Preparation of hydrophobic epoxy–polydimethylsiloxane–graphene oxide nanocomposite coatings for antifouling application

Abstract

Epoxy–polydimethylsiloxane–graphene oxide (EPG) nanocomposite coatings were successfully developed by loading different wt% of graphene oxide nanosheets (GNs) into an epoxy–hydroxy-terminated-polydimethylsiloxane (EP–hPD) matrix via a facile in situ preparation technique. The inclusion of GNs into EPN led to an increase in modulus of elasticity and tensile strength up to 1570.46 MPa and 31.54 MPa, respectively, in the case of 1 wt% loading of GNs in the EP–hPD matrix. Also, an increase in the water contact angle from 90.1° to 115.2°, 104.5° and 101.7° was discerned at 1, 3 and 5 wt% loadings of GNs respectively. Taber abrasion results demonstrated a decrease in abrasion loss by 33.3% at 1 wt% loading of GNs in comparison to the unreinforced coating. An improvement in the glass transition temperature (Tg) was observed from 63.5 °C for the neat sample to 77.6 °C, 76.3 °C and 71.6 °C for the 1, 3 and 5 wt% EPG nanocomposites, respectively. An inevitable enhancement in the properties of the nanocomposites was affirmed due to the synergistic effect of GNs dispersed within the EP–hPD blend matrix. The prominent findings of this work include a minimum corrosion rate of 0.73 × 10−2 mm per year and upgradation in the antifouling performance of the nanocomposite coatings in comparison to the neat coating.

Graphical abstract: Preparation of hydrophobic epoxy–polydimethylsiloxane–graphene oxide nanocomposite coatings for antifouling application

Supplementary files

Article information

Article type
Paper
Submitted
29 syys 2019
Accepted
08 joulu 2019
First published
09 joulu 2019

Soft Matter, 2020,16, 1211-1226

Preparation of hydrophobic epoxy–polydimethylsiloxane–graphene oxide nanocomposite coatings for antifouling application

S. Verma, S. Mohanty and S. K. Nayak, Soft Matter, 2020, 16, 1211 DOI: 10.1039/C9SM01952A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements