Al-substitution-induced defect sites enhance adsorption of Pb2+ on hematite

Abstract

Al-substitution in hematite is ubiquitous in nature and strongly affects the environmental behaviors of hematite. However, the defect microstructure caused by Al-substitution and its inner relationship with the surface reactivity of hematite remain unclear. In this study, the crystal structure of Al-substituted hematite was characterized by high-resolution electron transmission microscopy (HRTEM) and high angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). Acid–base titration and Pb2+ adsorption experiments were performed to investigate the surface reactivity of Al-substituted hematite. HRTEM images revealed that the proportion of (001) facets on hematite increased from 44.0 ± 3.8% to 84.8 ± 6.5% with increasing Al-substitution. HAADF-STEM images indicated that Al-substitution resulted in more vacancies of Fe atoms on hematite (001) facets. At these Fe defect sites, additional singly ([triple bond, length as m-dash]FeOH−0.5) and triply ([triple bond, length as m-dash]Fe3O−0.5) coordinated hydroxyl sites were formed. The weight loss due to dehydrogenation was 1.7%, 3.3% and 6.2% with increasing Al-substitution from 0%, 5% to 10%. Besides, the relative percentage of surface oxygen atoms in the surface hydroxyl sites of Al-substituted hematite was consistent with the results of thermogravimetric analysis. At pH 5, the relative charge density of the hematite with 0%, 5% and 10% Al-substitution was 73, 94 and 241 mC m−2, and their adsorption capacity for Pb2+ was 0.82, 1.23 and 3.51 μmol m−2, respectively. These results indicate that the formation of more defect sites with increasing Al-substitution can significantly enhance the surface charge density and Pb2+ adsorption capacity of hematite.

Graphical abstract: Al-substitution-induced defect sites enhance adsorption of Pb2+ on hematite

Supplementary files

Article information

Article type
Paper
Submitted
08 آبان 1397
Accepted
05 فروردین 1398
First published
06 فروردین 1398

Environ. Sci.: Nano, 2019,6, 1323-1331

Al-substitution-induced defect sites enhance adsorption of Pb2+ on hematite

Y. Liang, M. Wang, J. Xiong, J. Hou, X. Wang and W. Tan, Environ. Sci.: Nano, 2019, 6, 1323 DOI: 10.1039/C8EN01221K

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements