The selective oxidation of methane to methanol using in situ generated H 2 O 2 over palladium-based bimetallic catalysts †

The selective oxidation of methane to methanol, using H 2 O 2 generated in situ from H 2 and O 2 has been investigated using a series of TS-1 supported bimetallic palladium-based catalysts. The alloying of Pd with Au exhibited improved performance compared to monometallic Pd analogues, with the optimal AuPd catalyst stable over multiple uses. Complementary studies into catalytic performance towards the direct synthesis and subsequent degradation of H 2 O 2 indicated that catalysts that offered moderate activity toward H 2 O 2 synthesis and degradation were the most active for CH 4 oxidation, balancing the high activity of the Pd-only formulation, with the greater selectivity of the Au-only analogue. In particular, the ability of Au to promote the release of oxygen-based radical species from catalytic surfaces is considered to be crucial in achieving improved reactivity, compared to monometallic Pd analogues. The alloying of Pd with more abundant secondary metals was also explored with the NiPd/TS-1 catalyst exhibiting comparable activity to the AuPd analogue. However, unlike over AuPd/TS-1, where methanol is the primary product, the production of formic acid was found to be favoured by the NiPd/TS-1 catalyst.


Introduction
The selective oxidation of methane to methanol, an important platform chemical with an estimated annual global demand of approximately 100 bn litres, 1 is considered a grand challenge for catalytic chemistry, due to the large energy barrier for initial C-H bond activation and the need to prevent over oxidation to CO 2 .Methane is a thermally-stable molecule with four equivalent strong C-H bonds and its partial oxidation products are considerably more reactive than methane itself, making kinetic control of the partial oxidation reaction of paramount importance.Currently, methanol is formed indirectly in an energy-intensive two-step process: methane is initially converted into synthesis gas (CO + H 2 ) via steam (or dry) reforming before methanol synthesis is performed. 2These steps require high temperature and pressure, adding to the capital costs of producing methanol and rendering the process efficient only on large scales.The conversion of methane to a value-added product via an alternative route could increase the range of applications of oxidative methane processing including dealing with low-level methane production at landfill sites, and anaerobic digesters while also reducing natural gas flaring at oil wells.A recent IEA report estimated flaring emissions globally to be approximately 250 Mt. 3 Alternative dispositions for methane could result in the lowering of GHG emissions worldwide.Therefore, there is an urgent need to develop technologies to convert methane into useful chemicals.
Several notable advances have been made in developing catalysts for the direct conversion of methane to methanol.Flytzani-Stephanopoulos and co-workers recently reported that mononuclear rhodium species supported on ZSM-5 can catalyse the conversion of methane into various oxygenates, including methanol, formic acid and acetic acid using O 2 , CO and H 2 O at 150 °C. 4 Additionally, van Bokhoven and coworkers have demonstrated that methane could be anaerobically converted into methanol using H 2 O as an oxidant over Cu-exchanged mordenite. 5We have also reported that Au nanoparticles immobilised onto ZSM-5 are able to oxidise methane to methanol, formic acid and C 2 oxygenates, with minimal formation of CO 2 , at relatively low temperatures and in a closed cycle. 6he use of H 2 O 2 as an oxidant has yielded several breakthroughs in methane oxidation.][9][10][11][12] However, the practical limits of using H 2 O 2 as an oxidant to make methanol from methane are numerous.The technical and economic challenges associated with H 2 O 2 manufacture via current industrial routes (dominated by the Anthraquinone Oxidation Process), in addition to concerns associated with safe transport and storage of the oxidant, would likely preclude the application of pre-formed H 2 O 2 on an industrial scale.Furthermore, the cost of H 2 O 2 is typically greater than that of methanol.Alternatively, the selective partial oxidation of methane via the in situ production of H 2 O 2 from molecular H 2 and O 2 offers an attractive alternative and could reduce costs associated with the oxidant.5][16][17][18][19] Recently, in an attempt to overcome reagent diffusion limitations and improve oxidant utilisation Jin et al. investigated the modification of the external surface of a AuPd@ZSM-5 catalyst, with a hydrophobic organosilane layer, which was found to both promote the localised concentration of reagents near active sites and confine the synthesised H 2 O 2 near the AuPd nanoparticles for subsequent methane activation. 20In contrast to the reaction mechanism proposed for CuFe-ZSM-5 materials 21 (another class of materials widely studied for methane oxidation when used in conjunction with H 2 O 2 ), AuPd catalysed methane oxidation using H 2 O 2 has been shown to proceed via the activation of the methane C-H bond through a hydrogen abstraction pathway, which is mediated by reactive oxygen species (ROS, ˙OOH, ˙OH and ˙O2 − ), which are generated from H 2 O 2 over AuPd surfaces, and the resulting formation of a methyl radical (˙CH 3 ).The termination of the methyl radical species with transient ROS is crucial to the formation of methanol, methyl hydroperoxide, formic acid and carbon dioxide, thus it is possible to draw a direct correlation between the rate of ROS formation and methane oxidation. 14The key reaction steps within the in situ H 2 O 2 mediated activation of methane are reported in eqn (1)-( 5) below and we wish to highlight the comprehensive study by Serra-Maia et al.
The combination of commercial H 2 O 2 with TS-1 has been crucial in the development of several industrial oxidation processes, including the integrated hydrogen peroxide to propylene oxide (HPPO) process 23 and the ammoximation of cyclohexanone to cyclohexanone oxime, 24 a key precursor to the polyamide Nylon-6, with the high efficacy of such industrial processes often attributed to the ability of Ti IV sites within the titanosilicate framework to readily coordinate H 2 O 2 . 25In recent years a growing interest has been placed on the coupling of in situ generated H 2 O 2 with TS-1 for a range of oxidative transformations, including the oxidation of benzyl alcohol, 26 phenol, 27 cyclohexane 28 and propene. 29espite key advances in the area of methane oxidation using an in situ generated oxidant, there are still many opportunities to expand the number of known catalysts for this reaction and explore how different supports and metal compositions affect the catalysis.In this work, we investigate the role of the support and supported metal, as well as the mechanistic relevance of direct hydrogen peroxide synthesis and degradation to methane valourisation.

Catalyst preparation
All catalysts were prepared by the wet co-impregnation of metal salts onto the support (TS-1, TiO 2 (P25) or ZSM-5).The procedure to produce 2 g of 0.33 wt%Au-0.33 wt%Pd/TS-1, with an analogous methodology utilised for all catalyst formulations, is outlined as follows: PdCl 2 (1.1 mL, [Pd] = 6 mg mL −1 , Sigma Aldrich) and HAuCl 4 •3H 2 O solution (0.5388 mL, [Au] = 12.25 mg mL −1 , Strem Chemicals) were placed in a 50 mL round bottom flask, with total volume fixed to 16 mL using H 2 O (HPLC grade, Fischer Scientific).The resulting mixture was heated to 65 °C in a thermostatically controlled oil bath with stirring (600 RPM).Upon reaching 65 °C, TS-1 (1.987 g, HighChem) was added over the course of 5 min.The resulting slurry was then heated to 85 °C for 16 h to allow for complete evaporation of water.The resulting solid material was ground prior to calcination (static air, 400 °C, 3 h, 10 °C min −1 ).Chloride-based precursors were utilised in each case (H 2 PtCl 4 , MnCl 2 .4H 2 O, CuCl 2 and NiCl 2 •6H 2 O) using the same preparation as above and adjusting the amount of salt required.
Catalyst testing Note 1. Reaction conditions used within this study operate outside the flammability limits of gaseous mixtures.
Note 2. The conditions used within this work for H 2 O 2 synthesis and degradation using high-pressure batch conditions have previously been investigated, with the Catalysis Science & Technology Paper presence of CO 2 as a diluent for reactant gases and a methanol co-solvent in the case of the high-pressure experiments identified as key to maintaining high catalytic efficacy towards H 2 O 2 production. 30ote 3. The reaction conditions utilised within this work for the in situ valourisation of methane are based on those previously reported by Ab Rahim et al.In particular regard to the reaction temperature utilised in this work (50 °C), this has previously been identified to offer the greatest concentration of CH 3 OH, when utilising an in situ approach to methane oxidation, using a supported AuPd catalyst. 14

Methane oxidation via in situ H 2 O 2 synthesis
The selective oxidation of methane was carried out in a 50 mL stainless steel Parr autoclave reactor equipped with a PTFE liner.The autoclave liner was charged with catalyst (0.028 g) and solvent (H 2 O, 10.0 mL, HPLC grade Fisher Scientific) and the autoclave was sealed.After purging with N 2 (100 psi), N 2 , H 2 , CH 4 and O 2 were sequentially introduced to the reactor to achieve a composition of 21.55% N 2 , 0.86% H 2 , 75.86% CH 4 and 1.72% O 2 and a total pressure of 30.5 bar.Gaseous reagents were not continuously supplied.The autoclave was then heated to 50 °C before being stirred at 1500 RPM.After 0.5 h, stirring ceased and the reactor was cooled to 10 °C using ice water to minimise the loss of volatile products.The composition of the gas phase was quantified by gas bag analysis of the headspace using a Varian GC (SIL5CB column: 50 m, 0.33 mm internal diameter) equipped with a methaniser and flame ionisation detector.The liquid products were quantified using 1 H NMR on a Bruker 500 MHz spectrometer.The reaction sample (0.7 mL) and D 2 O (0.1 mL, Merck) were added to the NMR sample tube with a calibrated insert (1% TMS in CDCl 3 ) and spectra were integrated against this standard using predetermined calibrations.
TOF calculation was determined based on actual metal loading, with this achieved through the ICP-MS analysis of fresh samples (using a combination of microwave-assisted aqua-regia digestion), and the analysis of post-reaction solutions.

Catalyst reusability in the oxidation of methane via in situ H 2 O 2 synthesis
In order to determine catalyst reusability, a similar procedure to that outlined above for the oxidation of methane was followed using 0.075 g of catalyst.Following the initial test, the catalyst was recovered by filtration and dried (30 °C, 16 h, under vacuum).From the recovered sample, 0.028 g was used to conduct a standard methane oxidation reaction.

Direct synthesis of H 2 O 2 from H 2 and O 2
Hydrogen peroxide synthesis was evaluated using a Parr Instruments stainless steel autoclave with a nominal volume of 100 mL.To test each catalyst for H 2 O 2 synthesis, the autoclave was charged with the catalyst (0.01 g) and solvent (5.6 g MeOH and 2.9 g H 2 O, both HPLC grade, Fischer Scientific).The charged autoclave was then purged three times with 5% H 2 /CO 2 (100 psi) before filling with 5%H 2 /CO 2 to a pressure of 420 psi, followed by the addition of 25% O 2 / CO 2 (160 psi).Gaseous reagents were not continuously supplied.The temperature was then decreased to 2 °C followed by stirring (1200 RPM) of the reaction mixture for 0.5 h.The above reaction parameters represent the optimum conditions we have previously used for the synthesis of H From the solution 2 aliquots of 0.05 g were removed and titrated with acidified Ce(SO 4 ) 2 solution using ferroin as an indicator to determine an accurate concentration of H 2 O 2 at the start of the reaction.The autoclave was purged with 5%H 2 /CO 2 (100 psi) before being pressurised with 5%H 2 /CO 2 (420 psi) and cooled to 2 °C.Upon reaching 2 °C the reaction mixture was stirred at 1200 RPM for 0.5 h.After the reaction was complete the catalyst was removed from the reaction solvents and as previously two aliquots (approximately 0.05 g) were titrated against an acidified Ce(SO 4 ) 2 solution using ferroin as an indicator.The degradation activity is reported as mol

Catalyst characterisation
X-ray photoelectron spectroscopy (XPS) analyses were made on a Kratos Axis Ultra DLD spectrometer.Samples were floated from the spectrometer by pressing onto Scotch-665 double-sided adhesive tape.Data was collected using monochromatic AlK α radiation (140 W, 10 mA × 14 kV) at pass energies of 160 eV for survey spectra, and 40 eV for the high-resolution scans with step sizes of 1 eV and 0.1 eV respectively.The system was operated in the Hybrid mode, using a combination of magnetic immersion and electrostatic lenses and acquired over an area of approximately 300 × 700 μm 2 .A magnetically confined charge compensation system was used to minimize charging of the sample surface, and all spectra were taken with a 90°take-off angle.The charge compensation system typically overcompensates the positive charge by approximately 3 eV, therefore all binding energies were referenced to the C (1s) binding energy of adventitious carbon contamination was taken to be 284.8eV.Data were analysed using CasaXPS (v2.3.25) 31 after subtraction of a

Catalysis Science & Technology Paper
Shirley background and using modified Wagner sensitivity factors as supplied by the manufacturer.Transmission electron microscopy (TEM) was performed on a JEOL JEM-2100 operating at 200 kV.Samples were prepared by dispersion in ethanol by sonication and deposited on 300 mesh copper grids coated with holey carbon film.Energy dispersive X-ray analysis (EDX) was performed using an Oxford Instruments X-Max N 80 detector and the data were analysed using the Aztec software.
Aberration-corrected scanning transmission electron microscopy (AC-STEM) was performed using a probecorrected Hitachi HF5000 S/TEM, operating at 200 kV.The instrument was equipped with bright field (BF) and high angle annular dark field (HAADF) detectors for high spatial resolution STEM imaging experiments.This microscope was also equipped with a secondary electron detector and dual Oxford Instruments XEDS detectors (2 × 100 mm 2 ) having a total collection angle of 2.02 sr.Additional aberrationcorrected scanning transmission electron microscopy was performed using a ThermoFisher ThemisZ S/TEM, operating at 300 keV.The instrument was equipped with high angle annular dark field (HAADF) and a segmented DF4 detector for high spatial resolution STEM-HAADF and STEM-iDPC imaging experiments.The installed Super-X detector has a total area of 120 mm 2 and 0.7 sr solid angle.
To allow for quantification of total metal loading catalytic samples were digested via microwave-assisted aqua-regia digestion of the as-prepared (dried only) catalyst samples, using a Milestone Connect Ethos UP microwave with an SK15 sample rotor.Samples were analysed using an Agilent 7900 ICP-MS equipped with I-AS auto-sampler.All calibrants were matrix matched and measured against a five-point calibration using certified reference materials purchased from Perkin Elmer and certified internal standards acquired from Agilent.Actual metal loadings of key catalytic samples are provided in Table S1.† Total metal leaching from key catalysts was quantified via inductively coupled plasma mass spectrometry (ICP-MS).All samples were diluted by a factor of 10 using HPLC grade H 2 O (1%HNO 3 and 0.5%HCl matrix).All calibrants were matrix matched and measured against a five-point calibration using certified reference materials purchased from Perkin Elmer and certified internal standards acquired from Agilent.

Results and discussion
Selective oxidation of methane to methanol using H 2 and O 2 Initially, a series of supported AuPd catalysts were prepared by the wet co-impregnation of aqueous solutions of HAuCl 4 and PdCl 2 using a selection of catalyst supports.A 5 wt%AuPd/TiO 2 catalyst was identified as the benchmark formulation as it was previously investigated by Ab Rahim et al. who reported that the catalyst produced 1.6 μmoles of oxygenates, under identical reaction conditions to that used in this work. 14AuPd nanoparticles supported on ZSM-5 and TS-1 supports were also prepared: ZSM-5 was selected due to its strong performance in methane to methanol catalysis while TS-1, as discussed above, has been widely reported to facilitate a range of selective oxidations using H 2 O 2 , both preformed and generated in situ.In particular, a 5 wt%AuPdPt/TS-1 catalyst was recently shown to be highly active for H 2 O 2 synthesis. 32In this case, the introduction of Pt resulted in the electronic modification of Pd species, compared to the bimetallic AuPd parent material, with a resulting improvement in catalytic activity.The comparison of methane oxidation and H 2 O 2 synthesis is a key aspect of the current investigation, hence the inclusion of the 5 wt%AuPdPt/TS-1 catalyst in the initial set of screening experiments.While each support could be considered a strong candidate, the porosity, reducibility, acid-base properties and specific surface area vary significantly across the set of catalysts.The catalytic results are shown in Table 1 below, which includes data from the previous investigation by Ab Rahim et al. 14 As shown in Entry 1 of Table 1, in the absence of a catalyst very low levels of liquid products were observed.It is unlikely that the reaction would proceed non-catalytically and the concentration of methanol observed (0.06 μmoles) is on the limit of reliable detection and quantification.Furthermore, the observed CO 2 in the case of the blank experiment is likely

Catalysis Science & Technology Paper
adventitious, resulting from the incomplete purging of the reaction solution and the off-line nature of our gaseous analysis.Although it is clear that CO 2 may be formed through the overoxidation of methane activation products, such as methanol, methyl hydroperoxide and formic acid.Entries 2 and 3 in Table 1 compare the previous work with our current investigations.These data are generally in good agreement, indicated by similar levels of methanol and methyl hydroperoxide production.However, an increased production of formic acid and CO 2 was observed in the current work, and this is reflected in the different TOF values measured (0.73 compared to 0.38 in the previous study).The difference in performance may be related to the variation in the batch-onbatch synthesis of wet co-impregnation catalysts.Interestingly, the 5 wt%AuPd/ZSM-5 catalyst (Table 1, Entry 4) exhibited higher selectivity to formic acid than methanol, producing 1.99 μmoles of total oxygenates.The 5 wt%AuPdPt/TS-1 catalyst exhibited similar activity to that of 5 wt%AuPd/TiO 2 (2.40 and 2.51 mol of total oxygenates produced over the TiO 2 and TS-1 supported materials respectively), although the TS-1 based catalyst exhibited slightly lower CO 2 production.Table 1 Entry 6 shows the catalytic activity of a 0.66 wt%AuPd/TS-1 catalyst.The objective of preparing this catalyst was to minimise the formation of large nanoparticles.Williams et al. have previously reported that 0.13 wt%AuPd/TiO 2 catalysts were intrinsically more active for the selective oxidation of methane to methanol using preformed H 2 O 2 compared to catalysts prepared with higher metal loadings. 9Specifically, lower metal loadings facilitated decreased H 2 O 2 decomposition, which in turn increased the lifetime of reactive oxygen species in the reactor, leading to higher oxygenate production.Additionally, in the direct synthesis of H 2 O 2 , it has been shown that low-loaded AuPd catalysts are also highly active. 33The TOF of the 0.66 wt%AuPd/TS-1 catalyst was the highest of all the catalyst formulations screened, with a value of 1.68, approximately double that of the 5 wt%AuPd/TiO 2 formulation, although the oxygenate selectivity was slightly reduced (53 and 66% for the 0.66 wt%AuPd/TS-1 and 5 wt%AuPd/TiO 2 catalysts respectively).It is interesting to contrast the performance of the ZSM-5 and TS-1 supported materials (Table 1, Entries 4, 5 and 6).The AuPd/ZSM-5 catalyst mostly produced formic acid, while the TS-1 catalysts both favoured methanol and methyl hydroperoxide formation.The propensity of ZSM-5 to preferentially form formic acid over methanol was also reported by Hammond et al. 34 The origin of overoxidation was suggested to be the surface decomposition of methyl hydroperoxide to methanol, which liberates ˙OH radicals that subsequently react with methanol to produce formaldehyde and formic acid. 22Both supports have a microporous MFI structure, but only ZSM-5 possesses strong Brønsted and Lewis acid sites.Methoxy groups may adsorb more strongly on ZSM-5 than TS-1 (or TiO 2 ), increasing the surface lifetime of the intermediate and promoting overoxidation.TS-1, therefore, appears to be a more appropriate support for liquid-phase selective methane oxidation in the current work.
Based on the above data, a second series of low-loaded AuPd/TS-1 catalysts (total metal loading of 0.66 wt%) were prepared, via wet co-impregnation, with various Au : Pd ratios chosen in order to study the effect of nanoparticle composition on catalyst activity.Although the inclusion of Pt in the 5 wt%AuPd/TS-1 catalyst has been previously reported to be beneficial, 25 the presence of a third metal introduces complexity to the catalyst structure.Therefore, in the present study, the Au : Pd ratio was investigated without the addition of Pt.The reactivity of the 0.66 wt%AuPd/TS-1 catalyst series is presented in Table 2.
The rate of oxygenate formation varied across the series of catalysts.However, the greatest concentration was observed over the Pd-rich formulations, compared to the Au-rich analogues.In previous studies of selective methane oxidation over supported catalysts, methanol was the major oxygenate observed, which is generally the case in this work, with the exception of 0.66 wt%Pd/TS-1 and 0.44 wt%Au-0.22 wt%Pd/ TS-1 catalysts.In the case of these catalysts, formic acid was the major oxygenate produced and CO 2 production was lower compared to the rest of the catalytic series.
To further investigate catalyst performance and with a focus on the 0.33 wt%Au-0.33 wt%Pd/TS-1 formulation, catalyst activity was determined over multiple uses in the methane oxidation reaction (Table 3), with the extent of methanol and total oxygenate formation remaining consistent at ca. 0.6 μmol over each of the three reactions.

Catalysis Science & Technology Paper
Notably, we have previously reported the high stability of comparable materials, prepared by an analogous wet coimpregnation procedure, during application in both the direct synthesis of H 2 O 2 35 and in situ oxidative valorisation of chemical feedstocks, under reaction conditions considered far more conducive towards metal leaching than those utilised for the in situ oxidation of methane. 36In keeping with these earlier studies, no leaching of Au was detected over the three reactions, although a minor loss of Pd was observed (Table S2 †).Notably, the leaching of Pd was only measurable over the first two uses of the catalyst, with no further leaching upon use in the third reaction.However, further studies over extended reaction times are required in order to determine catalyst stability when utilised for methane activation, particularly given the formation of low concentrations of chelating agents such as formic acid. 37he catalyst testing results are promising and indicate that low-loaded Pd-based bimetallic catalysts can catalyse the selective oxidation of methane to methanol using H 2 and O 2 .To rationalise the activity trends of the AuPd/TS-1 catalysts, and to gain a deeper understanding of the reaction mechanism, the samples were tested for H 2 O 2 direct synthesis and degradation and characterised by XPS and TEM.H 2 O 2 synthesis and degradation experiments (Fig. 1) were carried out under reaction conditions optimised to enhance H 2 O 2 stability namely; sub-ambient temperature, a methanol co-solvent and a CO 2 gaseous diluent, all of which have been shown to inhibit H 2 O 2 degradation pathways. 30n keeping with earlier studies into AuPd nanoalloys immobilised on SiO 2 38 and TS-1 32 supports, catalytic activity towards both the direct synthesis and subsequent degradation of H 2 O 2 was found to correlate well with total Pd content.Indeed, the monometallic Pd catalyst offered the greatest activity towards both the direct synthesis of H 2 O 2 (66 mol H 2 O 2 kg cat −1 h −1 ) as well as its subsequent degradation (209 mol H 2 O 2 kg cat −1 h −1 ) outperforming both the Au-only and bimetallic formulations.Such observations have been attributed to the poor mixing of the Au and Pd metallic components when immobilised onto the titanosilicate support. 36Catalytic performance towards H 2 O 2 direct synthesis was not found to follow the same trend as that observed for methane oxidation (Table 2), with the bimetallic formulations achieving both higher oxygenate selectivity and TOFs than those observed over the monometallic Pd catalyst.
When considered alongside previous investigations that report the crucial role of Au in promoting the release of ROS from catalyst surfaces, 39,40 these observations indicate that the rate of methane oxidation is not simply a function of H 2 O 2 production.There is likely an important contribution from the highly reactive radical species that are generated as intermediates during the formation of H 2 O 2 .As such it is possible that the observed improved activity of the bimetallic catalysts is related to the release of ROS, which are known to be crucial in the formation of methyl radicals, via Habstraction, and subsequent formation of oxygenates. 22ig. 2 shows the correlation between oxygenate formation and catalyst composition in addition to catalytic activity towards H 2 O 2 synthesis and degradation.The observed trends approximate a volcano plot, where the highest rate of oxygenate production is associated with catalysts that offer moderate rates of H 2 O 2 synthesis and subsequent degradation, that is those materials that consist of approximately equal weight loadings of a Turnover frequency (TOF) calculated using the total moles of product and based on actual metal loading as determined by ICP-MS analysis of digested catalyst samples and analysis of post-reaction solutions.

Catalysis Science & Technology Paper
Au and Pd.This relationship may also indicate the contribution of ROS in addition to H 2 O 2 towards methane oxidation but also the importance of catalytic selectivity towards H 2 O 2 synthesis and the need to inhibit competitive H 2 O 2 degradation pathways.
The differences in observed catalysis across the catalytic series could be associated with a number of factors, namely the particle size and the electronic properties of the nanoparticles (which will be dictated by nanoalloy composition among other factors).To investigate these properties, XPS and TEM analyses were carried out.2][43] Analysis of the series of supported 0.66 wt%AuPd/TS-1 catalysts via XPS (Fig. S1 †) was challenging due to the low loadings of metal.In the case of the 0.66 wt%Pd/TS-1 catalyst, Pd was present almost entirely in the Pd 2+ oxidation state, which was expected as the catalysts were exposed to an oxidative heat treatment.However, the introduction of Au resulted in a slight shift in Pd speciation towards Pd 0 .Similar shifts in the Au 4f binding energy were also observed, whereby the Au-only catalyst exhibited a binding energy of ∼84.0 eV and this shifted downward after Pd addition.6][47] It should be noted that in all cases, due to the low metal loading, the signal-noise ratio was relatively high, which prohibited the meaningful deconvolution of the spectra.
Numerous previous publications have also identified the role of nanoparticle size on catalyst efficiency.The effect of particle size on selectivity towards H 2 O 2 was notably highlighted by Kim et al., who found that smaller Pd particles, which contain high proportions of defect sites, were less selective towards H 2 O 2 and promoted the degradation of the oxidant to H 2 O. 48 Williams et al. identified similar trends for the valorisation of methane to Catalysis Science & Technology Paper methanol when using preformed H 2 O 2 over supported AuPd catalysts. 9Particle size distributions of the TS-1 supported catalysts were calculated using TEM analysis (Table 4, with corresponding electron micrographs reported in Fig. S2 †), which revealed no clear trend: the 0.33 wt%Au-0.33 wt%Pd/TS-1 and 0.44 wt%Au-0.22 wt%Pd/TS-1 catalysts exhibited mean particle sizes of 23 and 17 nm, respectively, while all of the other samples were measured to be similar (7-11 nm).The particle size distributions, shown in Fig. S2, † indicate that most particles counted were <20 nm, but a minority of large particles (50-100 nm) were also detected, such observations are typical of the wet impregnation route to catalyst synthesis, particularly for AuPd catalysts, with a bimodal distribution of large Au-rich and small Pd-rich species widely reported. 49It should be noted that a positive correlation between Pd content and H 2 O 2 synthesis rates was also observed under conditions optimal for H 2 O 2 production.This, combined with the known ability of Au to promote ROS desorption from catalytic surfaces, 40 as discussed above, means we are unable to definitively assign the underlying cause for the improved catalysis observed over the bimetallic formulations.However, such observations are particularly intriguing.With a clear bi-modal particle size distribution evident from our TEM analysis, and with a focus on the 0.33 wt%Au-0.33 wt%Pd/TS-1 catalyst we subsequently conducted detailed HAADF-STEM and XEDS analysis, in order to determine the extent of alloy formation.These studies have confirmed the presence of both Pd-only nanoparticles (Fig. S3 †) and AuPd nanoalloys (Fig. S4 †), where the latter exist over a large particle size range, whereas no large (>20 nm) monometallic Pd species were detected.Notably, we have also confirmed that a considerable population of the AuPd alloyed particles adopt a Au-core Pd-shell morphology, which may be expected given the exposure to an oxidative heat treatment, and the propensity for Pd to undergo oxidation (Fig. 3). 50lthough the performance of the 0.66 wt%AuPd/TS-1 catalysts toward the selective oxidation of methane to methanol with an oxidant produced in situ is promising, from an economic/green chemistry perspective minimising precious metal content would be desirable.The alloying of Pd with a range of base metals has been reported to offer improved catalytic performance compared to Pd-only Catalysts exposed to an oxidative heat treatment (static air, 400 °C, 3 h, 10 °C min −1 ).150 or more particles were counted for 0.66 wt%Pd/ TS-1, 0.44 wt%Au-0.22 wt%Pd/TS-1, 0.33 wt%Au-0.33 wt%Pd/TS-1 and 0.11 wt%Au-0.55 wt%Pd/TS-1 catalysts.In the case of 0.66 wt%Au/TS-1 and 0.55 wt%Au-0.11wt%Pd/TS-1 catalysts, imaging particles was more challenging and counting >50 particles was not possible.
Fig. 3 Microstructural analysis of the 0.33 wt%Au-0.33 wt%Pd/TS-1 catalyst including HAADF-STEM image and X-EDS mapping of the highlighted area showing the presence of AuPd nanoalloys with a Au-core Pd-shell morphology, Au (green), Pd (red), Ti (blue), and Si (yellow).Further analysis is reported in Fig. S3 and S4.†

Catalysis Science & Technology Paper
5][56][57] Such improvements have often been attributed to the modification of the Pd oxidation state and the disruption of contiguous Pd ensembles. 58As such, we subsequently evaluated the performance of a range of bimetallic MPd/TS-1 (total metal loading = 0.66 wt%, 1 : 1 weight ratio, where M = Mn, Cu or Ni) catalysts for the oxidation of methane using H 2 and O 2 (Table 5).Oxygenates were observed in each reaction.However, in the case of CuPd/TS-1 and MnPd/TS-1 catalysts, total oxygenate formation was approximately half of that observed over the AuPd analogue and less than that observed over the Pd-only catalyst.Such observations can be rationalised when considering the high activity of Mn towards H 2 O 2 decomposition 59 and the previous reports that hydroperoxyl (OOH*) and H 2 O 2 formation over Cu-containing supported catalysts is kinetically unfavourable. 60Indeed, we have previously demonstrated that the introduction of Cu at high loadings into AuPd or Pd-only catalysts can significantly inhibit catalyst activity towards H 2 O 2 synthesis and a range of H 2 O 2 catalysed selective oxidative transformations, including the valorisation of methane. 61,62Although more recently the promotive effect that results from the introduction of dopant concentrations of Cu into AuPd nanoalloys has been identified, particularly for the direct synthesis of H 2 O 2 . 63,64otably, the Ni-Pd/TS-1 catalyst was able to achieve a nearidentical concentration of oxygenates (0.60 μmol) to that achieved over the AuPd analogue (0.59 μmol), although CO 2 production was somewhat higher over the NiPd formulation.Interestingly, formic acid was the major product in this case rather than methanol or methyl hydroperoxide.It is noteworthy that 0.41 μmol of total oxygenates were observed over the monometallic 0.66 wt%Pd/TS-1 catalyst confirming that, in a similar manner to Au, the alloying of Pd with Ni is beneficial to the catalytic performance.

Conclusions
We have shown that the oxidation of methane to methanol using in situ synthesised H 2 O 2 is catalysed by a range of supported Pd-based catalysts, with the introduction of Au into Pd, in particular, promoting catalytic performance.Evaluation of catalyst formulation, while maintaining total metal loading at 0.66 wt% revealed that the most active catalysts were those where the Au : Pd ratio was close to 1.Comparison of CH 4 oxidation rates with H 2 O 2 synthesis rates under idealised conditions indicated that the most active catalysts for CH 4 oxidation were moderately active for H 2 O 2 synthesis and degradation, with the enhanced performance of the AuPd alloyed catalysts considered to result from the ability of Au to both modify Pd oxidation states and promote the release of highly reactive oxygen-based radicals (ROS), which are formed as intermediates during H 2 O 2 formation.Reusability tests confirmed that the optimal AuPd catalyst was stable for multiple uses, with minimal leaching of metal species detected, however further study over extended reaction times is still required.We have also demonstrated that Au can be substituted for more economically attractive metals.In particular, the NiPd/TS-1 catalyst exhibited similar oxygenate production to that observed over the AuPd analogue, although formic acid was the dominant product.These studies represent a promising basis for further exploration for developing catalysts for the selective oxidation of methane and other chemical feedstocks.
2 O 2 .H 2 O 2 productivity was determined by titrating aliquots (approximately 0.5 g) of the final solution after reaction with acidified Ce(SO 4 ) 2 (0.01 M) in the presence of ferroin indicator.Catalyst productivities are reported as mol H 2 O 2 kg cat −1 h −1 .
2 degradation was determined in a manner similar to the direct synthesis activity of a catalyst.The autoclave was charged with MeOH (5.6 g, HPLC grade, Fischer Scientific), H 2 O 2 (50 wt% 0.69 g, Merck) H 2 O (2.21 g, HPLC grade, Fischer Scientific) and catalyst (0.01 g), with the solvent composition equivalent to a 4 wt% H 2 O 2 solution.

Table 1
Comparison of various supported metal catalysts for the selective oxidation of methane to methanol using H 2 and O 2 Methane oxidation reaction conditions: catalyst (0.028 g), H 2 O (10.0 ml), 435 psi total pressure (0.86% H 2 , 1.72% O 2 , 75.86% CH 4 , 21.65% N 2 ), 0.5 h, 50 °C, 1500 rpm. a With the exception of entry 2 turnover frequency (TOF) is calculated using the total moles of product and based on on actual metal loading as determined by ICP-MS analysis of digested catalyst samples.b 2.4 wt%Au-2.4wt%Pd-0.2wt%Pt/TS-1.Note: with the exception of entry 6 the metal loading of all catalysts is 5 wt% and for all formulations Au : Pd ratio is 1 : 1 (wt/wt).

Table 3
Catalytic activity of the 0.33 wt%Au-0.33 wt%Pd/TS-1 catalyst towards the in situ oxidation of methane with reuse

Table 4
Particle size of 0.66 wt%AuPd/TS-1 catalysts, prepared by wetimpregnation as a function of Au : Pd ratio as derived by TEM analysis

Table 5
Catalytic activity of 0.33%Pd-0.33%X/TS-1(X = Au, Cu, Ni, Mn) catalysts towards the selective oxidation of methane via in situ H 2 O 2 production Methane oxidation reaction conditions: catalyst (0.028 g), H 2 O (10.0 g), 435 psi total pressure (0.86% H 2 , 1.72% O 2 , 75.86% CH 4 , 21.65% N 2 ), 0.5 h, 50 °C, 1500 rpm. a Turnover frequency (TOF) calculated using the total moles of product and based on actual metal loading as determined by ICP-MS analysis of digested catalyst samples.Note: in the case of the Pd-only catalyst total Pd loading is 0.66%.