The solid solution series Tl(V1−xCrx)5Se8: crystal structure, magnetic and thermoelectric properties

Abstract

The crystal structure of single crystalline members of the solid solution series Tl(V1−xCrx)5Se8 (x = 0–1 and Δx = 0.2) was determined and the magnetic and thermoelectric properties of bulk TlV5Se8 were investigated. All compounds crystallize in the pseudo-hollandite-type structure (C2/m) with a nonlinear increase in the unit cell volume due to a simultaneous increase/decrease in the transition metal distances across the edge/face-sharing octahedra. A slight Tl deficiency was found for single crystalline TlV5Se8 and Tl(V0.8Cr0.2)5Se8 as well as for bulk TlV5Se8 according to Rietveld and single crystal structure refinements. The metallic character of bulk TlV5Se8 and its low electrical resistivity compared to poly- and single-crystalline TlCr5Se8 can probably be associated with this probable Tl deficiency. In TlV5Se8, anomalies in the low temperature Seebeck coefficient, i.e. a maximum at T ∼ 14 K and two sign changes at T ∼ 47 K and T ∼ 167 K, were found. Bulk TlV5Se8 is a highly frustrated (f = |θ|/TN ≈ 42 K) Curie–Weiss paramagnet ordering antiferromagnetically (θ = −1287 K) below TN ≈ 31 K with an effective magnetic moment of μ = 2.68 μB corresponding to V3+. Low-field M(H) measurements revealed the existence of a small ferromagnetic component below TN in bulk TlV5Se8 and, despite the observed spin frustration, no spin glass phase was found in this compound.

Graphical abstract: The solid solution series Tl(V1−xCrx)5Se8: crystal structure, magnetic and thermoelectric properties

Article information

Article type
Paper
Submitted
15 जून 2015
Accepted
27 जुलाई 2015
First published
27 जुलाई 2015

J. Mater. Chem. C, 2015,3, 10509-10517

The solid solution series Tl(V1−xCrx)5Se8: crystal structure, magnetic and thermoelectric properties

S. Maier, R. Lefèvre, X. Lin, R. Nunna, D. Berthebaud, S. Hèbert, A. Mar and F. Gascoin, J. Mater. Chem. C, 2015, 3, 10509 DOI: 10.1039/C5TC01766A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements