Greatly enhanced stability of CsPbBr3@PbBrOH through water induction

Abstract

In this paper, CsPbBr3@PbBrOH-1 (Cs-1) was synthesized at room temperature, and then CsPbBr3@PbBrOH-2 (Cs-2) with good stability was successfully synthesized by a water induction technique. The introduction of water can promote the conversion of a CsPbBr3 perovskite exposed on the sample surface to PbBrOH and further promote the isolation of CsPbBr3 quantum dots (QDs) inside the sample from the environment. PbBrOH-coated CsPbBr3 QDs have a clear crystal fringe and a good crystal structure. Under an optimum 367 nm excitation, Cs-1 and Cs-2 show excellent green emissions at ∼520 nm and ∼519 nm, respectively. The lifetime value of Cs-2 was determined to be ∼1.55 ns, which is slightly longer than that of Cs-1 of ∼1.31 ns. The photoluminescence quantum yield (PLQY) of the Cs-2 powder reached 52%. CsPbBr3@PbBrOH greatly improves the stability of CsPbBr3 QDs and possesses excellent polar solvent stability, photostability, thermal stability and thermal cycling stability. CsPbBr3@PbBrOH with superior luminescence properties and stability would be expected to be widely used in lighting and display areas.

Graphical abstract: Greatly enhanced stability of CsPbBr3@PbBrOH through water induction

Article information

Article type
Paper
Submitted
07 ago. 2022
Accepted
02 oct. 2022
First published
14 oct. 2022

J. Mater. Chem. C, 2022,10, 15843-15850

Greatly enhanced stability of CsPbBr3@PbBrOH through water induction

J. Li, G. Liu, Y. Lu and Z. Liu, J. Mater. Chem. C, 2022, 10, 15843 DOI: 10.1039/D2TC03322D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements