Honeycomb-like carbon nanoflakes as a host for SnO2 nanoparticles allowing enhanced lithium storage performance

Abstract

While possessing potential advantages as electrodes for lithium-ion batteries, SnO2@carbon composites have been suffering from one common drawback – aggregation of Sn particles during the repeated alloying–dealloying cycles and the resulting pulverization issue. We combat this issue through the fabrication of honeycomb-like SnO2@carbon nanoflakes (SnO2@CNFs) that are able to confine SnO2 nanoparticles within well-separated carbon cavities, so that the Li–Sn alloying–dealloying reaction occurs in the independent microreactors thus avoiding aggregation of Sn metal particles formed. The SnO2 particle size, loading amount and the coverage density are controlled by adjusting the weight ratio between the tin precursor and the CNF. Transmission electron microscopy confirms that the highly graphitic honeycomb-like CNF matrix efficiently buffers and accommodates volume changes of the Li–Sn alloy. Used as anode materials for lithium-ion batteries, the SnO2@CNFs with 66.0 wt% SnO2 display the highest lithium storage capacity, delivering a discharge capacity of 940 mA h g−1 after 150 cycles at 200 mA g−1. For the long-term and high-rate applications, the SnO2@CNFs with 41.5 wt% SnO2 show the best electrochemical performance, delivering a discharge capacity of 400 mA h g−1 at 1 A g−1 after 500 cycles.

Graphical abstract: Honeycomb-like carbon nanoflakes as a host for SnO2 nanoparticles allowing enhanced lithium storage performance

Supplementary files

Article information

Article type
Communication
Submitted
23 जनवरी 2017
Accepted
07 फरवरी 2017
First published
08 फरवरी 2017

J. Mater. Chem. A, 2017,5, 6817-6824

Honeycomb-like carbon nanoflakes as a host for SnO2 nanoparticles allowing enhanced lithium storage performance

H. Wang, J. Wang, D. Cao, H. Gu, B. Li, X. Lu, X. Han, A. L. Rogach and C. Niu, J. Mater. Chem. A, 2017, 5, 6817 DOI: 10.1039/C7TA00772H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements