Oxygen induced enhancement of NIR emission in brookite TiO2 powders: comparison with rutile and anatase TiO2 powders

Abstract

Brookite TiO2 attracts considerable attention in photocatalysis owing to its superior performance in several photocatalytic reactions. In this work, we investigated the behavior of charge carriers in brookite, rutile, and anatase TiO2 by using photoluminescence (PL) and transient absorption (TA) spectroscopies. PL measurements revealed that brookite TiO2 exhibits a visible and a NIR emission at ∼520 nm and ∼860 nm, respectively. Addition of methanol vapor quenched both the visible and NIR emissions by the hole-consuming reaction of methanol. However, exposure to O2 shows curious behaviors: the visible emission was quenched but the NIR emission was enhanced. These results can be accounted for by the enhancement of upward band bending resulting in the effective separation of electrons and holes into the bulk and the surface, respectively. Furthermore, the shallowly trapped electrons, which are responsible for visible PL, are consumed by O2; hence, the visible emission is quenched. However, in the case of NIR emission, the deeply trapped electrons are responsible and they are mainly located at the surface defects. The O2 adsorption promotes the hole accumulation at the surface and then assists the recombination of these deeply trapped electrons, resulting in the enhancement of the NIR emission. We also found that the lifetime of NIR emission (τ1 = 43 ± 0 ns and τ2 = 589 ± 1 ns) was much longer than that of visible emission (τ1 = 15 ± 0 ns and τ2 = 23 ± 0 ns), since the mobility of these deeply trapped electrons to encounter with holes is lower than that of the shallowly trapped electrons. However, even for this slow NIR emission, the actual lifetime of the deeply trapped electrons estimated by TA (1.5 ± 0.0 μs and 17 ± 0 μs) was one or two orders of magnitude longer, confirming that non-radiative recombination is dominant and it is much slower than radiative recombination: TAS and PL provide detailed information on the radiative and non-radiative recombination processes. The PL of anatase and rutile TiO2 powders was also measured and the difference from brookite TiO2 was discussed.

Graphical abstract: Oxygen induced enhancement of NIR emission in brookite TiO2 powders: comparison with rutile and anatase TiO2 powders

Article information

Article type
Paper
Submitted
12 oct. 2017
Accepted
27 oct. 2017
First published
27 oct. 2017

Phys. Chem. Chem. Phys., 2018,20, 3241-3248

Oxygen induced enhancement of NIR emission in brookite TiO2 powders: comparison with rutile and anatase TiO2 powders

J. J. M. Vequizo, S. Kamimura, T. Ohno and A. Yamakata, Phys. Chem. Chem. Phys., 2018, 20, 3241 DOI: 10.1039/C7CP06975H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements