DOI:
10.1039/D1TC05196B
(Paper)
J. Mater. Chem. C, 2022,
10, 4607-4613
Aggregation-induced emission active thermally-activated delayed fluorescence materials possessing N-heterocycle and sulfonyl groups†
Received
28th October 2021
, Accepted 10th January 2022
First published on 11th January 2022
Abstract
Novel thermally-activated delayed fluorescence (TADF) materials 2Cz2SB and 2Mi2SB, possessing N-heterocycle and arylsulfonyl groups, were synthesized and their photophysical properties in solution and the solid state were characterized. 2Cz2SB and 2Mi2SB exhibit typical TADF characteristics and aggregation-induced emission or crystallization-induced emission behaviour. Specifically, they display a blueshift of photoluminescence wavelength and an increase in photoluminescence quantum yield (ΦPL) in the aggregate and solid states, owing to suppression of thermal deactivation. The results of time-resolved IR analysis suggest that aggregate and solid state promoted suppression of geometrical changes in the excited state causes the observed increases in ΦPL.
Introduction
Thermally-activated delayed fluorescence (TADF)1,2 is a promising technology of highly-efficient organic light-emitting diodes (OLEDs).3–5 The key process in TADF is reverse intersystem crossing (RISC), which converts a triplet excited state to the corresponding singlet-excited state (Fig. 1). RISC takes place at ambient temperatures when the gap between the singlet and triplet state energies (ΔEST) is small (<0.3 eV). Many TADF materials have been developed,6–14 and applicated to the field of not only OLED but also imaging materials15,16 and photosensitizers.17–19 With the aim of improving the efficiencies of OLEDs, theoretical20 and experimental21,22 investigations have been carried out to uncover approaches to accelerate RISC by controlling the geometrical and electronic structures of TADF materials.
![image file: d1tc05196b-f1.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-f1.gif) |
| Fig. 1 Energy diagram for TADF with chemical structure of 2Cz2SB and 2Mi2SB. | |
Typical TADF materials are composed of electron-donating and electron-accepting moieties that cause a reduction of ΔEST, related to spatial separation of the HOMO and LUMO. As a result, many of these materials undergo self-quenching in the solid state or in emitting layers of OLEDs, that is caused by strong intermolecular charge-transfer (CT) interactions.23,24 Thus, the phenomenon of aggregation-induced emission (AIE),25–28 in which aggregation leads to suppression of thermal deactivation modes, is applicable to designing efficient solid-state TADF materials. In fact, many AIE-active TADF materials have been developed to date.29–31
In the current investigation, which focused on the discovery of new and efficient TADF materials, we prepared 2Cz2SB and 2Mi2SB (Fig. 1) that contain a benzene core substituted by N-heterocycle electron-donating and tert-butylphenylsulfonyl electron-accepting moieties. Because the sulfonyl sulfur atom in the accepting group is sp3-hybridized, the two π-conjugated donor and acceptor systems do not directly interact, making 2Cz2SB and 2Mi2SB potential TADF materials. In addition, para-disubstituted32 carbazole (Cz) or 2-methylimidazole (Mi) moieties were utilized as weak electron-donors, to reduce CT interactions in the excited state.
In the effort described below, we explored the TADF and AIE characteristics of 2Cz2SB and 2Mi2SB using spectroscopic methods. The results show that these materials display excellent TADF behaviour both in solution and in the solid states. The photoluminescence quantum yields (ΦPL) of 2Cz2SB and 2Mi2SB are increased in the crystalline or aggregate state relative to those in solution in a manner expected for operation of AIE. We also fabricated an inverted OLED using 2Cz2SB and observed that it exhibits green electroluminescence (EL).
Results and discussion
Synthesis
TADF materials 2Cz2SB and 2Mi2SB were synthesized starting with 1,2,4,5-tetrafluorobenzene by using the pathways shown in Scheme 1. Nucleophilic aromatic substitution (SNAr) reaction of 1,2,4,5-tetrafluorobenzene with two equivalents of potassium 4-(tert-butyl)benzenethiolate33 selectively produced the 1,4-substituted product 1 in 72% yield.34 Oxidation of 1 using m-chloroperoxybenzoic acid (mCPBA) formed the corresponding sulfone 2 in excellent yield.35 Finally, SNAr reactions of 2 with the anions of carbazole and 2-methylimidazole generated 2Cz2SB (67%) and 2Mi2SB (32%), respectively.36 The structures of 2Cz2SB and 2Mi2SB were characterized by using 1H, 13C NMR and IR spectroscopy, and mass spectrometric analyses. Also, the structure of 2Cz2SB was confirmed by using X-ray crystallographic analysis (Fig. 2). The manner of packing structure of 2Cz2SB has no remarkable intermolecular interactions, owing to the bulky arylsulfonyl group (Fig. S1, ESI†).
![image file: d1tc05196b-s1.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-s1.gif) |
| Scheme 1 Routes for synthesis of 2Cz2SB and 2Mi2SB. | |
![image file: d1tc05196b-f2.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-f2.gif) |
| Fig. 2 ORTEP drawing of 2Cz2SB (thermal ellipsoids are shown in 50% probability). | |
Theoretical calculations
Density functional theory (DFT, B3LYP/6-31G(d,p)) calculations showed that the respective Cz and Mi moieties in the optimized geometries of 2Cz2SB and 2Mi2SB are highly twisted with respect to the central benzene ring. The authenticity of the calculated structure of 2Cz2SB was confirmed by using X-ray crystallographic analysis (Fig. 2). The calculations also show that the HOMO and LUMO of 2Cz2SB are localized on the electron-donating Cz and -accepting disulfonylbenzene (2SB) moieties, respectively (Fig. 3). The HOMO and LUMO of 2Mi2SB are also localized on the respective Mi and 2SB moieties. 2Mi2SB has a relatively low HOMO energy level (−6.08 eV) because of the weak electron-donating ability of the Mi moieties. The localized electronic structures of these materials lead small ΔEST values of 0.07 eV for 2Cz2SB and 0.03 eV for 2Mi2SB, determined by using time-dependent (TD)-DFT calculations. These values were in good agreement with the experimental values of ΔEST for 2Cz2SB (0.02 eV) and 2Mi2SB (0.07 eV) determined in 2-methyltetrahydrofuran matrix at 77 K (Fig. S2, ESI†). Based on the calculated wavelength of the electronic transition (λET = 385 nm, 3.22 eV), 2Mi2SB is expected to display blue TADF.37
![image file: d1tc05196b-f3.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-f3.gif) |
| Fig. 3 Frontier molecular orbitals of (a) 2Cz2SB and (b) 2Mi2SB (B3LYP/6-31G(d,p)). | |
Spectroscopic measurements
UV-Vis absorption and photoluminescence (PL) spectra of solutions of 2Cz2SB and 2Mi2SB in CH2Cl2 were recorded (Fig. 4a). The absorption spectrum of 2Cz2SB contains a weak and broad band at λAB = 359 nm and structured bands at 327 nm, assignable to intramolecular CT and π–π* transitions, respectively. The CT absorption band of 2Mi2SB at 330 nm is weak, reflecting the weak electron-donating ability of the Mi moiety. Excitation at 290 nm of these solutions led to PL at λPL = 540 and 521 nm for 2Cz2SB and 2Mi2SB, respectively. These PL maxima are greatly different from the calculated electronic transitions (429 nm for 2Cz2SB and 385 nm for 2Mi2SB), probably because of the occurrence of geometrical changes in the excited states. Analysis of the PL decay profiles of 2Cz2SB and 2Mi2SB in degassed CH2Cl2 (Fig. 4c), showed that the former contains prompt and delayed PL components with respective lifetimes (τPL) of 12 and 7700 ns (Table 1). Note that the delayed component was largely quenched by molecular oxygen under air. 2Mi2SB behaves similarly in that its decay profile is associated with two τPL components of 8.2 and 580 ns. The ΦPL value of 2Cz2SB was determined to be 0.07 under an air atmosphere, and is increased to 0.10 under degassed conditions. Although the ΦPL of 2Mi2SB is small under aerated (0.02) and degassed conditions (0.04), it is larger under Ar. The above observations indicate that 2Cz2SB and 2Mi2SB are typical TADF materials. The rate constants for ISC (kISC) and RISC (kRISC) for 2Cz2SB were estimated to be the order of 107 and 104 s−1, respectively, which are typical for TADF materials possessing sulfonyl groups.14,38,39 On the other hand, kISC and kRISC for 2Mi2SB were the order of 108 and 106 s−1, respectively, which are much larger than those of 2Cz2SB. Although unfortunately ΦPL of 2Mi2SB is not so high probably due to nonradiative deactivation, the Mi moiety can be positioned as one of the better donor parts for TADF materials.
![image file: d1tc05196b-f4.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-f4.gif) |
| Fig. 4 (a) UV-Vis absorption and PL spectra of 2Cz2SB (blue) and 2Mi2SB (red) in CH2Cl2 (2 × 10−5 M, λEX = 290 nm). (b) PL spectra of crystals of 2Cz2SB and 2Mi2SB. PL decay profiles of (c) degassed CH2Cl2 solutions (λEX = 295 nm) and (d) crystals (λEX = 365 nm). | |
Table 1 Photophysical properties of 2Cz2SB and 2Mi2SB in CH2Cl2
Material |
λ
AB (nm) |
λ
PL (nm) |
τ
PL,soln (ns) |
Φ
PL,air
|
Φ
PL,Ar
|
k
ISC (107 s−1) |
k
RISC (104 s−1) |
2Cz2SB |
379, 329 |
540 |
12, 7700 |
0.07 |
0.10 |
7.7 |
4.3 |
2Mi2SB |
329, 269 |
521 |
8.2, 580 |
0.02 |
0.04 |
11.1 |
175 |
A crystal of 2Cz2SB displays a PL band at 501 nm (Fig. 4b), which is greatly (ca. 40 nm) blueshifted as compared to that in CH2Cl2 solution. The PL decay profile of a crystal of 2Cz2SB contains prompt and delayed components with τPL of 16 and 3300 ns (Fig. 4d and Table 2). These τPL values do not change remarkably on proceeding from aerated to degassed conditions, likely because the O2-blocking effect of crystals.40–43 Crystals of 2Cz2SB have ΦPL = 0.32, which is larger than the value in degassed CH2Cl2. These results show that geometrical changes that occur in the excited state in solution are largely suppressed in the crystalline state. The elongation of the prompt component in τPL (12 to 16 ns) supports this understanding. Crystals of 2Mi2SB similarly show a blueshift of 53 nm and relatively large ΦPL of 0.28, possessing τPL of 38 and 1900 ns. The remarkable elongation of the prompt component in τPL (8.2 to 38 ns) are also observed for 2Mi2SB. Therefore, 2Cz2SB and 2Mi2SB have AIE or crystallization-induced emission (CIE) properties.44
Table 2 PL Properties of 2Cz2SB and 2Mi2SB in the crystalline state
Material |
λ
PL (nm) |
τ
PL (ns) |
Φ
PL
|
2Cz2SB |
501 |
16, 3300 |
0.32 |
2Mi2SB |
468 |
38, 1900 |
0.28 |
AIE behaviour
To gain further insight into AIE characteristics, PL spectroscopic measurements were carried out of 2Cz2SB in THF/H2O mixtures (Fig. 5). In this experiment, ΦPL were determined by using an absolute method with an integrating sphere to eliminate the influence of light diffraction and optical path length changes. As compared to that in pure THF, the PL wavelength of 2Cz2SB in solutions of 0–50 vol% of H2O content is redshifted up to 552 nm and ΦPL decreases (Fig. 5b). This behaviour is associated with the increase of solvent polarity brought about by addition of H2O, which enhances intramolecular CT interactions. On the other hand, addition of further amounts of H2O (>75 vol%) causes an increase of ΦPL to 0.196 and blueshift of λPL down to 521 nm. These changes are typical of the AIE phenomenon promoted by formation of aggregates. The PL properties of 2Cz2SB in 90 vol% of H2O content are similar to those in the crystalline state. Therefore, the AIE characteristics of 2Cz2SB appear to be a consequence of formation of small crystal-like aggregates caused by addition of H2O to the THF solution.
![image file: d1tc05196b-f5.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-f5.gif) |
| Fig. 5 (a) Photographs taken under blacklight (λEX = 365 nm), (b) PL spectra, and (c) plots of absolute ΦPL against H2O content (vol%) in THF solution of 2Cz2SB (2 × 10−5 M). | |
Time-resolved IR
Time-resolved IR (TR-IR) spectroscopy, a powerful tool to obtain information about geometries of excited species,22,45–47 was carried out on 2Cz2SB in a benzene solution and KBr pellet. An FT-IR spectrum of 2Cz2SB in KBr contains multiple bands in the 1100–1400 cm−1 region (Fig. 6a). By reference to known compounds48 and quantum chemical calculations (Fig. S11, ESI†), peaks at 1159 and 1330 cm−1 are assignable to symmetric and asymmetric stretching of sulfonyl groups in 2Cz2SB, respectively, which were the focus of our measurements. Strong bleaching of the bands at 1159 and 1330 cm−1 was observed at 1 ns after 355-nm photoexcitation of 2Cz2SB in a benzene solution (Fig. 6b, blue). IR absorption bands simultaneously appear at 1138 and 1301 cm−1. According to population analysis estimated by using the PL decay profile (Fig. S8, ESI†), the major excited species existing 1 ns after photoexcitation is 12Cz2SB* (12Cz2SB*/32Cz2SB* = 96/4). Thus, the 1138 and 1301 cm−1 peaks are assigned to symmetric and asymmetric stretching of sulfonyl groups in 12Cz2SB*, respectively. The IR absorption maxima shift to 1140 and 1316 cm−1 at 100 ns after photoexcitation (Fig. 6b, green). The major excited species at 100 ns after photoexcitation is 32Cz2SB* (12Cz2SB*/32Cz2SB* = 2/98) and, thus, these bands assigned to symmetric and asymmetric stretching of the sulfonyl group in 32Cz2SB*, respectively. The results show that although the SO bonds in 12Cz2SB* are considerably weakened by intramolecular CT, the strengths of those in 32Cz2SB* can be recovered by geometrical relaxation.
![image file: d1tc05196b-f6.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-f6.gif) |
| Fig. 6 (a) FT-IR spectrum of 2Cz2SB in KBr. TR-IR spectra of 2Cz2SB in (b) N2-saturated benzene and (c) KBr. TR-IR spectra at 1 and 100 ns after photoexcitation are displayed as blue and green, respectively. Red circles indicate shift of frequencies. | |
In contrast, TR-IR spectra of 2Cz2SB in KBr pellets did not show remarkable peak shifts between 1 and 100 ns after photoexcitation (Fig. 6c), indicating that geometrical changes between 12Cz2SB* and 32Cz2SB* in this medium are significantly suppressed. Since a suppression of geometrical change between the excited singlet and triplet states generally accelerates TADF process in carbazolyl benzonitriles,22 this result is in good agreement with the increase of ΦPL in the solid state relative to those in the solution. On the other hand, the shifts between the bleaching and the corresponding peak at 1 ns originate from the geometrical change between the ground state 2Cz2SB and the singlet excited state 12Cz2SB*. In general, the smaller geometrical change, the smaller Stokes shift. Therefore, the apparent fact that these shifts observed in KBr pellets (Fig. 6c) is smaller than those in the solution (Fig. 6b) is consistent with the blueshift of PL wavelengths of the KBr pellet.
Fabrication of inverted OLED
Because 2Cz2SB displays good TADF characteristics in the solid state, we used it to fabricate an OLED utilizing a solution process. For this purpose, we employed an inverted OLED structure, which can be simply fabricated and is air-stable.49–53 Specifically, an ethanol solution of polyethyleneimine (PEI) was spincoated on an aluminum-zinc oxide-coated substrate to serve as an electron-injection layer. An emitting layer composed of 2Cz2SB:poly(methyl methacrylate) (PMMA) = 70/30 (wt/wt) was then spincoated on the PEI layer. After drying (60 °C, 30 min), MoO3 and Al were vacuum-deposited as a hole-injection layer and anode, respectively. Green EL at 523 nm was observed when the external voltage of >4 V was applied to the 2Cz2SB inverted OLED (Fig. 7). The EL spectrum was nearly identical to PL spectrum (Fig. 4b) of crystals of 2Cz2SB. The maximum current efficiency was 0.64 cd A−1 and can be improved by using a bipolar host matrix (electrically inactive host matrix, PMMA, was used here to form the emissive layer by means of a spin coating process).
![image file: d1tc05196b-f7.tif](/image/article/2022/TC/d1tc05196b/d1tc05196b-f7.gif) |
| Fig. 7 An EL spectrum and device structure of the solution-processed OLED containing 2Cz2SB. (Inset: Photograph of OLED upon application of external voltage of 5 V). | |
Conclusions
In the above effort, we synthesized the novel TADF materials 2Cz2SB and 2Mi2SB bearing N-heterocycle and arylsulfonyl groups. These materials have excellent TADF characteristics both in the solution and solid states. Relative to those in solutions, the ΦPL values of 2Cz2SB and 2Mi2SB are increased in the crystalline or aggregated states, which is typical AIE or CIE behaviour. We also fabricated an inverted OLED using 2Cz2SB and observed that it displays green EL. TR-IR analysis of SO-stretching vibrations revealed that the magnitude of geometrical changes in the solid state of 2Cz2SB is suppressed, demonstrating that this substance displays AIE behaviour. The above findings indicate that the arylsulfonyl group containing sp3-hybridyzed sulfonyl sulfur atom is effective to suppress intermolecular interactions. This characteristics is also useful to create materials sensitive to external stimuli and/or environmental changes, which makes it potentially applicable to the design of a “soft crystal”.54
Experimental
Preparation of materials.
The details of preparation of 1 and 2 are given in the ESI.†
1,4-Bis(9H-carbazol-9-yl)-2,5-bis((4-tert-butyl)phenylsulfonyl)benzene (2Cz2SB).
To a 100 mL round-bottom flask, carbazole (0.276 g, 1.65 mmol), NaH (60 wt% in oil dispersion, 0.075 g, 1.88 mmol), and dry DMF (25 mL) were added and stirred for 30 min at room temperature. To the solution, 2 (0.380 g, 0.750 mmol) and DMF (5 mL) was added and stirred for 26 h at 100 °C. The reaction mixture was quenched by addition of water (50 mL) and extracted with CH2Cl2 (50 mL × 2). The combined extracts were washed with brine, dried over Na2SO4, and evaporated under reduced pressure. Silica-gel column chromatography (n-hexane/CHCl3 = 2/1) followed by recrystallization from CHCl3–n-hexane afforded 2Cz2SB as yellow needles (405 mg, 0.51 mmol, y. 67%). mp 324 °C (differential scanning calorimetry); 1H NMR (400 MHz, CDCl3) δppm 1.13 (s, 18H), 6.71 (d, J = 8.1 Hz, 4H), 6.89 (AA’BB’, J = 8.7 Hz, 4H), 6.96 (AA’BB’, J = 8.7 Hz, 4H), 7.20–7.33 (m, 8H), 8.11 (d, J = 8.4 Hz, 4H), 8.40 (s, 2H); 13C NMR (75 MHz, CDCl3) δppm 30.9 (6C), 35.0 (2C), 110.4 (4C), 120.1 (4C), 121.9 (4C), 123.8 (4C), 125.6 (4C), 126.2 (4C), 127.9 (4C), 134.2 (2C), 134.6 (2C), 137.7 (2C), 142.1 (4C), 149.1 (2C), 157.9 (2C); IR (ATR) ν/cm−1 1477, 1330, 1220, 1157, 1093, 840, 748, 722, 664; anal. calcd. for C50H44N2O4S2: C, 74.97; H, 5.54 N, 3.50. Found: C, 74.72; H, 5.42; N, 3.68.
1,4-Bis(2-methylbenzoimidazol-1-yl)-2,5-bis((4-tert-butyl)phenylsulfonyl)benzene (2Mi2SB).
To a 100 mL round bottom flask, 2-methylbenzoimidazole (0.437 g, 3.3 mmol), NaH (60 wt% oil dispersion, 0.15 g, 3.8 mmol), and DMF (50 mL) were added and stirred for 30 min at room temperature under Ar atmosphere. After addition of 2 (0.761 g, 1.5 mmol), the mixture was stirred for 20 min at 100 °C. After cooling to room temperature, the mixture was quenched by addition of water (50 mL). The mixture was extracted by CH2Cl2 (100 mL × 2) and then dried over Na2SO4. The solution was concentrated to dryness under reduced pressure and the obtained solid was washed with EtOH. Recrystallization from CHCl3–n-hexane gave 2Mi2SB as colourless powder (0.350 g, 0.48 mmol, y. 32%). mp > 300 °C; 1H NMR (400 MHz, CDCl3) δppm 1.20 (s, 18H), 2.45 (s, 6H), 6.16 (d, J = 8.0 Hz, 2H), 6.85 (dd, J = 8.0 Hz, 7.6 Hz, 2H), 7.04 (AA’BB’, J = 8.0 Hz, 4H), 7.07 (AA’BB’, J = 8.0 Hz, 4H), 7.19 (dd, J = 7.6 Hz, 7.6 Hz, 2H), 7.72 (d, J = 7.6 Hz, 2H), 8.40 (s, 2H); 13C NMR (100 MHz, CDCl3) δppm 14.6 (2C), 30.9 (6C), 35.2 (2C), 108.8 (2C), 119.2 (2C), 122.9 (2C), 123.2 (2C), 126.3 (4C), 127.8 (4C), 133.6 (2C), 134.2 (2C), 136.2 (2C), 136.7 (4C), 142.4 (2C), 147.3 (2C), 152.3 (2C), 158.8 (2C); IR (ATR) ν/cm−1 1483, 1390, 1323, 1161, 1094, 833, 740, 687, 652, 626; HR-MS (ESI+) m/z = 731.2710 (calcd. for C42H43N4O4S2 (M + H)+, 731.2726). anal. calcd. for C42H42N4O4S2: C, 69.02; H, 5.79; N, 7.67; found: C, 67.64; H, 5.51; N 7.51.
Crystallographic analysis
X-Ray crystallographic analysis of single crystals of 2Cz2SB was performed on a Rigaku R-AXIS RAPID diffractometer using multi-layer mirror monochromated Mo-Kα radiation (λ = 0.71075 Å) at 296 K. Crystal structure refinement was carried out using SHELXL55 and Yadokari-XG 2009.56 Crystal data for 2Cz2SB: a colourless block crystal, C50H44N2O4S2, Mw = 800.99, crystal dimensions 0.80 × 0.50 × 0.80 mm, triclinic, space group P
, a = 10.6264(8), b = 13.5683(12), c = 14.6053(13) Å, α = 86.590(3)°, β = 87.124(2)°, γ = 78.622(2)°, V = 2059.2(3) Å3, Z = 2, d = 1.292 g cm−3, 9151 reflections collected, 5586 independent (Rint = 0.0259), GOF = 1.030, R1 = 0.0728 (I > 2.00 σ(I)), wR2 = 0.2052 for all reflections. The CIF file is deposited to Cambridge Crystallographic Data Centre (CCDC†) (ID = 2002881).
TR-IR spectroscopic measurements
TR-IR measurements were performed using home-built setups with pump–probe scheme. The sample solutions were continuously circulated through a home-built IR cell equipped with BaF2 windows with an optical path length of 0.1 mm. A probe pulse passed through the IR cell was dispersed by a 19 cm polychromator, followed by detection using a 64-channel mercury cadmium telluride IR detector array. All measurements in 0.9 mM benzene solutions were performed after 1 h N2-prebubbling and while bubbling maintained. For the measurement of KBr pellets, the samples were prepared by mixing 2 mg of 2Cz2SB and 100 mg of ground KBr and by pressing it in a die, forming a pellet with diameter of 13.0 mm and thickness of 0.5 mm. The details were given in the ESI† and previous reports.46,47,57
Theoretical calculations
Theoretical calculations on 2Cz2SB and 2Mi2SB were performed by using various functionals and 6-31G(d,p) basis set on Gaussian 09.58 The M06-2X or PBE0 functional provided relatively reproductive IR spectra of ground state of 2Cz2SB (Fig. S11, ESI†). Unfortunately, geometries of 2Cz2SB in the singlet excited and triplet excited states reproducing TR-IR spectra cannot be found, due to complicated conformational changes of arylsulfonyl groups.
Author contributions
Y. M., H. I., and H. N. designed this research project. Y. Y. and T. O. synthesized molecules. Y. M., Y. Y., T. O., M. S. and K. M. measured photophysical properties. K. I. and A. N. fabricated OLED device under the supervision of H. N. M. S. and K. M. measured TR-IR spectra under the supervision of K. O. manuscript was prepared by contribution of all authors. All authors approved the final version of the manuscript.
Conflicts of interest
There are no conflicts to declare.
Acknowledgements
This paper is dedicated to the memory of Emeritus Prof. Toshio Mukai and Emeritus Prof. Tsutomu Miyashi at Tohoku University. This study was partially supported by JSPS KAKENHI Grant Numbers JP17H06371, JP17H06375, JP18K14202, JP19H00888, JP19H02599, JP20H02716, JP20H05106, JP20K15264, JP20K21007, JP21H04564, JP21H05494, and JP24109009. KM also acknowledges support of Qdai-jump Research Program Wakaba Challenge.
Notes and references
- H. Uoyama, K. Goushi, K. Shizu, H. Nomura and C. Adachi, Nature, 2012, 492, 234–238 CrossRef CAS PubMed
.
- C. Adachi, Jpn. J. Appl. Phys., 2014, 53, 60101 CrossRef
.
- C. W. Tang and S. A. VanSlyke, Appl. Phys. Lett., 1987, 51, 913–915 CrossRef CAS
.
- Q. Peng, A. Obolda, M. Zhang and F. Li, Angew. Chem., Int. Ed., 2015, 54, 7091–7095 CrossRef CAS PubMed
.
- R. Nagata, H. Nakanotani, W. J. Potscavage and C. Adachi, Adv. Mater., 2018, 30, 1801484 CrossRef PubMed
.
- J. Nishida, Y. Kawakami, S. Yamamoto, Y. Matsui, H. Ikeda, Y. Hirao and T. Kawase, Eur. J. Org. Chem., 2019, 3735–3743 CrossRef CAS
.
- H. Kaji, H. Suzuki, T. Fukushima, K. Shizu, K. Suzuki, S. Kubo, T. Komino, H. Oiwa, F. Suzuki, A. Wakamiya, Y. Murata and C. Adachi, Nat. Commun., 2015, 6, 1–8 Search PubMed
.
- T. Sato, M. Uejima, K. Tanaka, H. Kaji and C. Adachi, J. Mater. Chem. C, 2015, 3, 870–878 RSC
.
- G. H. Kim, R. Lampande, J. B. Im, J. M. Lee, J. Y. Lee and J. H. Kwon, Mater. Horiz., 2017, 4, 619–624 RSC
.
- A. Klimash, P. Pander, W. T. Klooster, S. J. Coles, P. Data, F. B. Dias and P. J. Skabara, J. Mater. Chem. C, 2018, 6, 10557–10568 RSC
.
- E. Spuling, N. Sharma, I. D. W. Samuel, E. Zysman-Colman and S. Bräse, Chem. Commun., 2018, 54, 9278–9281 RSC
.
- T. Hatakeyama, K. Shiren, K. Nakajima, S. Nomura, S. Nakatsuka, K. Kinoshita, J. Ni, Y. Ono and T. Ikuta, Adv. Mater., 2016, 28, 2777–2781 CrossRef CAS PubMed
.
- Y. Kondo, K. Yoshiura, S. Kitera, H. Nishi, S. Oda, H. Gotoh, Y. Sasada, M. Yanai and T. Hatakeyama, Nat. Photonics, 2019, 13, 678–682 CrossRef CAS
.
- Q. Zhang, J. Li, K. Shizu, S. Huang, S. Hirata, H. Miyazaki and C. Adachi, J. Am. Chem. Soc., 2012, 134, 14706–14709 CrossRef CAS PubMed
.
- X. Xiong, F. Song, J. Wang, Y. Zhang, Y. Xue, L. Sun, N. Jiang, P. Gao, L. Tian and X. Peng, J. Am. Chem. Soc., 2014, 136, 9590–9597 CrossRef CAS PubMed
.
- F. Ni, Z. Zhu, X. Tong, M. Xie, Q. Zhao, C. Zhong, Y. Zou and C. Yang, Chem. Sci., 2018, 9, 6150–6155 RSC
.
- J. Lu, B. Pattengale, Q. Liu, S. Yang, W. Shi, S. Li, J. Huang and J. Zhang, J. Am. Chem. Soc., 2018, 140, 13719–13725 CrossRef CAS PubMed
.
- T.-Y. Shang, L.-H. Lu, Z. Cao, Y. Liu, W.-M. He and B. Yu, Chem. Commun., 2019, 55, 5408–5419 RSC
.
- E. Speckmeier, T. G. Fischer and K. Zeitler, J. Am. Chem. Soc., 2018, 140, 15353–15365 CrossRef CAS PubMed
.
- H. Noda, X.-K. Chen, H. Nakanotani, T. Hosokai, M. Miyajima, N. Notsuka, Y. Kashima, J.-L. Brédas and C. Adachi, Nat. Mater., 2019, 18, 1084–1090 CrossRef CAS PubMed
.
- T. Kobayashi, A. Niwa, K. Takaki, S. Haseyama, T. Nagase, K. Goushi, C. Adachi and H. Naito, Phys. Rev. Appl., 2017, 7, 34002 CrossRef
.
- M. Saigo, K. Miyata, S. Tanaka, H. Nakanotani, C. Adachi and K. Onda, J. Phys. Chem. Lett., 2019, 10, 2475–2480 CrossRef CAS PubMed
.
- H. S. Kim, S.-R. Park and M. C. Suh, J. Phys. Chem. C, 2017, 121, 13986–13997 CrossRef CAS
.
- J. Lee, N. Aizawa, M. Numata, C. Adachi and T. Yasuda, Adv. Mater., 2017, 29, 1604856 CrossRef PubMed
.
- J. Luo, Z. Xie, J. W. Y. Lam, L. Cheng, H. Chen, C. Qiu, H. S. Kwok, X. Zhan, Y. Liu, D. Zhu and B. Z. Tang, Chem. Commun., 2001, 1740–1741 RSC
.
- Y. Hong, J. W. Y. Lam and B. Z. Tang, Chem. Soc. Rev., 2011, 40, 5361–5388 RSC
.
- S. Suzuki, S. Sasaki, A. S. Sairi, R. Iwai, B. Z. Tang and G. Konishi, Angew. Chem., Int. Ed., 2020, 59, 9856–9867 CrossRef CAS PubMed
.
- T. Beppu, S. Kawata, N. Aizawa, Y.-J. Pu, Y. Abe, Y. Ohba and H. Katagiri, ChemPlusChem, 2014, 79, 536–545 CrossRef CAS PubMed
.
- J. Yang, M. Fang and Z. Li, Aggregate, 2020, 1, 6–18 CrossRef
.
- S. Xu, T. Liu, Y. Mu, Y.-F. Wang, Z. Chi, C.-C. Lo, S. Liu, Y. Zhang, A. Lien and J. Xu, Angew. Chem., Int. Ed., 2015, 54, 874–878 CrossRef CAS PubMed
.
- J. Guo, J. Fan, L. Lin, J. Zeng, H. Liu, C.-K. Wang, Z. Zhao and B. Z. Tang, Adv. Sci., 2019, 6, 1801629 CrossRef PubMed
.
- T. Hosokai, H. Matsuzaki, H. Nakanotani, K. Tokumaru, T. Tsutsui, A. Furube, K. Nasu, H. Nomura, M. Yahiro and C. Adachi, Sci. Adv., 2017, 3, e1603282 CrossRef PubMed
.
- B. B. Jarvis and G. P. Stahly, J. Org. Chem., 1980, 45, 2604–2609 CrossRef CAS
.
- P. Robson, T. A. Smith, R. Stephens and J. C. Tatlow, J. Chem. Soc., 1963, 3692–3703 RSC
.
- X.-P. Zhou, Z. Xu, M. Zeller, A. D. Hunter, S. S.-Y. Chui and C.-M. Che, Inorg. Chem., 2011, 50, 7142–7149 CrossRef CAS PubMed
.
- N. Jürgensen, A. Kretzschmar, S. Höfle, J. Freudenberg, U. H. F. Bunz and G. Hernandez-Sosa, Chem. Mater., 2017, 29, 9154–9161 CrossRef
.
- A. Monkman, ACS Appl. Mater. Interfaces, 2021 DOI:10.1021/acsami.1c09189
.
- R. Guo, P. Leng, Q. Zhang, Y. Wang, X. Lv, S. Sun, S. Ye, Y. Duan and L. Wang, Dyes Pigm., 2021, 184, 108781 CrossRef CAS
.
- D. Zhou, C. H. Ryoo, D. Liu, S. Wang, G. Qian, Y. Zheng, S. Y. Park, W. Zhu and Y. Wang, Adv. Opt. Mater., 2020, 8, 1901021 CrossRef CAS
.
- J. Yang, X. Zhen, B. Wang, X. Gao, Z. Ren, J. Wang, Y. Xie, J. Li, Q. Peng, K. Pu and Z. Li, Nat. Commun., 2018, 9, 840 CrossRef PubMed
.
- M. Shimizu, R. Shigitani, M. Nakatani, K. Kuwabara, Y. Miyake, K. Tajima, H. Sakai and T. Hasobe, J. Phys. Chem. C, 2016, 120, 11631–11639 CrossRef CAS
.
- A. Sakai, E. Ohta, Y. Matsui, S. Tsuzuki and H. Ikeda, ChemPhysChem, 2016, 17, 4033–4036 CrossRef CAS PubMed
.
- M. Shimizu, A. Kimura and H. Sakaguchi, Eur. J. Org. Chem., 2016, 467–473 CrossRef CAS
.
- Y. Dong, J. W. Y. Lam, A. Qin, Z. Li, J. Sun, H. H.-Y. Sung, I. D. Williams and B. Z. Tang, Chem. Commun., 2007, 40–42 RSC
.
- Y. Shimoda, K. Miyata, M. Saigo, Y. Tsuchiya, C. Adachi and K. Onda, J. Chem. Phys., 2020, 153, 204702 CrossRef CAS PubMed
.
- K. Koike, D. C. Grills, Y. Tamaki, E. Fujita, K. Okubo, Y. Yamazaki, M. Saigo, T. Mukuta, K. Onda and O. Ishitani, Chem. Sci., 2018, 9, 2961–2974 RSC
.
- T. Mukuta, S. Tanaka, A. Inagaki, S. Koshihara and K. Onda, ChemistrySelect, 2016, 1, 2802–2807 CrossRef CAS
.
-
R. M. Silverstein, F. X. Webster and D. J. Kiemle, Spectrometric Identification of Organic Compounds, John Wiley, 7th edn, 2005 Search PubMed
.
- K. Morii, M. Ishida, T. Takashima, T. Shimoda, Q. Wang, M. K. Nazeeruddin and M. Grätzel, Appl. Phys. Lett., 2006, 89, 183510 CrossRef
.
- H. Fukagawa, K. Morii, M. Hasegawa, Y. Arimoto, T. Kamada, T. Shimizu and T. Yamamoto, Appl. Phys. Express, 2014, 7, 82104 CrossRef CAS
.
- M. Takada, T. Nagase, T. Kobayashi and H. Naito, Org. Electron., 2017, 50, 290–295 CrossRef CAS
.
- M. Takada, T. Kobayashi, T. Nagase and H. Naito, Jpn. J. Appl. Phys., 2016, 55, 03DC06 CrossRef
.
-
M. Takada and H. Naito, in New Polymeric Materials Based on Element-Blocks, ed. Y. Chujo, Springer Singapore, Singapore, 2019, pp. 413–422 Search PubMed
.
- M. Kato, H. Ito, M. Hasegawa and K. Ishii, Chem. – Eur. J., 2019, 25, 5105–5112 CrossRef CAS PubMed
.
- G. M. Sheldrick, Acta Crystallogr., Sect. C: Struct. Chem., 2015, 71, 3–8 Search PubMed
.
- C. Kabuto, S. Akine, T. Nemoto and E. Kwon, J. Cryst. Soc. Jpn., 2009, 51, 218–224 CrossRef
.
- T. Mukuta, N. Fukazawa, K. Murata, A. Inagaki, M. Akita, S. Tanaka, S. Koshihara and K. Onda, Inorg. Chem., 2014, 53, 2481–2490 CrossRef CAS PubMed
.
-
M. J. Frisch, G. W. Trucks, H. B. Schlegel, G. E. Scuseria, M. A. Robb, J. R. Cheeseman, G. Scalmani, V. Barone, B. Mennucci, G. A. Petersson, H. Nakatsuji, M. Caricato, X. Li, H. P. Hratchian, A. F. Izmaylov, J. Bloino, G. Zheng, J. L. Sonnenberg, M. Hada, M. Ehara, K. Toyota, R. Fukuda, J. Hasegawa, M. Ishida, T. Nakajima, Y. Honda, O. Kitao, H. Nakai, T. Vreven, J. A. Montgomery Jr., J. E. Peralta, F. Ogliaro, M. Bearpark, J. J. Heyd, E. Brothers, K. N. Kudin, V. N. Staroverov, R. Kobayashi, J. Normand, K. Raghavachari, A. Rendell, J. C. Burant, S. S. Iyengar, J. Tomasi, M. Cossi, N. Rega, J. M. Millam, M. Klene, J. E. Knox, J. B. Cross, V. Bakken, C. Adamo, J. Jaramillo, R. Gomperts, R. E. Stratmann, O. Yazyev, A. J. Austin, R. Cammi, C. Pomelli, J. W. Ochterski, R. L. Martin, K. Morokuma, V. G. Zakrzewski, G. A. Voth, P. Salvador, J. J. Dannenberg, S. Dapprich, A. D. Daniels, Ö. Farkas, J. B. Foresman, J. V. Ortiz, J. Cioslowski and D. J. Fox, Gaussian 09, 2009 Search PubMed
.
Footnote |
† Electronic supplementary information (ESI) available: General, preparation of substrates, crystal packing structure of 2Cz2SB, determination of excited state energy levels, physical properties in benzene, numerical simulations for population of excited species, fabrication of inverted OLED and device characterization, full description of TR-IR spectra, quantum chemical calculations, and NMR spectra. CCDC 2002881. For ESI and crystallographic data in CIF or other electronic format see DOI: 10.1039/d1tc05196b |
|
This journal is © The Royal Society of Chemistry 2022 |