Characterization of mechanical degradation in an all-solid-state battery cathode

Abstract

Solid-state batteries (SSBs) are considered promising next-generation energy storage devices but tend to suffer from rapid capacity fade. Here, we demonstrate that mechanical contact loss between the solid conductor and cathode, induced by its volume changes during cycling, plays a significant role in the observed capacity fade. Focused ion beam-scanning electron microscope (FIB-SEM) tomography with nanoscale resolution was used for 3D characterization of the composite electrode morphology before and after cycling. The tomography data demonstrates the development of voids and cracks near the cathode particles and significant contact loss between the cathode particles and solid electrolyte after cycling. The observed mechanical degradation in the electrode composite highlights the difficulty and importance of engineering mechanically stable SSBs. The application of large external pressure after long-term cycling led to recovery of lost capacity and reduced the cell resistance, confirming the effect of mechanical degradation.

Graphical abstract: Characterization of mechanical degradation in an all-solid-state battery cathode

Supplementary files

Article information

Article type
Communication
Submitted
17 Uzt. 2020
Accepted
11 Abu. 2020
First published
20 Abu. 2020
This article is Open Access
Creative Commons BY-NC license

J. Mater. Chem. A, 2020,8, 17399-17404

Characterization of mechanical degradation in an all-solid-state battery cathode

T. Shi, Y. Zhang, Q. Tu, Y. Wang, M. C. Scott and G. Ceder, J. Mater. Chem. A, 2020, 8, 17399 DOI: 10.1039/D0TA06985J

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements