Ce4+-Substituted Ni–Al mixed oxide: fluoride adsorption performance and reusability

In this study, Ce4+-doped Ni–Al mixed oxides (NACO) were synthesized and comprehensively characterized for their potential application in fluoride adsorption. NACOs were examined using Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy (SEM), revealing a sheet-like morphology with a nodular appearance. X-ray diffraction (XRD) analysis confirmed the formation of mixed oxides of cubic crystal structure, with characteristic planes (111), (200), and (220) at 2θ values of 37.63°, 43.61°, and 63.64°, respectively. Further investigations using X-ray Photoelectron Spectroscopy (XPS) identified the presence of elements such as Ni, Al, Ce, and O with oxidation states +2, +3, +4, and −2, respectively. The Brunauer–Emmett–Teller (BET) analysis indicated that NACO followed a type IV physisorption isotherm, suggesting favorable surface adsorption characteristics. The adsorption kinetics was studied, and the experimental data exhibited a good suit to both pseudo-first order and pseudo-second order, as indicated by high R2 values. Moreover, the Freundlich isotherm model demonstrated a good fit to the experimental data. The result also revealed that NACO has a maximum capacity for adsorption (qmax) of 132 mg g−1. Thermodynamic studies showed that fluoride adsorption onto NACO was feasible and spontaneous. Additionally, NACO exhibited excellent regeneration capabilities, as evidenced by a remarkable 75.71% removal efficiency at the sixth regeneration stage, indicating sustained adsorption capacity even after multiple regeneration cycles. Overall, NACOs displayed promising characteristics for fluoride adsorption, making them potential candidates for efficient and sustainable water treatment technologies.


Introduction
Fluoride contamination is a signicant global issue, particularly in developing countries, as it has detrimental effects on groundwater quality and poses serious health risks to humans, including dental and skeletal uorosis. 1To address this problem, various methods such as adsorption, coagulation, precipitation and membrane ltration have been proposed for uoride (F − ) removal.Among these techniques, adsorption is widely recognized as one of the most effective and cost-efficient approaches for deuoridation. 2 Therefore, the on-going search for a suitable adsorbent material to remove uoride from water is of utmost importance.It is crucial to develop an efficient and affordable material to eliminate uoride from water.
The search for an appropriate adsorbent material involves exploring natural and synthetic substances that have the ability to bind uoride ions.Natural adsorbents like activated alumina, bone char, and zeolites have been extensively studied and utilized for uoride removal, showing promising results in reducing uoride concentrations in water.However, these materials may have limitations in terms of cost, availability, or regeneration capabilities. 3n recent years, developing mixed oxides, a class of materials with a combination of two or more metal oxides, have garnered signicant attention due to their remarkable properties and diverse applications.These materials offer synergistic advantages over their individual oxide counterparts, exhibiting enhanced catalytic activity, improved stability, and tailored electronic and optical properties.They have demonstrated exceptional performance in a wide range of applications, particularly in water treatment and photo-/electrocatalysis.For instance, CuO x @Co 3 O 4 core-shell nanowires exhibited remarkable sensitivity, selectivity, and response time in glucose oxidation, making them promising candidates for nonenzymatic glucose sensors. 4Similarly, MOF-on-MOF-derived hollow Co 3 O 4 /In 2 O 3 nanostructure, showcased superior photocatalytic CO 2 reduction efficiency, highlighting their potential in sustainable energy applications. 5Mg-Al layered double hydroxide (LDH) derived mixed oxide with enhanced uoride removal capacity (222 mg g −1 ) was reported. 6LDHs, with their layered structure and exchangeable interlayer cations, serve as excellent precursors for the fabrication of mixed oxides.Calcination of LDHs leads to the decomposition of the hydroxide layers, resulting in the formation of mixed oxides with well-dened structures and compositions.This method offers several advantages, including ease of synthesis, high crystallinity, and control over the morphology and particle size of the mixed oxides. 3he remarkable performance of mixed oxides derived from LDHs stems from their unique structural and compositional features.The intimate contact between different metal oxides within the mixed oxide structure facilitates synergistic interactions, leading to enhanced electron transfer and catalytic activity.Additionally, the presence of multiple metal ions with different oxidation states and electronic properties can modulate the redox potential of the mixed oxide, further improving its catalytic performance.Moreover, calcined layered double hydroxides (CLDHs) can adsorb different anions by reconstructing their original LDH structure through the memory effect. 3n line with these advancements, the present study proposes Ce 4+ -doped Ni-Al mixed oxides as a novel uoride adsorbent material.By introducing Ce 4+ dopants into the Ni-Al mixed oxide structure, electron-decient Ce 4+ sites are created, activating the surface hydroxyl groups and resulting in an enhanced uoride adsorption capacity.
To further elaborate on the signicance of this study and considering actual applications in real world, investigating the inuence of various factors on uoride removal efficiency using Ce 4+ -doped Ni-Al mixed oxides is crucial.These factors include Ce 4+ dopant concentrations, pH levels, initial uoride concentration, adsorbent dosage, temperature, and contact time.By systematically studying these parameters, a comprehensive understanding of their impact on uoride removal efficiency can be obtained, aiding in the optimization of the deuoridation process.
In summary, the study proposes Ce 4+ -doped Ni-Al mixed oxides as a novel adsorbent material for uoride removal, leveraging the creation of electron-decient Ce 4+ sites and activation of surface oxides to enhance uoride adsorption capacity.By investigating various factors and regenerability, the study contributes to the advancement of an efficient and costeffective adsorbent for removing uoride from aqueous solutions.Merck provided sodium hydroxide (NaOH), potassium uoride (KF) and hydrochloric acid (HCl).All of these compounds were analytical reagent grade and did not require further purication while being used.The solutions used in the experiment were made using type I deionized water (DI).

Experimental section
The Ce-doped Ni-Al mixed oxide adsorbents were obtained by calcination of the corresponding LDH at 450 °C using a microwave furnace for 2 hours.Initially, the precursor layered double hydroxide (LDH) containing different amounts of the dopant (at 5%, 10% and 20% of Ce to substitute Al) were synthesized following the method reported by Wagassa et al. 7 The synthesis process of LDH was conducted under controlled pH conditions of 10 ± 0.5.Finally, the obtained MOs are coded as NACO-0, NACO-5, NACO-10 and NACO-20 indicating the amount of dopant.

Characterization
The Ce-doped Ni-Al MOs were thoroughly characterized using various techniques.Scanning Electron Microscopy (SEM, a TESCAN VEGA3 equipment) and High-Resolution Transmission Electron Microscopy (HRTEM, a JEOL JEM 2100 PLUS) were used to analyze the surface morphology.The elemental composition of the MOs was determined by Energy Dispersive X-ray Spectroscopy (EDS).The oxidation states of elements in the surface layer of MOs were measured with X-ray Photoelectron Spectroscopy (XPS) of an Oxford Instrument Omicron ESCA.X-ray powder diffraction (XRD) patterns were produced by scanning over the 2 range of 10 to 90°at a constant scanning rate with an X-ray diffractometer (Rigaku Miniex-600) equipped with a copper Ka source.The VERTEX70 spectrometer (BRUKER, Germany) was used to record the spectra of attenuated total reection Fourier transform infrared (ATR FT-IR) from 400 to 4000 cm −1 .

Adsorption experiment
A batch adsorption technique was used to evaluate the efficiency of the synthesized MOs under different experimental conditions.Initially, the adsorption efficiencies of Ce-doped Ni-Al MOs were compared to identify the most effective MO for further study.Several factors such as interaction time, initial F − concentration, adsorbent amount, agitation rate, pH of solution and temperature were explored.The contact time ranged from 15 to 120 min to examine the adsorption kinetics.Solution pH was varied from 3 to 11 to assess its impact on the adsorption process.Adsorbent doses (0.25 to 1.25 g L −1 ) were tested to determine the optimal amount for uoride removal.The initial F − concentration was varied from 10 to 60 mg L −1 to investigate the adsorption capability.Agitation rates from 50 to 250 rpm were used to study the effect of rate of mixing.Finally, the temperature was adjusted from 25 to 55 °C to evaluate its inuence on the adsorption process.
Aer each adsorption process, the uoride ion concentration was determined aer ltering the samples through a 0.45 mm nylon syringe lter.A uoride ion selective electrode was used to determine the ltered samples.Subsequently, the equilibrium adsorption capacity (q e ) and present removal (R) were calculated using the equations below: In these equations, C o represents initial F − concentration, C e represents equilibrium F − concentration, V denotes solution volume, and m indicates mass of the adsorbent.

NACOs characterization
The as-prepared NACOs were analyzed using XRD.The obtained results are displayed in Fig. 1A.The XRD patterns revealed distinct diffraction peaks at specic angles of 37.63°, 43.61°, and 63.64°, which corresponded to the crystallographic planes (111), (200), and (220), respectively.These crystallographic planes were identied to correspond to NiO (JCPDS: 01-1239). 8,9he presence of well-dened diffraction peaks that corresponded to crystallographic planes (111), (200), and (220) suggested the formation of a well-dened crystal structure for the NACOs at lower concentration of the Ce dopant.However, as the amount of Ce increases distinct peaks typically associated with cerium oxide appeared at 29.0°(CPDS no.34-0394). 10The XRD analysis provides valuable insights into the crystallography and phase impurity of the NACOs, as evidenced by the diffraction pattern when the amount of dopant increases. 8verage lattice constants of the synthesized NACO mixed oxide were determined from the planes (111), ( 200) and ( 220) which are the characteristics of the cubic system of NiO using eqn (3). 11The obtained results are depicted in Table 1.
where a is distance between atoms in crystal, d is lattice spacing (inter-atomic spacing) and (hkl) is Miller indices.From the results, it can be observed that the lattice parameters of NACOs are ranged from 4.142 Å to 4.155 Å.These values are lower than that of pure NiO lattice parameter signifying the presence of Al 3+ and Ce 4+ ions in NiO nanoparticles. 12Thus, these XRD ndings indicate that mixed metal oxides with a NaCl-type crystal structure were achieved through the thermal decomposition of the respective hydrotalcite-like compounds.As it is a simple cubic structure in which the metal cations and anions are arranged in alternating layers. 13verage crystallite sizes of NACOs were calculated based on Debye-Scherrer equation from the three prominent XRD peaks of the materials.The determined results are presented in Table 1.As indicated in the Table 1 the crystallite sizes of all the materials are the same except NACO-5 with a slight change and this suggests that the introduction of Ce 4+ ions did not significantly affected the crystallite size of NACOs. 14 where l is XRD wavelength (Cu Ka = 0.15418 nm), K is 0.9 (Scherrer constant), b is FWHM and q is diffraction angle (Bragg's).
The investigation of the composition of NACOs revealed intriguing ndings through the utilization of ATR FT-IRS.Notably, ATR FT-IR peak observed at 995 cm −1 in NACO-5, 1022 cm −1 in NACO-10, and 1042 cm −1 in NACO-20 provides clear evidence of the presence of Ce-O in the samples (Fig. 1B).The shi towards higher wavenumbers with increasing Ce concentration indicates the inuence of Ce on the vibrational behavior of the mixed oxides. 15This phenomenon may be ascribed to changes in the crystal structure and bonding environment resulting from the incorporation of Ce 4+ ions into the lattice.Furthermore, another notable observation was the pronounced peak at 405 cm −1 , signifying the formation of mixed oxides involving Ni, Al, and Ce. 16,17The appearance of this peak suggests the presence of intricate interactions and bonding arrangements among these elements, leading to the creation of distinct mixed metal oxides.The formation of these complex oxides may have important implications for the material's properties, such as adsorption, catalytic activity, electronic behavior, or structural stability.
BET analysis was implemented to assess the surface area and pore size of the produced NACO nanoparticles.Fig. 1C depicts the N 2 adsorption-desorption isotherms for NACO-0 and NACO-20.It is evident from the graphs that both NACO-0 and NACO-20  Paper RSC Advances revealed a type IV physisorption isotherm, signifying the existence of mesopores.This means that the nanoparticles have pores with widths between 2 and 50 nm.It is characterized by a sharp increase in adsorption at low relative pressures, followed by a plateau at higher relative pressures.This is due to the capillary condensation of nitrogen gas in the mesopores. 18The surface area and pore volume of NACO-20 were determined to be 138.89m 2 g −1 and 0.156 cm 3 g −1 , respectively (Table 2).Meanwhile, NACO-0 displayed a specic surface area of 130.77 m 2 g −1 , as shown in Table 2.It is reasonable to infer that the inclusion of Ce 4+ in NACO could facilitate the penetration of N 2 gas, resulting in a higher surface area.The addition of Ce 4+ to NACO nanoparticles can increase the surface area by creating more defects and vacancies in the crystal lattice.These defects and vacancies can act as nucleation sites for N 2 adsorption, which in turn increases the overall surface area of the material.Additionally, the Ce 4+ ions can also help to stabilize the mesoporous structure of the nanoparticles, which further enhances N 2 adsorption. 18PS was also used to ascertain the chemical states of elements present in NACO.The survey scan revealed the existence of Ni 2p, Ce 3d, Al 2p and O 1s, indicating the successful incorporation of these elements into the mixed oxide structure, while the negligible C 1s signal indicated the removal of carbonate during calcination of the precursor LDH (Fig. 2).The Ni 2p spectra exhibited two characteristic peaks at 855.25 eV (2p 3/2 ) and 873.12 eV (2p 1/2 ), with additional satellite peaks at 861.38 eV and 879.84 eV, which are indicative of the oxidation state Ni 2+ . 19Similarly, the Ce 3d spectra showed peaks at 873.09 eV (3d 5/2 ) and 879.97 eV (3d 3/2 ), in line with peak at 898.4 eV (3d 3/2 ), suggesting the presence of Ce 4+ in the mixed oxide. 20Furthermore, the Al 2p spectra displayed peaks at 67.8 eV (2p 3/2 ) and 73.4 eV (2p 1/2 ), consistent with the presence of Al 3+ ions. 21These XPS results provided valuable insights into the oxidation states of the constituent elements within NACO mixed oxide, which is crucial for understanding its surface chemistry and potential as an efficient uoride adsorbent.
The TEM-EDS mapping analysis revealed a compelling demonstration of the uniform distribution of Ni, Al, Ce, and O elements within the NACO mixed metal oxide (Fig. 4E).This mapping technique allowed for a comprehensive visualization of the elemental composition across NACO, indicating a homogeneous dispersion of the aforementioned elements throughout the NACO structure.Notably, the absence of carbon in the synthesized NACO can be attributed to the effective removal of the layered double hydroxide (LDH) interlayer anion (CO 3 2− ) during the calcination process.This observation is consistent with the XPS ndings, thus reinforcing the reliability and coherence of the obtained results.Furthermore, the EDS provided the composition of Ce-doped Ni-Al MO.The mole ratios of the elements were calculated by dividing the weight percentage of each element by its atomic weight (Fig. 3).The actual mole composition of all the Fig. 2 XPS spectrum of elements existing in NACO with their characteristic binding energies.
elements from the EDS analysis were found to be almost similar to the theoretical ones.Almost the intended amount of Ce was found in the yield of Ce-doped Ni-Al MO.NACO mixed oxide was thoroughly characterized using HRTEM-SAED techniques (Fig. 4).The TEM analysis revealed the presence of aggregates exhibiting a sheet-like morphology, with 2.57 nm average size.The HRTEM measurements further conrmed the crystalline structure of the material by determining the values of d-spacing of 0.23 nm and 0.21 nm, which corresponded to (111) and (200) crystallographic planes, respectively.Notably, these values were found to be in excellent agreement with the results obtained from XRD analysis, corroborating the reliability of the characterization methods employed.Furthermore, the SAED analysis established the polycrystalline nature of NACO, indicating the presence of multiple crystal orientations within it.The d-spacing obtained from SAED are quite similar to that of HRTEM.

Inuence of pH, dose, agitation and coexisting ions on uoride adsorption
In this study, the adsorption capacity and efficacy of uoride were investigated by evaluating the performance of NACO at various pH levels ranging from 3 to 11 (Fig. 5A).The results revealed a clear trend in the uoride adsorption capacity of NACO with changing pH, in which NACO-20 was identied as having better performance and was considered in studying all the adsorption parameters.At lower pH values of 3, NACO demonstrated a high adsorption capacity of 27.06 mg g −1 , indicating its strong affinity for uoride ions.However, as the pH increased, the adsorption capacity of NACO decreased signicantly.The adsorption capacity dropped to 2.6 mg g −1 at pH 11, suggesting a reduced ability of NACO to effectively adsorb uoride ions.Similarly, the removal efficiency exhibited a downward trend with increasing pH.At pH 3, NACO achieved a removal efficiency of 67.64%, indicating its However, as the pH increased to 11, the removal efficiency decreased signicantly to 6.49%, highlighting a diminished effectiveness of NACO in removing uoride ions under alkaline conditions.This decrease in efficiency can be credited to the changing surface charge of NACO and the speciation of uoride ions with varying pH values.At lower pH, the surface of NACO tends to be positively charged, favoring the electrostatic interaction and adsorption of uoride ions.However, at higher pH, the surface charge becomes more negative, leading to repulsion between the negatively charged NACO surface and uoride ions, resulting in decreased adsorption efficacy.Another crucial factor is the impact of varying adsorbent amounts on uoride adsorption using NACO.Six different concentrations of the adsorbent were employed, namely 0.25, 0.5, 0.75, 1.0, 1.25, and 1.5 g L −1 (Fig. 5B).In terms of adsorption capacity, the highest value was observed at the lowest adsorbent concentration, with a recorded capacity of 57.20 mg g −1 .As the adsorbent amount increased gradually, the adsorption capacity experienced a signicant decline reaching a capacity of 19.13 mg g −1 at 1.5 g L −1 .The experimental reduction in adsorption capacity might be ascribed to the limited accessibility of active sites on NACO surface as its amount increased.However, the highest removal efficiency, about 95%, was achieved at an adsorbent concentration of 1.0 g L −1 .Aer reaching this highest peak the removal efficiency remained constant.
The consequence of agitation speed on the adsorption of uoride ions using NACO mixed metal oxide was also investigated.The experiment aimed to evaluate how varying agitation speeds inuenced the adsorption capacity and efficiency of uoride ions onto the synthesized mixed metal oxide.At an agitation speed of 50 rpm, the adsorption capacity was measured as 29.56 mg g −1 , while at 100 rpm, it increased to 31.94 mg g −1 (Fig. 5C).Further increase in agitation speed to 150 rpm resulted in a slight decrease in adsorption capacity to 31.20 mg g −1 .At 200 rpm and 250 rpm, the adsorption capacities were measured as 31.10 mg g −1 and 30.58 mg g −1 , respectively.Similarly, the removal efficiency of uoride ions demonstrated a similar pattern.At 50 rpm, the removal efficiency was 73.90%, which increased to 79.85% at 100 rpm.At 150 rpm, the removal efficiency slightly decreased to 78.01%.At 200 rpm and 250 rpm, the removal efficiencies were measured as 77.76% and 76.45%, respectively.These ndings can be ascribed to the accessibility of active sites on the surface of NACO, mass transfer limitations, and the level of agitation-induced mixing.Lower agitation speeds may result in slower diffusion of uoride ions to the active sites, leading to relatively lower adsorption efficiencies.Conversely, higher agitation speeds enhance the diffusion process, thereby improving the adsorption efficiencies.It is worth noting that excessive agitation can potentially cause desorption of adsorbed uoride ions from the surface of NACO which may be due to attrition of the adsorbent and mechanical impacts at high agitation speed.This detachment can subsequently reduce the overall adsorption efficiency, as observed at the highest agitation speed of 250 rpm. 22he effect of coexisting ions which are commonly found in drinking water, namely SO  adsorption of F − by Ce-doped Ni-Al MO was also studied in the present work.The removal efficiencies of F − were investigated at different concentrations of these coexisting ions, namely 5, 10, and 20 ppm, in the presence of 20 mg per L F − (Fig. 5D).The results showed that the presence of coexisting ions inuenced the removal efficiency of F − .In the presence of SO 4 2− ions at concentrations of 5, 10, and 20 ppm, removal efficiencies of 74.3%, 75.72%, and 76.18% were obtained, respectively.Similarly, in the presence of NO 3 − ions at concentrations of 5, 10, and 20 ppm, removal efficiencies of 73.90%, 73.50%, and 69.03% were obtained, respectively.Finally, in the presence of Cl − ions at concentrations of 5, 10, and 20 ppm, removal efficiencies of 73%, 71.08%, and 66.97% were obtained, respectively.These results indicated that the coexisting ions can slightly affect the removal efficiency of uoride, with varying degrees of inuence depending on the specic ion.Ce 4+ can interact differently with various anions depending on the solution's pH.The pH inuences the speciation of the anions and the availability of Ce 4+ for interaction. 23

Investigation of uoride adsorption kinetics
The adsorption kinetics of uoride onto NACO was examined by varying the contact time from 15 to 120 min at initial F − concentration of 20 mg L −1 , pH of 3 and temperature of 25 °C.
The Table 3 showed that the q t_pred data from both methods is generally close to the q t_exp data.However, there are some differences between the two methods.For example, the q t_pred data from the PFO method is slightly lower than the q t_exp data at the early time points (15 and 30 min), while the q t_pred data from the PSO method is slightly higher than the q t_exp data at the later time points (90 and 120 min).Even though the results suggest that the q t_pred data from PFO is slightly closer to the q t_exp data than the q t_pred data from PSO, both methods are able to predict the q t_exp data reasonably well.
For PFO model, q e was determined to be 30.37 mg g −1 .Furthermore, the rate constant (K 1 ) associated with the PFO model was found to be 0.22, indicating the speed at which the adsorption process occurs (Table 4).The goodness of t for this model was assessed using R 2 , yielding an impressive value of 0.99.This high R 2 value suggests that PFO model effectively describes the adsorption kinetics of F − onto NACO.
Similarly, q e obtained from the PSO model was determined to be 30.54mg g −1 , indicating a slight increase compared to the PFO model (Table 4).The rate constant (K 2 ) associated with the PSO model was found to be 0.07, suggesting a relatively slower adsorption process compared to the PFO model.The PSO model's goodness of t was evaluated using the R 2 , which yielded a value of 0.989, indicating a strong correlation between the model and the experimental data (Fig. 6A).In conclusion, the results demonstrated that both models were able to describe the adsorption process effectively, as evidenced by high R 2 values.This means that the process is inuenced by both mass transfer and chemical reaction that takes place between the adsorbent and adsorbate. 24

Isotherms of uoride adsorption
The adsorption behavior of uoride onto NACO was investigated by examining the adsorption isotherms at various initial F − concentrations ranging from 10 to 60 ppm.The obtained data was analyzed using different nonlinear isotherm models, namely Freundlich, Langmuir and Temkin (Tables 4, 5 and Fig. 6B).
As shown in Table 5, the error between the q eq_exp values and the q eq_pred values is greater for the Temkin model than for the other models and is least for the Freundlich model.This suggested that the Freundlich model was the best-tting model, as it has the lowest overall error between the q eq_exp values and the q eq_pred values.
For the Freundlich isotherm model, the obtained parameters were K f = 17.75 and N = 2.08, with a high coefficient of determination (R 2 ) of 0.999 (Table 4).The Freundlich model suggests that F − adsorption onto NACO is favorable and follows a heterogeneous process. 25he Langmuir model yielded a q max of 132 mg g −1 , and a Langmuir constant (K L ) of 0.07, with R 2 value of 0.97 (Table 4).The Langmuir model assumes adsorption of monolayer type onto a homogeneous surface, indicating that the adsorption of uoride onto NACO follows a Langmuir-type mechanism. 26ble 3 Comparisons of q t_pred from kinetic models with q t_exp Time (min) q t_exp (mg g −1 ) q t_pred (mg g −1 ), PFO q t_pred (mg g The Temkin isotherm model resulted in a Temkin constant (K T ) of 0.92 and a Temkin heat of adsorption (B T ) of 92.9, along with R 2 value of 0.962 (Table 4).The Temkin model implies a weaker adsorbent-adsorbate interaction, suggesting that the adsorption of uoride onto NACO involves a combination of physical and chemical interactions.27 In summary, these isotherm models provide valuable insights into the adsorption behavior of uoride onto the synthesized NACO material.The high R 2 values obtained indicate a satisfactory match of the experimental data to Freundlich model, implying that the adsorption process is heterogeneous.These results suggest that NACO has a high affinity for uoride and could be promising adsorbent for water treatment applications targeting uoride removal.

Thermodynamics of adsorption of uoride
The consequence of temperature on the adsorption of uoride onto NACO was investigated in this study.The thermodynamic parameters, including the Gibbs free energy change (DG), dimensionless equilibrium constant (K c ), enthalpy change (DH) and entropy change (DS), were estimated using van't Hoff tting based on the equilibrium constants obtained from the adsorption experiments (Fig. 6C).The data at different temperatures are summarized in Table 6.The DG with negative values indicates that F − adsorption onto NACO is spontaneous at the studied temperatures.The magnitude of DG suggests the thermodynamic favorability of the adsorption and that NACO has a high affinity for uoride ions.The negative DH values indicate the adsorption process is exothermic, implying that the adsorption is driven by heat release.The positive DS values suggest an increase in the randomness of the system during the adsorption course, possibly due to the rearrangement of F − or changes in the adsorbent's surface as it interacts with F − . 28he obtained data provide insights into the thermodynamic parameters governing the adsorption process and shed light on the feasibility and spontaneity of uoride adsorption onto NACO at different temperatures.This information is valuable for understanding the underlying mechanisms of uoride adsorption and for optimizing adsorption processes in water treatment applications.

Investigation of regeneration and reusability
A series of regeneration cycles were conducted to evaluate the reusability performance of NACO nanomaterial for adsorbing uoride from aqueous solutions.The experimental setup involved using 0.5 g L −1 of NACO nanomaterial as adsorbent and an initial uoride amount of 20 mg L −1 .The removing efficiencies for the rst six regeneration cycles were determined to be 89.39%,88.33%, 87.023%, 85.23%, 83.39%, 78.9%, and 75.71%, respectively (Fig. 6D).
These results indicate that NACO nanomaterial possesses excellent regeneration capabilities, allowing for repeated usage without signicant loss in adsorption efficiency.The high removal efficiencies obtained in the subsequent cycles suggest that the nanomaterial maintains its adsorption

RSC Advances
Paper capacity even aer multiple regeneration cycles.This nding is of great signicance for practical applications, as it highlights the potential of NACO nanomaterial as a cost-effective and sustainable adsorbent for F − removing from aqueous solutions.

Adsorption mechanism of F − onto NACOs
][31] The electrostatic interaction between F − ions and Ce 4+doped Ni-Al MOs is indeed the primary driving force for adsorption.The positive charge of the Ce 4+ , Ni 2+ , and Al 3+ ions in MOs attract the negatively charged F − ions.The strength of this interaction depends on the pH of the solution.At low pH, the surface of the MOs is protonated, which increases the positive charge of the surface and strengthens the interaction.As the pH increases, the surface of MOs becomes deprotonated, which reduces their positive charge and weakens the electrostatic interaction with F − . 30,31he formation of complexes between NACOs and F − is another important mechanism in the adsorption of F − onto NACOs.The complexes are formed when a ligand, such as F − , shares an electron pair with a metal ion, such as Ce 4+ , and Al 3+ .The formation of complexes is favored at low pH, where the positive ions are more likely to be hydrated.Hydrated ions have a larger radius than anhydrous ions.This means that the hydrated cations are more likely to be able to form complexes with F − ions.These complexes can help to hold the F − ions onto the surface of the material. 29,31he complex formation can be explained in terms of Lewis acid-base interaction between positive ions of NACOs and F − .This is because for instance Ce 4+ is a Lewis acid, which means it has an empty orbital that can accept electron pairs, whereas F − is a Lewis base, which means it has a lone pair of electrons that it can donate.
The reconstruction of the Ce-doped Ni-Al mixed oxides into a hydrotalcite-like structure during adsorption can also contribute to the high adsorption capacity.Fluoride ions are strongly adsorbed and intercalated into the interlayers of the reconstructed hydrotalcite-like sheets, enhancing the overall adsorption capacity. 32TR FT-IR study provided evidence to support the proposed mechanisms for F − adsorption by NACOs as the emergence of intensied peaks between 2400 to 1500 cm −1 , and a new peak at around 620 cm −1 in the exhausted material (Fig. 7).The presence of intensied peaks in the spectrum of the exhausted material compared to the pristine material indicated changes in the chemical environment of the material.These changes could be due to the interaction between the F − ions and the surface of the NACOs.Additionally, the presence of new peaks suggested the formation of new chemical species as a result of the adsorption process. 30,31

Conclusions
NACO with sheet-like morphology and nodular appearance was successfully synthesized.The XRD analysis conrmed the formation of mixed oxides with NaCl-type crystal structure.TEM-EDS mapping and XPS analysis veried the presence of Ni, Al, Ce, and O elements in different oxidation states.The NACO Table 5 Comparisons of q eq_pred from isotherm models with q t_exp C eq (mg L −1 ) q eq_exp (mg g −1 ) q eq_pred (mg g −1 ), Freundlich q eq_pred (mg g −1 ), Langmuir q eq_pred (mg g −1 ), Temkin  exhibited type IV physisorption isotherm behavior according to BET analysis.Both PFO and PSO kinetic models tted well with the experimental data.The Freundlich isotherm model showed excellent t (high R 2 values).Langmuir model revealed a q max of 132 mg g −1 for uoride.Thermodynamics indicated the feasibility and spontaneity of uoride adsorption onto NACO.Remarkably, NACO demonstrated a high uoride removal efficiency of 75.71% even aer multiple regeneration cycles, highlighting its promising potential for uoride adsorption applications.
Overall, these ndings establish Ce 4+ -doped Ni-Al mixed oxides as a promising and efficient adsorbent material for uoride removal, opening up possibilities for its application in water treatment and environmental remediation strategies.Further research could focus on optimizing the synthesis parameters and exploring other dopants to further enhance the material's performance.

Fig. 3 Fig. 4
Fig.3Percentage composition and mole ratio of elements in NACO-5 from EDS analysis spectra.

Fig. 5
Fig. 5 Graphs indicating influence of (A) pH, (B) dose, (C) agitation and (D) existence of other ions on fluoride adsorption performance of NACO.

Fig. 6
Fig. 6 Graphs of (A) kinetics, (B) isotherms and (C) van't Hoff fitted to fluoride adsorption data and (D) reuse performance of NACO for fluoride adsorption.

Table 4
Outputs of kinetics and isotherm models fitted to results from adsorption of fluoride onto NACO

Table 6
Thermodynamic outputs of fluoride adsorption onto NACO at various temperatures