A simple synthesis of nanoporous Sb/C with high Sb content and dispersity as an advanced anode for sodium ion batteries

Abstract

Sodium ion batteries (SIBs) have attracted increasing attention for large-scale energy storage. Among all anodes for SIBs, antimony (Sb) is one of the most attractive ones, but it suffers from a rapid capacity fading because of about 290% volume change upon sodiation/desodiation. Here a facile bottom-up strategy has been developed to prepare nanoporous Sb/C with high Sb content and dispersity via a ball-milling assisted solid state reaction between Sb2O3 and CaC2. The simultaneous and stoichiometric generation of Sb and C facilitates a high dispersion of Sb in, theoretically, 23 wt% carbon. Feeding excess CaC2 can adjust the porosity of the composite, and tailor Sb particles from crystalline (10–20 nm in size) to amorphous (at the subnanometer scale). The synthesized amorphous Sb/C composite exhibits an unprecedented performance for sodium storage. It delivers a high reversible capacity of 480 mA h g−1 at 0.1 A g−1, 403 mA h g−1 after 1000 cycles at 1.0 A g−1, and 283 mA h g−1 after 3000 cycles at 5.0 A g−1. This study may provide a basis for developing high-capacity and long-cycle-life SIBs for practical applications.

Graphical abstract: A simple synthesis of nanoporous Sb/C with high Sb content and dispersity as an advanced anode for sodium ion batteries

Supplementary files

Article information

Article type
Communication
Submitted
18 जनवरी 2018
Accepted
08 फरवरी 2018
First published
09 फरवरी 2018

J. Mater. Chem. A, 2018,6, 5555-5559

A simple synthesis of nanoporous Sb/C with high Sb content and dispersity as an advanced anode for sodium ion batteries

Y. Yuan, S. Jan, Z. Wang and X. Jin, J. Mater. Chem. A, 2018, 6, 5555 DOI: 10.1039/C8TA00592C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements