Synthesis of Zn-based 1D and 2D coordination polymer nanoparticles in block copolymer micelles

Abstract

Nanoparticles of the 1D and 2D coordination polymers [Zn(OAc)2(bipy)]n and [Zn(TFA)2(bppa)2]n were prepared, employing polystyrene-block-poly(4-vinylpyridine) diblock copolymers with different weight fractions of the 4-vinylpyridine (4VP) block and comparable overall molecular weights of Mn ≈ 155 kg mol−1 as template (SV-15 and SV-42 with 15 and 42 wt% 4VP, respectively). [Zn(OAc)2(bipy)]n nanoparticles were successfully synthesised within the 4VP core of SV-42 micelles, showing a core size of Dcore = 47 ± 5 nm and a hydrodynamic diameter of Dh = 157 ± 46 nm, determined by transmission electron microscopy (TEM) and dynamic light scattering (DLS). The crystallinity of the composite is quite low, showing only low intensity reflexes in the powder X-ray diffraction (PXRD) pattern with the highest particle load. No indications for larger microcrystals were detected by scanning electron microscopy (SEM), proving the successful integration of the coordination polymer nanoparticles within the micellar cores. Nanocomposites of the 2D coordination network [Zn(TFA)2(bppa)2]n were synthesised using both diblock copolymers. The particle core sizes (from TEM) and hydrodynamic diameters (from DLS) correlate with the 4VP fraction of the micelles, resulting in Dcore = 46 ± 6 nm for SV-42 and 15 ± 2 nm for SV-15 and Dh = 340 ± 153 nm and 177 ± 57 nm, respectively. The successful synthesis was proven by PXRD and SEM images, confirming the absence of larger crystallites. Hence, it is possible to synthesise nanocomposites of Zn-based 1D and 2D coordination polymers by a direct approach utilizing diblock copolymer micelles as template.

Graphical abstract: Synthesis of Zn-based 1D and 2D coordination polymer nanoparticles in block copolymer micelles

Supplementary files

Article information

Article type
Paper
Submitted
26 אפר 2020
Accepted
05 ספט 2020
First published
08 ספט 2020
This article is Open Access
Creative Commons BY license

Nanoscale Adv., 2020,2, 4557-4565

Synthesis of Zn-based 1D and 2D coordination polymer nanoparticles in block copolymer micelles

C. Göbel, G. Hörner, A. Greiner, H. Schmalz and B. Weber, Nanoscale Adv., 2020, 2, 4557 DOI: 10.1039/D0NA00334D

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements