th August 2023 , Accepted 30th November 2023

First published on 19th December 2023


Abstract

The significance of developing a selective and sensitive sensor for quality control purposes is underscored by the prevalent use of kojic acid (KA) in cosmetics, pharmaceuticals, and food items. KA's utility stems from its ability to inhibit tyrosinase activity. However, the instability of KA and its potential adverse effects have created a pressing need for accurate and sensitive sensors capable of analyzing real samples. This research introduces an electrochemical ratiometric sensor designed to accurately detect KA in actual cosmetic and food samples. The ratiometric sensor offers distinct advantages such as enhanced selectivity, reproducibility, and sensitivity. It achieves this by leveraging the ratio between two output signals, thereby producing reliable and undistorted results. The sensor is constructed by modifying a Glassy Carbon Electrode (GCE) with a nanocomposite consisting of Ti3C2 MXene, Prussian blue, and gold nanoparticles. The incorporation of MXene and gold nanoparticles heightens sensitivity and reduces impedance. Meanwhile, the Prussian blue signal diminishes proportionally with increasing KA concentration, forming the basis for the ratiometric sensing mechanism. The outcomes of the study reveal a broad linear range (1–600 μM), a low detection limit (1 μM), and strong selectivity for KA. These findings suggest the sensor's potential efficacy in quality control across cosmetics, pharmaceuticals, and food products.


1. Introduction

Tyrosinase inhibitors have gained notable attention recently due to their significant role in a variety of cosmetic products and their influence on the food industry, cosmetics, and pharmaceutical sectors.1,2 However, concerns persist regarding their safety, potential for cytotoxicity, and stability issues.3 Among these inhibitors, kojic acid (KA), a well-known compound, has found widespread application in both the cosmetic and pharmaceutical realms. Its discovery traces back to 1907 when Saito first isolated it from Aspergillus oryzae cultures. Yabuta later coined the term “kojic acid” in 1912, while its molecular structure was more comprehensively elucidated in 1924.4 KA offers a multitude of advantages, including its abilities in skin lightening, antibacterial action, inhibition of proliferation, anti-inflammatory effects, and antioxidative properties.5 In the cosmetic industry, KA is prominently acknowledged for its capacity to inhibit tyrosinase, thereby restricting melanin formation (refer to Fig. S1). It is a common component in topical treatments for various skin conditions such as melasma, spots, and brown discolouration resulting from post-inflammatory hyperpigmentation (PIH).5 Beyond this, KA functions as a safeguard against UV radiation and as a preservative, thereby extending the shelf life of cosmetic products.6,7 Combinations of KA with alpha-hydroxy acids are commonly employed in products designed to lighten the skin, combating age spots and freckles. Additionally, the manganese and zinc complexes of KA are attributed to its role as a radioprotective agent against exposure to gamma-rays.8 However, the application of KA is accompanied by significant cytotoxicity and instability issues, prompting further investigations to accurately quantify KA concentrations in cosmetic and food samples.9 Excessive exposure to KA can lead to adverse effects such as allergic reactions, skin irritation, and genotoxicity.5 To adhere to regulatory standards and uphold quality control, it is imperative to precisely monitor the presence and concentration of KA in food, cosmetic, and pharmaceutical products. The Cosmetic Ingredient Review (CIR) has sanctioned a safe usage level of 1% for KA in cosmetic products.6

The detection of KA holds significant implications across diverse industries and applications, constituting a crucial field with extensive practical utility. Enhanced KA sensors, boasting improved sensitivity and selectivity, offer the potential to guarantee the safety and quality of products in industries such as food, cosmetics, and pharmaceuticals. Moreover, they offer valuable insights into disease diagnosis and treatment by precisely monitoring KA levels in biological samples like blood, urine, and saliva. This underscores the vital role of KA sensing as a far-reaching research domain. A variety of sensing techniques, including fluorescence-based,10 spectrophotometry,11 electrochemistry,12 high-performance liquid chromatography,13 and mass spectrometry,14 have been documented for KA determination in food and cosmetic items. Of these, electrochemical methods exhibit high sensitivity, selectivity, cost-effectiveness, and user-friendliness, positioning them as a promising and favoured choice.15,16 However, further research is imperative to enhance their potential applications.

In recent times, notable progress has occurred in the domain of electrochemical sensor applications through the enhancement of 2D materials using metal nanoparticles.17 These nanoparticles integrated into 2D materials serve to amplify the electroactive surface and conductivity, thereby augmenting the sensitivity of electrochemical detection. A specific category of 2D materials, known as MXenes, composed of transition metal carbides/nitrides has attracted considerable scientific attention due to their distinctive chemical and electronic properties, viable synthesis methods, and the capacity for controlled property modulation by adjusting the proportions of M and/or X elements.18 The concept of electrochemical ratiometric sensors, introduced in 2013,19 signifies a significant advancement in the realm of electrochemical biosensors and is presently gaining prominence. Traditional electrochemical sensors typically rely on the absolute magnitude of a solitary signal for both identification and quantification purposes. Conversely, ratiometric electrochemical sensors measure the ratio of electrochemical signals, enabling the determination and quantification of the targeted analyte. This approach yields heightened selectivity, reproducibility, accuracy, and sensitivity, which are essential prerequisites for modern electrochemical sensors.20–23 In this study, we present an on-off mode ratiometric electrochemical sensor tailored for the precise and sensitive detection of KA (Scheme 1). This sensor utilizes a nanocomposite consisting of MXene, Prussian blue, and gold nanoparticles to modify a glassy carbon electrode (GCE). Notably, there exists no prior record of a ratiometric sensor being employed for KA detection in the existing literature.


image file: d3ra05629e-s1.tif
Scheme 1 Schematic representation for the fabrication of GCE/MXene/PB/AuNPs modified electrode for electrochemical ratiometric KA determination.

2. Materials and methods

2.1. Chemicals and reagents

Potassium bromide, iron(III) ferrocyanide (Prussian blue), potassium hexacyanoferrate(III) (ACS reagent, ≥99%), kojic acid (≥98.5%, HPLC), magnesium chloride (anhydrous, ≥98%), glucose, sodium chloride (ACS reagent, ≥99.0%), sodium bicarbonate (ACS reagent, ≥99.7%), trisodium citrate dihydrate, sulfuric acid (ACS reagent, 95.0–98.0%), hydrochloric acid (ACS reagent, 37%), and Nafion perfluorinated resin solution were purchased from Sigma-Aldrich (Korea). Potassium chloride (>99.5%) was purchased from Kanto Chemicals Co., Inc. Gold colloidal nanoparticles with a diameter of 40 nm were sourced from Bore Da Biotech. Phosphate-buffered saline at pH 7.4 was acquired from Thermo Fisher Scientific. Calcium hydroxide was purchased from Daejung Chemicals in Korea, while anhydrous ethyl alcohol with a purity of 99.9% was obtained from Samchun Chemical, Korea. The working glassy carbon electrode (GCE), a spiral platinum counter electrode, and Ag/AgCl reference electrodes were procured from BASi. All the chemicals and buffers were prepared with deionized water with a resistance not less than 18.2 MΩ cm.

2.2. Synthesis of Ti3C2Tx MXene from the MAX phase

The Ti3C2Tx MXene was prepared by the conventional etching of Al atoms from the Ti3AlC2 MAX phase using HF acid (Fig. 1a).24 Briefly, 48% HF was slowly added to 5.0 g of the Ti3AlC2 MAX phase followed by magnetic stirring for 24 hours at room temperature. The resulting MXene suspension was collected and then washed repeatedly with DI water until the suspension reached near neutral pH (pH ≥ 6). The suspension was then sonicated, centrifuged, washed with absolute ethanol, and dried at room temperature.
image file: d3ra05629e-f1.tif
Fig. 1 (a) Schematic diagram of the synthesis of Ti3C2Tx MXene from Ti3AlC2 MAX phase by acid etching method. (b) XRD pattern of Ti3AlC2 MAX phase, Ti3C2Tx MXene, MXene/PB, and MXene/PB/AuNPs nanocomposite. (c) FT-IR spectra of MXene and MXene/PB/AuNPs, and (d) UV-vis spectrum of MXene, MXene/PB, and MXene/PB/AuNPs.

2.3. Fabrication of GCE/MXene/PB/AuNPs/NF electrode

To examine the electrochemical performance of the electrochemical sensor, the working electrode was fabricated. Initially, a glassy carbon electrode (GCE) underwent polishing using 0.05 μm alumina slurry, followed by sonication in deionized water and ethanol. Subsequently, it was dried using a nitrogen stream. The working electrode was formed via the drop-casting technique. Briefly, 5 mg of the synthesized MXene and 2 mg of Prussian blue were dispersed in 1 mL of distilled water through continuous vortexing and sonication for 15 minutes, resulting in PB/MXene solution. Then, 100 μL each of gold nanoparticles and PB/MXene were sonicated together for 20 minutes to create the MXene/PB/AuNPs composite. Ultimately, 4 μL of the assembled GCE/MXene/PB/AuNPs nanocomposite was drop-cast onto the GCE surface and left to dry at room temperature for an hour. A final surface coating using 1% Nafion was applied to the electrode to prevent nanoparticles leaching into the electrolyte during analysis. For the control experiment, GCE, GCE/MXene, GCE/MXene/PB, GCE/MXene/PB/AuNPs, GCE/PB/AuNPs, and GCE/MXene/PB/AuNPs/NF were prepared following the aforementioned procedure. Prior to electrochemical measurements, all prepared electrodes underwent stabilization through repeated cycling in pH 7.4 (0.1 M) until a consistent voltammogram was achieved. Subsequently, the GCE/MXene/PB/AuNPs/NF electrode underwent optimization for optimal performance (see ESI).

2.4. Instrumentation

Field emission transmission electron microscopy (FE-TEM) measurements were made on a JEOL JEM-F200 instrument. Fourier-transform infrared (FTIR) spectra were obtained using a Thermo Scientific Nicolet 6700 with sample pellets prepared by using ultrapure KBr. X-ray diffraction (XRD) analysis was performed on Bruker-AXS New D8-Advance X-ray diffractometer with Cu Kα radiation. Ultraviolet-visible (UV-vis) spectroscopy analysis was performed on a Biotek Synergy H1 microplate reader using 96-well clear polystyrene microplates. X-ray photoelectron spectroscopy analysis was performed on Thermo Fisher Scientific K-alpha+ X-ray photoelectron spectroscope.

Electrochemical analyses were executed using a CHI 660E electrochemical workstation manufactured by CH Instruments, Inc. The analyses included cyclic voltammetry (CV), Differential Pulse Voltammetry (DPV), and impedance analysis. These experiments were conducted using a standard three-electrode setup: a Glassy Carbon Electrode (GCE) modified for the working electrode, a platinum counter electrode in spiral form, and an Ag/AgCl reference electrode. The initial stage of electrochemical assessment involved the gradual modification of the nanocomposite on the GCE surface. This was achieved by employing a CV within a pH 7.4 PBS solution. The potential window ranged from −0.5 to 1.0 V, and the scan rate was fixed at 0.05 V s−1. DPV was employed to investigate the dose responses of different concentrations of KA. The DPV parameters were configured as follows: a scan rate of 20 mV s−1, a pulse amplitude of 50 mV, a pulse width of 0.06 s, and a pulse period of 0.5 s. Impedance analysis spanned a frequency spectrum of 1 to 100[thin space (1/6-em)]000 Hz. Furthermore, the sensitivity and selectivity of the modified electrode were assessed via DPV conducted in a pH 7.4 PBS.

3. Results and discussion

3.1. Material characterization

Preliminary spectral analysis on the synthesized Ti3C2Tx MXene and MXene/PB/AuNPs nanocomposite was performed by XRD, FT-IR, and UV-vis spectroscopy. The crystal structure of the Ti3AlC2 MAX phase, as-synthesized Ti3C2Tx MXene and the MXene/PB/AuNPs nanocomposite was analysed by X-ray diffraction analysis (Fig. 1b). The XRD pattern of the Ti3C2Tx MAX phase was consistent with the pattern of bulk Ti3AlC2 (PDF #52-0875). The HF treatment resulted in a decrease in the structural order as well as crystallinity of the Ti3AlC2 MAX phase. The most intense peak at 39.2°, corresponding to the (1 0 4) crystallographic plane was absent in the XRD pattern of Ti3C2Tx MXene, confirming the removal of the Al layer of atoms from the MAX phase.25 Besides, the XRD patterns of the synthesized MXene were consistent with the simulated spectrum of Ti3C2OH.26 In the XRD spectrum of MXene/PB, the peaks corresponding to 2θ = 17.4°, 24.7°, 35.2°, 39.5°, 43.5°, 50.6°, 53.9°, 57.1°, 66.1°, and 68.8° were assigned to the lattice planes (2 0 0), (2 2 0), (4 0 0), (4 2 0), (4 2 2), (4 4 0), (6 0 0), (6 2 0). (6 4 0), and (6 4 2) reported for Fe4[Fe(CN)6]3 (Prussian blue) cubic crystal system, which is in agreement with the standard XRD pattern (PDF #00-052-1907).27

This result also confirmed the Prussian blue particles inside the nanocomposite. When gold nanoparticles were introduced into the nanocomposite, an additional low-intensity peak was observed at 38.1°, which was assigned to the (1 1 1) plane, matching the JCPDS patterns of pure crystalline gold (JCPDS no. 04-0784). Besides, the (1 1 1) plane was assumed to be the most predominant. The average crystalline size of the Ti3C2Tx, Prussian blue, and gold nanoparticles was calculated by using the Debye–Scherrer equation (eqn (1)).

 
D = /β[thin space (1/6-em)]cos[thin space (1/6-em)]θ (1)
where D is the crystalline size in nm, λ is the X-ray wavelength (0.15406 nm), K is the Scherrer constant (0.9), β is the full width at half maximum (FWHM) in radians, and θ is the peak position in radians. The crystalline size of the Ti3C2Tx MXene, PB NPs, and AuNPs was calculated to be. 4.72 nm, 28.67 nm, and 2.64 nm respectively. FTIR analysis was performed to gain further insights into the chemical functionalities of the nanocomposite. As shown in Fig. 1c, from the FTIR spectra of MXene and MXene/PB/AuNPs nanocomposite, the absorption band for MXene around 3545 cm−1 was likely due to the absorbed water and indicates the hydrophilic nature of the MXene.28 The peaks around 603 and 1529 cm−1 were assigned to Ti–O and C–F respectively. The band at 2091 cm−1 was assigned to the characteristic CN stretching of Fe–CN in Prussian blue.29 The UV-vis spectrum (Fig. 1d) of Ti3C2Tx MXene exhibited no characteristic absorption above 300 nm, consistent with the delaminated thin films of Ti3C2Tx,30 whereas the MXene/PB has shown an intense band centered around 720 nm originating from the charge transfer between Fe2+ and Fe3+ inside Prussian blue, and the MXene/PB/AuNPs have shown an additional peak around 530 nm, characteristic of the surface plasmon resonance (SPR) peak of AuNPs.

The surface chemical composition of the as-synthesized Ti3C2Tx MXene and MXene nanocomposite was analysed by X-ray photoelectron spectroscopy (XPS) (Fig. 2 and S2). From the survey spectrum of the nanocomposite (Fig. S3), the presence of elements titanium, carbon, oxygen, nitrogen, gold, iron, fluorine, and sulphur was confirmed, which was also supported by the elemental mapping results. The deconvoluted spectrum of Ti 2p (Fig. 2a) was composed of peaks cantered around ∼454.6, and ∼457.6 eV corresponding to the Ti–C bond and Ti3+ respectively.31 The peak centered around ∼459 eV corresponds to Ti4+, probably due to TiO4, which also explains the oxide peak in the deconvoluted spectrum of O 1s. The signals from C 1s (Fig. 2b) cantered at ∼284.7, ∼286.2, and ∼288.6 eV were attributed to sp3 carbon, C–O groups, and OC[double bond, length as m-dash]O. The core-level spectrum of O 1s (Fig. 2c) comprised peaks around ∼533.5, ∼532.3, and ∼530.8 eV corresponding to CO, C[double bond, length as m-dash]O, and oxide. As shown in Fig. 2d, the core-level spectrum of Fe 2p was deconvoluted into peaks corresponding to the binding energies of Fe(II)2p1/2, Fe(III)2p1/2, Fe(II)2p3/2, and Fe(III)2p3/2, also confirmed the co-existence of Fe2+ and Fe3+.32 The XPS spectrum of Au 4f (Fig. 2e) fitted by two components around ∼84, and ∼87 eV, attributed to the Au (0) from the AuNPs.33 The deconvoluted core-level spectra of N 1s (Fig. 2f) consist of three peaks at 402.6, 399.2, and 397.5 eV, identifying the existence of the nitrile group of [Fe(CN)6]4−.34 The fluorine fraction of the nanocomposite (Fig. 2g), which was contributed mainly by Nafion was deconvoluted into peaks corresponding to C–F and CF3,35 whereas the sulphur fraction originating from Nafion was deconvoluted into peaks (Fig. 2h) corresponding to C–S, and SO3.36


image file: d3ra05629e-f2.tif
Fig. 2 XPS deconvoluted core-level peaks for (a) Ti 2p, (b) C 1s, (c) O 1s, (d) Fe 2p, (e) Au 4f, (f) N 1s, (g) F 1s, and (h) S 2p.

3.2. Morphology

The morphology of the as-synthesized Ti3C2Tx MXene and MXene nanocomposite was analysed by FE-TEM analysis. As shown in Fig. 3a, a signature accordion-like structure was observed for the Ti3C2Tx MXene. The composition of the MXene and the nanocomposite was also confirmed by energy-dispersive X-ray spectroscopy (EDS) analysis. EDS elemental mapping of MXene confirmed the homogenous distribution of elements titanium, carbon, and oxygen on MXene layers (Fig. 3b–e). The FE-TEM analysis also confirmed the distribution of Prussian blue and gold nanoparticles on the MXene nanolayers (Fig. 3f–h). From the HR-TEM image (Fig. S4), the diffraction fringe with an interlayer spacing of 0.991 nm is indexed to the (0 0 2) lattice plane of Ti3C2Tx MXene.37 As shown in Fig. 3i–p and S5, the elemental analysis on the nanocomposite confirmed the distribution of elements titanium, carbon, oxygen, nitrogen, gold, iron, fluorine, and sulphur, which was consistent with the XPS analysis.
image file: d3ra05629e-f3.tif
Fig. 3 (a) FE-TEM image of Ti3C2Tx MXene, (b) EDS layered image of Ti3C2Tx, and EDS elemental mapping of (c) titanium, (d) oxygen, and (e) carbon. (f) FE-TEM image of Ti3C2Tx/PB/AuNPs nanocomposite showing the distribution of PB NPs, and AuNPs over MXene nanolayers. (g) FE-TEM image of Ti3C2Tx/PB/AuNPs/NF nanocomposite, (h) EDS layered image of Ti3C2Tx/PB/AuNPs/NF, and EDS elemental mapping of (i) titanium, (j) carbon, (k) oxygen, (l) iron, (m) nitrogen, (n) gold, (o) sulphur, and (p) fluorine.

3.3. Preparation and optimization of electrocatalytic properties of GCE/MXene/PB/AuNPs/NF

The electrochemical performance of the MXene nanocomposite for KA detection was investigated by fabricating the MXene nanocomposite modified GCE (GCE/MXene/PB/AuNPs/NF). The prepared GCE/MXene/PB/AuNPs/NF electrode was stored at 4 °C in the refrigerator before use. AuNPs and MXene were well reported to increase the electroactive surface area, thereby increasing the sensitivity of electrochemical sensors. In this work, MXene also served to entrap and stabilize the nanoparticles. The Nafion coating increased the sensitivity by preventing the leaching out of the nanomaterials into the electrolyte solution. The electrode was initially optimized for the optimal performance of the sensor (Fig. S6, ESI).

3.4. Sensing mechanism

In the presence of KA, the oxidation peak around 0 V decreased and another oxidation peak appeared around 0.7 V (vs. Ag/AgCl) in the DPV curve, thereby forming the basis (Ip (0 V)/Ip (0.7 V)) of the on-off mode ratiometric sensor. The impact of pH on the ratiometric response of KA detection using GCE/MXene/PB/AuNPs was investigated across a pH range of 5–9 (Fig. 4a). The oxidation peak current at 0 V, responsible for the Prussian blue oxidation, decreased with a decrease in pH, whereas the oxidation peak at 0.7 V, which is due to KA oxidation, varied with pH changes and a maximum was observed at pH 5. However, since Ip (0 V)/Ip (0.7 V) ratio was found to be higher at pH 7.4 (Fig. 4b), pH 7.4 was selected for the fabrication of the ratiometric sensor. As shown in Fig. 4c, the peak potential (Ep) for KA oxidation at 0.7 V shifted towards the negative as pH increased, indicating the involvement of protons in the current-limiting electrode process. Therefore, a mechanism for the ratiometric sensor was proposed (Fig. S7), which involves two key electrochemical processes occurring at the electrode surface. The first process involves the reduction of Prussian blue to Prussian white, which is responsible for the decrease in oxidation current around ∼0 V, while the second process entails the oxidation of KA and is responsible for the increase in oxidation current around ∼0.7 V. These chemical transformations provide the foundation for the ratiometric sensor, allowing precise measurement of KA in a reliable and consistent manner using the GCE/MXene/PB/AuNPs/NF electrode.
image file: d3ra05629e-f4.tif
Fig. 4 (a) pH dependency studies on the GCE/MXene/PB/AuNPs/NF. (b) Plot of the ratio of peak currents at 0 V and 0.7 V (Ip (0 V)/Ip (0.7 V)) vs. pH, and (c) plot of peak potential vs. pH.

3.5. Performance of the electrochemical ratiometric KA sensor

To optimize the performance of the ratiometric sensor platform, DPV responses of GCE, GCE/MXene, GCE/MXene/PB, GCE/MXene/PB/AuNPs, GCE/PB/AuNPs, and GCE/MXene/PB/AuNPs/NF was recorded in the presence of 100 μM KA. As shown in Fig. 5a, the highest peak current response was shown by the GCE/MXene/PB/AuNPs/NF electrode modification, and consequently selected for the sensor fabrication. The ratiometric KA sensor was fabricated by injecting increasing concentrations of KA into 20 mL of PBS (pH 7.4) and the DPV response was recorded by using the GCE/MXene/PB/AuNPs/NF electrode. A gradual decrease in the peak current around 0 V, and an increase in the peak current around 0.7 V was observed with an increase in the concentration of KA (Fig. 5b). The ratio of the peak current responses (Ip (0 V)/Ip (0.7 V)) was then plotted against the logarithmic concentration of KA. A good linear relationship was observed (R2 = 0.99) between the peak current ratio and the logarithmic KA concentration over the range of 1–600 μM with a limit of detection of 1 μM (Fig. 5c). The results also demonstrated the superior performance of our reported sensor in comparison with the previously reported electrochemical KA detection methods (Table 1).
image file: d3ra05629e-f5.tif
Fig. 5 (a) CV responses of bare GCE, GCE/MXene, GCE/MXene/PB, GCE/MXene/PB/AuNPs, GCE/PB/AuNPs, and GCE/MXene/PB/AuNPs/NF towards 100 μM KA. (b) DPV responses of GCE/MXene/PB/AuNPs/NF towards increasing concentrations of KA, and (c) the corresponding linear calibration plot of vs. logarithmic concentration of KA.
Table 1 Literature comparison of various electrochemical sensors reported for KA detection
Electrode modification Sensing technique Linear range (μM) LOD (μM) Real sample Ref.
CuO/Fe2O3-Chi/GCE Amperometry 0.2–674 0.08 Cosmetics, sauce, vinegar 38
MIP/GCE DPV 0.01–0.2 0.003 Cosmetics samples 39
PVP/ABPE LSV 1.0–100 0.5 Sauce, vinegar 40
Pre-anodized SPCE SWV Up to 260 0.17 Cosmetics samples 41
EPPG electrode LSV 0.75–15 0.23 42
MWNT/ARS/GCE Amperometry 0.4–6 0.1 Sauce, vinegar 43
RGSs/GCE LSV 0.01–0.14 44
GCE SWV 35–250 7.84 Cosmetics samples 45
MWCNTs-SPCE DPV 20–5000 16 Vinegar 12
PGA/GCE CV 8–660 0.8 Bean paste, rice wine 46
Gr-Pt/CS/GCE DPV 0.2–1000 0.2 Sauce, vinegar 47
V2O5/NPs/HMIHPF6/CPE SWV 0.08–500 0.02 Bean paste, rice wine, vinegar 48
CPE/MgO-NPs-/M3BIBr DPV 0.1–700 0.04 Edible oil, chilli sauce 49
TiO2/Fe3O4/MWCNTs/IL-CPE DPV 0.5–300 0.2 Edible oil, chilli sauce 50
NiO/NPs/CPE SWV 5–600 0.8 Urine, serum, vinegar 51
(Hpy)(PF6)/N-CQDs/Fe3O4/CPE DPV 0.03–300 0.008 Tomato sauce, vinegar 52
[Fe(HL)2Cl2]nanocomplex-IL/CPE DPV 0.3–237 0.09 Edible oil, chilli sauce 53
MXene/PB/AuNPs/NF DPV 1–600 1 Cosmetic samples, vinegar This work


3.6. Selectivity and reproducibility of the KA sensor

Selectivity is a crucial parameter for the successful implementation of sensors. A selective sensor can distinguish between the target analyte and other interfering compounds present in the sample matrix, thereby ensuring accurate quantification. The importance of the selectivity for a KA sensor cannot be overemphasized, since inaccurate quantification of KA can result in false positives or false negatives, leading to significant consequences in food safety, cosmetic quality control, and disease diagnosis and treatment. A selective KA sensor can provide accurate results, ensuring the safety and quality of food, cosmetic, and pharmaceutical products, as well as contributing to the development of disease diagnosis and treatment methods. Various interfering compounds and ions such as ethanol, glucose, citrate, Na+, K+, Mg2+, Cl, SO42−, CO32−, and Ca2+ can co-exist in food, pharmaceutical, cosmetic, and biological samples. Therefore, the selectivity of the ratiometric KA sensor was performed in the presence of a higher concentration (1 mM) of interfering molecules and ions. From Fig. 6a and b, it is evident that the tested molecules and ions produced negligible interference on the final response of the ratiometric sensor. The reproducibility of the sensor was evaluated by fabricating five independent electrodes and then testing a known KA concentration within the observed linear range of the sensor. As shown in Fig. 6c, the sensor responses were reproducible with an RSD of 1.8%.
image file: d3ra05629e-f6.tif
Fig. 6 (a) Interference study on the GCE/MXene/PB/AuNPs/NF electrode with 600 μM KA and 1 mM of interfering ions and molecules (Ca2+, Mg2+, K+, SO42−, Na+, Cl, CO32−, citrate, and glucose). (b) The corresponding plot of peak current ratio vs. interferents. (c) Reproducibility test using five GCE/MXene/PB/AuNPs/NF electrodes (inset shows the corresponding plot of peak current ratio vs. electrodes).

3.7. Real sample analysis

To validate the practical application of the developed sensor, real samples, including cosmetics (Kojic acid soap) and food products (Apple cider vinegar) were tested for the presence of KA. A simple and efficient sample preparation method was used to prepare the samples (ESI), and the sensor response toward KA was then measured using the optimized conditions established in the previous sections. The results indicated the presence of KA in the analysed cosmetic sample; however, no KA was detected in the food product. To further assess the accuracy and feasibility of the KA sensing platform, the determination of KA was conducted in real samples by a standard addition method. Three different concentrations of the KA within the linear calibration range of the sensor were prepared in real samples, tested with the sensor, and the percentage recoveries were calculated. As shown in Table 2, the observed recoveries were in the range of 96.2–104.1, and the relative standard deviation (RSD) was in the range 3.1–4.6%. The results indicated reliable detection of KA from the tested cosmetic and food samples. The developed sensor exhibited excellent selectivity towards KA, as there were no significant interferences from other potential interfering compounds present in the samples, confirming the accuracy and reliability of the developed sensor for the determination of KA in real samples. Overall, the developed sensor shows great potential for use as a rapid and efficient tool for monitoring KA levels in cosmetic and food products, thereby ensuring product quality and safety.
Table 2 Recovery experiment on the GCE/MXene/PB/AuNPs/NF electrode using real samples
Sample Detected (μM) Spiked (μM) Found (μM) Recovery (%) RSD (n = 3, %)
Kojic acid soap 19.5 50 69.9 100.5 3.7
100 121.7 101.8 3.6
200 225.6 102.7 4.1
Apple cider vinegar 50 48.1 96.2 4.6
100 102.5 102.5 3.1
200 208.3 104.1 4.3


4. Conclusions

In conclusion, this study presents a new ratiometric electrochemical sensor with outstanding potential for detecting and monitoring KA in real samples. It involves a GCE modified with a nanocomposite of MXene, Prussian blue, and gold nanoparticles. The GCE/MXene/PB/AuNPs/NF sensor exhibits excellent sensitivity, reproducibility, and ability to detect KA in the presence of other interfering ions and molecules, making it a promising sensor for a wide range of analytical applications. Moreover, the sensor's performance in detecting KA in commercial food, and skin-lightening products demonstrates its potential for food, beverage, and cosmetic sample monitoring. The wide linear response (1–600 μM), low detection limit (1 μM), high selectivity, and sensitivity highlight the sensor's broad implications and promising capabilities for various industries and scientific fields, including biomedical, environmental, and chemical analysis. Furthermore, the electrochemical responses, derived from the modification of an atomically smooth glassy carbon electrode (GCE) surface, present an exciting avenue for extending these findings to the realm of practical applications on portable P–O–C devices.

Author contributions

Gopi Karuppaiah: methodology, investigation, data curation, formal analysis. Aneesh Koyappayil: conceptualization, methodology, visualization, writing the original draft & editing. Anna Go: methodology. Min-Ho Lee: funding acquisition, project administration, supervision, writing – review & editing.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

This research was supported by Basic Science Research Program through the National Research Foundation of Korea (NRF) (RS-2023-00243390). This research was also supported by the Ministry of Trade, Industry, and Energy (Grant no. 20008763).

Notes and references

  1. M. S. Fernandes and S. Kerkar, Ann. Microbiol., 2017, 67, 343–358 CrossRef .
  2. S. Zolghadri, A. Bahrami, M. T. Hassan Khan, J. Munoz-Munoz, F. Garcia-Molina, F. Garcia-Canovas and A. A. Saboury, J. Enzyme Inhib. Med. Chem., 2019, 34, 279–309 CrossRef PubMed .
  3. F. Solano, S. Briganti, M. Picardo and G. Ghanem, Pigm. Cell Res., 2006, 19, 550–571 CrossRef .
  4. M. Schaechter, Encyclopedia of Microbiology, Elsevier/Academic Press Amsterdam, Amsterdam SE-, 3rd edn, 2009 Search PubMed .
  5. M. Saeedi, M. Eslamifar and K. Khezri, Biomed. Pharmacother., 2019, 110, 582–593 CrossRef .
  6. V. Phasha, J. Senabe, P. Ndzotoyi, B. Okole, G. Fouche and A. Chuturgoon, Cosmetics, 2022, 9, 64 CrossRef .
  7. C. Yang, Y. Qi, J. Zheng, X. U. Fan, P. Liang and C. Song, J. Food Prot., 2018, 81, 636–645 CrossRef CAS .
  8. S. K. Singh, Curr. Org. Chem., 2020, 24, 354–401 CrossRef .
  9. B. K. Singh, S. H. Park, H.-B. Lee, Y.-A. Goo, H. S. Kim, S. H. Cho, J. H. Lee, G. W. Ahn, J. P. Kim, S. M. Kang and E.-K. Kim, Ann. Dermatol., 2016, 28, 555–561 CrossRef CAS .
  10. P. Hu and H. Wang, J. Chin. Chem. Soc., 2022, 69, 1772–1778 CrossRef CAS .
  11. J. Wang, J. Hu, B. Xiao, T. Yang, J. He and P. Yu, J. Phys.: Conf. Ser., 2022, 2329, 12032 CrossRef .
  12. M. Buleandra, A. A. Rabinca, F. Tache, Z. Moldovan, I. Stamatin, C. Mihailciuc and A. A. Ciucu, Sens. Actuators, B, 2017, 241, 406–412 CrossRef CAS .
  13. Y. Higashi and Y. Fujii, J. Cosmet. Sci., 2012, 63, 205–212 CAS .
  14. T. Y. Kim, J. Y. Jang, S. J. Jeon, H. W. Lee, C.-H. Bae, J. H. Yeo, H. B. Lee, I. S. Kim, H. W. Park and J.-C. Kim, J. Microbiol. Biotechnol., 2016, 26, 1383–1391 CrossRef CAS .
  15. K. Aneesh and S. Berchmans, J. Solid State Electrochem., 2017, 21, 1263–1271 CrossRef CAS .
  16. C. S. Rao Vusa, V. Manju, K. Aneesh, S. Berchmans and A. Palaniappan, RSC Adv., 2016, 6, 4818–4825 RSC .
  17. A. Koyappayil, A. K. Yagati and M.-H. Lee, Biosensors, 2023, 13, 91 CrossRef CAS .
  18. A. Koyappayil, S. G. Chavan, Y.-G. Roh and M.-H. Lee, Biosensors, 2022, 12, 454 CrossRef CAS .
  19. X. Chai, X. Zhou, A. Zhu, L. Zhang, Y. Qin, G. Shi and Y. Tian, Angew. Chem., Int. Ed., 2013, 52, 8129–8133 CrossRef CAS .
  20. T. Yang, R. Yu, Y. Yan, H. Zeng, S. Luo, N. Liu, A. Morrin, X. Luo and W. Li, Sens. Actuators, B, 2018, 274, 501–516 CrossRef CAS .
  21. C. V. Raju, Y. V. Manohara Reddy, C. H. Cho, H. H. Shin, T. J. Park and J. P. Park, Food Chem., 2023, 428, 136811 CrossRef CAS PubMed .
  22. Y. V. Manohara Reddy, J. H. Shin, J. Hwang, D.-H. Kweon, C.-H. Choi, K. Park, S.-K. Kim, G. Madhavi, H. Yi and J. P. Park, Biosens. Bioelectron., 2022, 214, 114511 CrossRef CAS PubMed .
  23. H. Maseed, V. M. Reddy Yenugu, S. S. Devarakonda, S. Petnikota, M. Gajulapalli and V. V. S. S. Srikanth, ACS Appl. Nano Mater., 2023, 6, 18531–18538 CrossRef CAS .
  24. M. Naguib, M. Kurtoglu, V. Presser, J. Lu, J. Niu, M. Heon, L. Hultman, Y. Gogotsi and M. W. Barsoum, Adv. Mater., 2011, 23, 4248–4253 CrossRef CAS .
  25. W. Lv, J. Zhu, F. Wang and Y. Fang, J. Mater. Sci.: Mater. Electron., 2018, 29, 4881–4887 CrossRef CAS .
  26. A. Koyappayil, S. G. Chavan, M. Mohammadniaei, A. Go, S. Y. Hwang and M.-H. Lee, Microchim. Acta, 2020, 187, 277 CrossRef CAS .
  27. X. Zhang, C. Sui, J. Gong, R. Yang, Y. Luo and L. Qu, Appl. Surf. Sci., 2007, 253, 9030–9034 CrossRef CAS .
  28. M. Mahmood, A. Rasheed, I. Ayman, T. Rasheed, S. Munir, S. Ajmal, P. O. Agboola, M. F. Warsi and M. Shahid, Energy Fuels, 2021, 35, 3469–3478 CrossRef CAS .
  29. H. Maaoui, P. Kumar, A. Kumar, G.-H. Pan, R. Chtourou, S. Szunerits, R. Boukherroub and S. L. Jain, Photochem. Photobiol. Sci., 2016, 15, 1282–1288 CrossRef CAS .
  30. A. Pazniak, P. Bazhin, N. Shplis, E. Kolesnikov, I. Shchetinin, A. Komissarov, J. Polcak, A. Stolin and D. Kuznetsov, Mater. Des., 2019, 183, 108143 CrossRef CAS .
  31. M. Ivanovskaya, E. Ovodok, D. Kotsikau, I. Azarko, M. Micusik, M. Omastova and V. Golovanov, RSC Adv., 2020, 10, 25602–25608 RSC .
  32. J. Yang, Z. Huang, B. Yang, H. Lin, L. Qin, M. Nie and Q. Li, J. Mater. Sci., 2021, 56, 3268–3279 CrossRef CAS .
  33. X. Liang, Z. Wang and C. Liu, Nanoscale Res. Lett., 2009, 5, 124 CrossRef PubMed .
  34. Q. Wu, G. Wu, L. Wang, W. Hu and H. Wu, Mater. Sci. Semicond. Process., 2015, 30, 476–481 CrossRef CAS .
  35. H.-L. Hsu, K. R. Leong, I.-J. Teng, M. Halamicek, J.-Y. Juang, S.-R. Jian, L. Qian and N. P. Kherani, Mater., 2014, 7, 5643–5663 CrossRef .
  36. H. Wang, X. Qiu, W. Wang, L. Jiang and H. Liu, Front. Chem., 2019, 7, 855 CrossRef CAS .
  37. Q. Yang, T. Jiao, M. Li, Y. Li, L. Ma, F. Mo, G. Liang, D. Wang, Z. Wang, Z. Ruan, W. Zhang, Q. Huang and C. Zhi, J. Mater. Chem. A, 2018, 6, 18525–18532 RSC .
  38. Z. Yang, Z. Yin and F. Chen, Electrochim. Acta, 2011, 56, 1089–1093 CrossRef CAS .
  39. Y. Wang, J. Tang, X. Luo, X. Hu, C. Yang and Q. Xu, Talanta, 2011, 85, 2522–2527 CrossRef CAS .
  40. X. Yang and H. Zhang, Food Chem., 2007, 102, 1223–1227 CrossRef CAS .
  41. Y. Shih and J.-M. Zen, Electroanalysis, 1999, 11, 229–233 CrossRef CAS .
  42. L. C. S. Figueiredo-Filho, D. A. C. Brownson, O. Fatibello-Filho and C. E. Banks, Analyst, 2013, 138, 4436–4442 RSC .
  43. J. Liu, D. Zhou, X. Liu, K. Wu and C. Wan, Colloids Surf., B, 2009, 70, 20–24 CrossRef CAS .
  44. Y. Wang, D. Zhang and J. Wu, J. Electroanal. Chem., 2012, 664, 111–116 CrossRef CAS .
  45. G. N. Calaça, S. Machado, K. Wohnrath, C. A. Pessoa and N. Nagata, J. Electrochem. Soc., 2015, 162, H847 CrossRef .
  46. X. Ma and M. Chao, Food Anal. Methods, 2014, 7, 1458–1464 CrossRef .
  47. L. Wang, W. Qi, R. Su and Z. He, Food Anal. Methods, 2014, 7, 109–115 CrossRef .
  48. M. Sheikhshoaie, I. Sheikhshoaie and M. Ranjbar, J. Mol. Liq., 2017, 231, 597–601 CrossRef CAS .
  49. Z. Shamsadin-Azad, M. A. Taher, S. Cheraghi and H. Karimi-Maleh, J. Food Meas. Charact., 2019, 13, 1781–1787 CrossRef .
  50. P. M. Jahani, M. Jafari, V. K. Gupta and S. Agarwal, Int. J. Electrochem. Sci., 2020, 15, 5712–5722 CrossRef CAS .
  51. S. Avazpour, A. Pardakhty, E. Nabatian and S. Ahmadzadeh, Bionanoscience, 2020, 10, 502–511 CrossRef .
  52. S. Cheraghi, F. Shalali and M. A. Taher, J. Food Meas. Charact., 2023, 17, 1728–1734 CrossRef .
  53. M. Fazlia and N. Akbarzadeh-T, J. Electrochem. Sci. Eng., 2022, 12, 1179–1192 CAS .

Footnotes

Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d3ra05629e
These authors contributed equally to this work.

This journal is © The Royal Society of Chemistry 2023