Degradation of (La0.8Sr0.2)0.98MnO3−δ–Zr0.84Y0.16O2−γ composite electrodes during reversing current operation

Author affiliations


Reversing-current operation of solid oxide cell (La0.8Sr0.2)0.98MnO3−δ–Zr0.84Y0.16O2−γ (LSM–YSZ) oxygen electrodes is described. Degradation was characterized by impedance spectroscopy in symmetric cells tested at 800 °C in air with a symmetric current cycle with a period of 12 hours. No change in cell resistance could be detected, in 1000 h tests with a sensitivity of ∼1% per kh, at a current density of 0.5 A cm−2 corresponding to an overpotential of 0.18 V. At a current density to 0.6 A cm−2 (0.33 V overpotential) measurable resistance degradation at a rate of 3% per kh was observed, while higher current/overpotential values led to faster degradation. Degradation was observed mainly in the ohmic resistance for current densities of 0.6, 0.8 and 0.9 A cm−2, with little change in the polarization resistance. Polarization degradation, mainly observed at higher current density, was present as an increase in an impedance response at ∼30 kHz, apparently associated with the resistance of YSZ grain boundaries within the electrode. Microstructural and chemical analysis showed significant changes in electrode structure after the current cycling, including an increase in LSM particle size and a reduction in the amount of YSZ and LSM at the electrode/electrolyte interface – the latter presumably a precursor to delamination.

Back to tab navigation

Publication details

The article was received on 09 feb. 2015, accepted on 06 maí 2015 and first published on 27 júl. 2015

Article type: Paper
DOI: 10.1039/C5FD00020C
Author version
Download author version (PDF)
Citation: Faraday Discuss., 2015,182, 365-377

  •   Request permissions

    Degradation of (La0.8Sr0.2)0.98MnO3−δ–Zr0.84Y0.16O2−γ composite electrodes during reversing current operation

    G. A. Hughes, J. G. Railsback, K. J. Yakal-Kremski, D. M. Butts and S. A. Barnett, Faraday Discuss., 2015, 182, 365
    DOI: 10.1039/C5FD00020C

Search articles by author