Facile synthesis of metal oxide/reduced graphene oxide hybrids with high lithium storage capacity and stable cyclability

Abstract

We report an environment-friendly approach to synthesize transition metal oxide nanoparticles (NPs)/reduced graphene oxide (rGO) sheets hybrids by combining the reduction of graphene oxide (GO) with the growth of metal oxide NPs in one step. Either Fe2O3 or CoO NPs were grown onto rGO sheets in ethanol solution through a solvothermal process, during which GOs were reduced to rGO without the addition of any strong reducing agent, e.g.hydrazine, or requiring any post-high-temperature annealing process. The GO or rGO during the precipitation of metal oxide NPs may act as heterogeneous nucleation seeds to facilitate the formation of small crystal grains. This may allow more efficient diffusion of Li ions and lead to high specific capacities. These metal oxide NPs–rGO hybrids were used as anodes for Li-ion batteries, which showed high capacities and excellent charge–discharge cycling stability in the voltage window between 0.01 and 3.0 V. For example, Fe2O3 NPs/rGO hybrids showed specific capacity of 881 mA h g−1 in the 90th cycle at a discharge current density of 302 mA g−1 (0.3 C), while CoO NPs/rGO hybrids showed a lower capacity of 600 mA h g−1 in the 90th cycle at a discharge current density of 215 mA g−1 (0.3 C). These nanohybrids also show excellent capacities at high C rate currents, e.g. 611 mA h g−1 for Fe2O3/rGO sample in the 300th cycle at 2014 mA g−1 (2 C). Such synthesis technique can be a promising route to produce advanced electrode materials for Li-ion batteries.

Graphical abstract: Facile synthesis of metal oxide/reduced graphene oxide hybrids with high lithium storage capacity and stable cyclability

Supplementary files

Article information

Article type
Paper
Submitted
05 אוק 2010
Accepted
17 נוב 2010
First published
22 דצמ 2010

Nanoscale, 2011,3, 1084-1089

Facile synthesis of metal oxide/reduced graphene oxide hybrids with high lithium storage capacity and stable cyclability

J. Zhu, T. Zhu, X. Zhou, Y. Zhang, X. W. Lou, X. Chen, H. Zhang, H. H. Hng and Q. Yan, Nanoscale, 2011, 3, 1084 DOI: 10.1039/C0NR00744G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements