Straintronic effect for superconductivity enhancement in Li-intercalated bilayer MoS2

Abstract

In this study, ab initio calculations were performed to show that the superconductivity in Li-intercalated bilayer MoS2 could be enhanced by applying either compressive or tensile strain. Moreover, the mechanism for superconductivity enhancement for the tensile strain case was found to be different than that of the compressive strain case. Enhanced electron phonon coupling (EPC) under tensile strain could be explained by an increase in the nesting function involved with the change in the Fermi surface topology in a wide range of Brillouin zones. The superconducting transition temperature Tc of 0.46 K at zero strain increased up to 9.12 K under a 6.0% tensile strain. Meanwhile, the enhancement in compressive strain was attributed to the increase in intrinsic electron phonon matrix elements. Furthermore, the contribution from interband scattering was large, which suggested the importance of electron pockets on the Fermi surface. Finally, 80% of the total EPC (λ = 0.98) originated from these pockets and the estimated Tc was 13.50 K.

Graphical abstract: Straintronic effect for superconductivity enhancement in Li-intercalated bilayer MoS2

Supplementary files

Article information

Article type
Communication
Submitted
25 mai 2020
Accepted
03 juil. 2020
First published
06 juil. 2020
This article is Open Access
Creative Commons BY license

Nanoscale Adv., 2020,2, 3150-3155

Straintronic effect for superconductivity enhancement in Li-intercalated bilayer MoS2

P. Mano, E. Minamitani and S. Watanabe, Nanoscale Adv., 2020, 2, 3150 DOI: 10.1039/D0NA00420K

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements