Effects of accelerated degradation on metal supported thin film-based solid oxide fuel cells

Abstract

A thin film-based solid oxide fuel cell is deposited on a Ni-based metal porous support by pulsed laser deposition with a multi-scale-graded microstructure design. The fuel cell, around 1 μm in thickness, is composed of a stabilized-zirconia/doped-ceria bi-layered dense electrolyte and nanostructured Ni-stabilized zirconia and La0.6Sr0.4CoO3 electrodes as the anode and cathode, respectively. The cell is tested at intermediate temperatures (600–650 °C) with the aim to discern the degradation mechanisms occurring in the cell under accelerated conditions. Under open circuit conditions, electrochemical performances are steady, indicating the stability of the cell. Under electrical load, a progressive degradation is activated. Post-test analysis reveals both mechanical and chemical degradation of the cell. Cracks and delamination of the thin films promote a significant nickel diffusion and new phase formation. Signs of elemental distribution at low temperature are detected throughout the cell, indicating a combination of low energy surface elemental interdiffusion and electromigration effects.

Graphical abstract: Effects of accelerated degradation on metal supported thin film-based solid oxide fuel cells

Article information

Article type
Paper
Submitted
19 דצמ 2017
Accepted
25 מרץ 2018
First published
30 מרץ 2018

J. Mater. Chem. A, 2018,6, 7887-7896

Effects of accelerated degradation on metal supported thin film-based solid oxide fuel cells

R. P. Reolon, S. Sanna, Y. Xu, I. Lee, C. P. Bergmann, N. Pryds and V. Esposito, J. Mater. Chem. A, 2018, 6, 7887 DOI: 10.1039/C7TA11091J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements