Tri-layered Si/Co3O4/ZnO heterojunction for high-performance visible photodetection

Abstract

Tri-layered heterojunction devices based on oxide thin films are attracting significant attention for ultra-fast visible photodetection. However, the responsivity of these devices is still low. In this work, high performance photodetectors based on a tri-layered heterojunction of n-Si/p-Co3O4/n-ZnO were fabricated. Under no applied bias, a maximum responsivity and detectivity of 14.2 mA W−1 and 1.34 × 1012 Jones were achieved respectively, for a power density of 9.35 mW cm−2. Remarkably, a significant increase in the responsivity of approximately 864% was found when the device was biased at −2 V. This effect is understood based on the coupling of the photovoltaic and pyroelectric effects. Also, upon applying an external bias of −2 V, at a laser power density of 9.35 mW cm−2 and at a chopper frequency of 10 Hz, the device exhibits a detectivity and sensitivity of 3.4 × 1011 Jones and 2.2, respectively, together with a rise and fall time of 4 and 2 μs, respectively. Compared to high performance Al/Si/SnO/ZnO/ITO and Au/pCuI/ZnO devices, our voltage-biased Al/Si/Co3O4/ZnO/ITO devices exhibit a >40% increase in R and >10× higher D*. Furthermore, an important advantage of our PDs is the p-type component, Co3O4, which is more stable and stoichiometric than CuI and SnO, ensuring PD performance that is stable with time. Therefore, n-Si/p-Co3O4/n-ZnO heterojunction devices shows great promise for ultrafast visible photodetection.

Graphical abstract: Tri-layered Si/Co3O4/ZnO heterojunction for high-performance visible photodetection

Supplementary files

Article information

Article type
Paper
Submitted
20 अप्रैल 2024
Accepted
20 मई 2024
First published
20 मई 2024

J. Mater. Chem. C, 2024,12, 8727-8736

Tri-layered Si/Co3O4/ZnO heterojunction for high-performance visible photodetection

L. Domingues, A. R. Jayakrishnan, A. Kaim, K. Gwozdz, M. C. Istrate, C. Ghica, M. Pereira, A. Castro, L. Marques, R. L. Z. Hoye, J. L. MacManus-Driscoll and J. P. B. Silva, J. Mater. Chem. C, 2024, 12, 8727 DOI: 10.1039/D4TC01624F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements