Thermal sensitivity of frequency upconversion in Al4B2O9:Yb3+/Nd3+ nanoparticles

Abstract

We report measurements of frequency upconversion (UC) processes in ytterbium (Yb3+) and neodymium (Nd3+) doped Al4B2O9 nanoparticles – labeled as Al4B2O9:Yb3+/Nd3+ – prepared by a polymeric precursor method. The nanoparticles investigated contained 1 mol%Yb3+ and 2 mol%Nd3+. The samples were characterized by X-ray diffraction, high-resolution transmission electron microscopy, optical diffuse reflectance and photoluminescence. UC emissions in the range of 770 to 940 nm were studied by exciting the samples with a continuous-wave diode laser operating at 977.7 nm, on resonance with the Yb3+ transition 2F7/22F5/2. The linear dependence of the UC signals versus the laser intensity was investigated and the thermal sensitivity of the UC process was measured by changing the sample temperature from 26 to 60 °C. The UC photoluminescence behavior was understood to be due to the energy transfer from the excited Yb3+ to Nd3+ initially in the ground state manifold, in a process involving phonon-annihilation. The potential of the Al4B2O9:Yb3+/Nd3+ nanoparticles to be used as optical thermometers was favorably evaluated in comparison with other materials. A large average thermal sensitivity of 2.6 × 10−2 K−1 was achieved.

Graphical abstract: Thermal sensitivity of frequency upconversion in Al4B2O9:Yb3+/Nd3+ nanoparticles

Article information

Article type
Paper
Submitted
04 آبان 1395
Accepted
24 دی 1395
First published
24 دی 1395

J. Mater. Chem. C, 2017,5, 1240-1246

Thermal sensitivity of frequency upconversion in Al4B2O9:Yb3+/Nd3+ nanoparticles

A. F. Silva, F. Elan, E. L. Falcão-Filho, L. J. Q. Maia and C. B. de Araújo, J. Mater. Chem. C, 2017, 5, 1240 DOI: 10.1039/C6TC04630D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements