Immediate soft-tissue adhesion and the mechanical properties of the Ti–6Al–4V alloy after long-term acid treatment

Abstract

Close attachment of soft tissues onto implantable devices inside the body is regarded as an optimal condition for preventing complications (e.g., infections and abscess formation around implants, and the migration of small injectable devices). We have recently reported that an α-type commercially pure Ti (CpTi) film after a long-term acid treatment and air drying showed a remarkable soft tissue adhesiveness immediately (i.e., within a few seconds) after the attachment onto soft tissues. Herein, we conducted acid treatment for (α + β)-type Ti–6Al–4V alloys and compared their mechanical properties and the immediate soft-tissue adhesiveness with α-type CpTi. The acid treatment for Ti–6Al–4V also promoted immediate soft-tissue adhesion, although the treatment was less effective than for CpTi. The tensile strength of acid-treated Ti–6Al–4V was much higher than that of acid-treated CpTi or human skin tissues, although the degree of hydrogen embrittlement was more severe than that for CpTi. These results suggest that the small amount of Al in the major α phase and/or the minor β phase of Ti–6Al–4V has a significant influence not only on the mechanical properties but also on the immediate soft-tissue adhesiveness of Ti-based solid-state adhesives after the acid treatment.

Graphical abstract: Immediate soft-tissue adhesion and the mechanical properties of the Ti–6Al–4V alloy after long-term acid treatment

Supplementary files

Article information

Article type
Paper
Submitted
23 Ապր 2021
Accepted
27 Օգս 2021
First published
27 Օգս 2021

J. Mater. Chem. B, 2021,9, 8348-8354

Immediate soft-tissue adhesion and the mechanical properties of the Ti–6Al–4V alloy after long-term acid treatment

Y. Wang, M. Okada, S. C. Xie, Y. Y. Jiao, E. S. Hara, H. Yanagimoto, T. Fukumoto and T. Matsumoto, J. Mater. Chem. B, 2021, 9, 8348 DOI: 10.1039/D1TB00919B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements